Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (40)
- Beitrag zu einem Tagungsband (7)
- Posterpräsentation (3)
- Beitrag zu einem Sammelband (2)
- Sonstiges (1)
- Forschungsbericht (1)
Sprache
- Englisch (54) (entfernen)
Schlagworte
- TEM (9)
- Alumina (4)
- Transmission electron microscopy (4)
- Alumina coatings (3)
- Coatings (3)
- Corrosion protection (3)
- Nanoparticles (3)
- Oxidation (3)
- Sol-gel (3)
- Third body (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (7)
- 5.1 Mikrostruktur Design und Degradation (7)
- 5.6 Glas (3)
- 6 Materialchemie (3)
- 6.7 Materialsynthese und Design (3)
- 6.1 Oberflächen- und Dünnschichtanalyse (2)
- 6.3 Strukturanalytik (2)
- 9 Komponentensicherheit (2)
- 9.5 Tribologie und Verschleißschutz (2)
- 6.2 Material- und Oberflächentechnologien (1)
The transformation of doped or seeded pseudoboehmite to corundum was studied by combining thermal analysis, X-ray diffraction, transmission electron microscopy, and electron paramagnetic resonance spectroscopy. The temperature of phase transformation to corundum was lowered by about 130 °C when Fe3+ or corundum seeds were added to the sols. Action of Fe3+ ions depends on the actual degree of thermally induced transformation of pseudoboehmite via transition aluminas to corundum and the ability of these alumina phases to incorporate Fe3+ ions. These ions tend to aggregate with increasing iron concentration of the alumina phases and can work as nucleation centers. Small (not, vert, similar20 nm) corundum particles act as active nucleation sites whereas larger grains (200400 nm) also present in the samples are less effective. For the first time trapping and stabilization of NO2 molecules in transition aluminas formed by a solgel route was shown.
Up to ~ 3 µm thick alumina coatings on corundum ceramic, sodalimesilica glass and Inconel718 were produced from mixtures of boehmite sols and corundum suspensions.
Transmission electron micrographs in combination with electron diffraction and energy dispersive X-ray spectroscopy served to identify crystallographic phases and to characterize the microstructure of the coatings. Using corundum ceramic as substrate the initially deposited boehmite transforms via transition aluminas to corundum while heating to 1200 °C. In the cases of glass and Inconel718 thermal treatments up to 520 °C and 1100 °C, respectively, cause diffusion of ions from the substrates into the coatings. Thus additional oxide phases were formed.
All coatings are free of cracks or delaminations and do not show any directed crystal growth.
Modified Yoldas sols can be used to prepare crack-free well adherent layers on different substrate materials such as sodalime glass, corundum and metal (IN-718). These layers having thicknesses of 0.6 µm are strain tolerant and withstand thermal cycling between 810 °C and room temperature. Introducing alpha-Al2O3 filler particles into modified Yoldas sols allows the preparation of thicker layers of 1.6 µm, which as well can be thermally cycled without noticeable delaminations. Chemical bonding seems to be the predominant layer bonding mechanism.
Alumina coatings with differing phase compositions were deposited on Inconel-718 (IN-718) Ni-base
superalloy substrates using solgel processing. Mass gain measurements served for studying the oxidation
behavior of coated metal surfaces if exposed to 800°C and 900°C for up to 4000 h in static air. Itwas found, that
alumina coatings significantly reduce the oxidation related mass gain of IN-718 even after heating to 900°C
for 4000 h. Transmission electron microscopy (TEM) studies revealed diffusion of elements from the metal
substrate (IN-718) into the alumina coatings and to a much lower degree from the coating into the
substrate. These diffusion processes are greatly influenced by the phase composition of the coatings, especially
by the presence of alpha-alumina.
Diffraction of hard synchrotron radiation as well as constant-wavelength and time-of-flight neutron diffraction were used for the structural characterization of a silicon carbide powder having extremely low levels of chemical impurities, high perfection of the crystalline lattice and a grain size of up to 150 µm. The presence of three polytypes was ascertained and the ratios of their mass fractions were determined to be w15R : w6H = 0.002,3(8) and w4H : w6H = 0.000,6(2).
By addition of LiF-containing sintering additives to commercial BaTiO3 powder, more than 98% of the theoretical density was reached at a sintering temperature of 900 °C both on powder compacts and laminates. Dielectric measurements were performed on ceramic samples in the temperature and frequency ranges from -20 °C to 125 °C and from 103 to 106 Hz, respectively. High relative permittivity (εr ~ 3160) and low dielectric loss (tan δ ~ 0.014) were measured for tapes of the favoured material. The breakdown strength for tapes with a thickness of about 80 µm is 30 kV/mm. The microprobe analysis showed, that no interfacial reaction between the dielectric layer and the Ag-electrode had occurred.
The newly developed barium titanate ceramics completely densifying at 900 °C turned out to be promising for integration of buried capacitors in LTCC multilayers.
Weld metal microstructure for alloy 6060 aluminum welds, made using the gas-tungsten arc process and alloy 4043 filler metal, has been characterized using optical metallography, EPMA microprobe analysis, SEM/EBSD and STEM/EDX electron microscopy, and single-sensor differential thermal analysis (SS-DTA). In addition, alloy 6060 castings were solidified at variable cooling rates approaching that of welding, to provide a reference for comparison with weld microstructure. It was found that a major change in cast microstructure occurs at cooling rates higher than 27 K/s resulting in a structure similar to that observed in weld metal. Rapid cooling is believed to favor low temperature solidification reactions that normally would be achieved only at higher silicon content. Accordingly, additions of 4043 filler metal that increase the weld metal silicon content have only limited affect on weld solidification range and microstructure. This has direct implications regarding how 4043 filler additions improve weldability and weld quality.
Alumosols in combination with well dispersed corundum were successfully used to form up to 2.5 ìm thick coatings on the Ni-base alloy SC16. These coatings withstood heat treatments at 700 °C in a water vapour containing atmosphere. The heat treatment caused formation of delta-alumina in the coating and diffusion of chromium and titanium into the coating.
Transmission electron microscopy study of rapid thermally annealed Pd/Ge contacts on IN0.53Ga0.47As
(1996)
Single walled carbon nanotubes (SWNT) have been produced in an electric arc discharge by using a graphite rod as anode which is filled with a powder mixture of graphite and metallic catalysts like nickel and yttrium. The soot material containing approximately a third of SWNT was collected from the cathode region as a soft, voluminous material. The main by-products in this process are amorphous carbon and graphitic nanoparticles which have to be removed by an appropriate purification process. The as-produced soot material was purified by gas phase oxidation in air at 355 °C. The oxidation of amorphous carbon in air is advantageous against wet chemical methods because it is better controllable. Thermogravimetric analysis and electron microscopy were used to investigate the oxidation behavior of the different kinds of carbon. Oxidation of SWNT and amorphous carbon occurs simultaneously even at moderate temperatures, whereas amorphous carbon is more rapidly oxidized than SWNT. For optimizing the purification procedure by gas phase oxidation, kinetic studies were used to determine the oxidation time for each component in the soot at a given temperature. So it is possible to remove the amorphous carbon quantitatively with minimal losses of SWNT. But it was found that graphitic nanoparticles have the highest stability against oxidation and could therefore not be quantitatively removed by this method without the complete destruction of SWNT. Therefore, the electric arc discharge process has to be a controlled process for minimum production of graphitic nanoparticles to obtain a material with a high content of SWNT.