Inconel 718 was spin coated twice and fourfold with a sol to obtain 200- and 400-nm-thick transition alumina films on the surface. Bare and solgel alumina-coated Inconel 718 samples were exposed to NaCl solution to study their corrosion behavior by means of electrochemical impedance spectroscopy. In combination with scanning electron microscopy, it was shown that bare Inconel 718 is after initial passivation prone to pitting corrosion. For the coated Inconel 718 samples, an improvement in the protective effect of the coatings with time was observed. This observation is in contradiction to the results of other authors who observed degradation of alumina coatings exposed to NaCl solution with time. Transmission electron microscopy revealed a formation of (1) a compacted region at the coating surface as well as (2) a chromium-rich region at the interface between coating and alloy during the contact with a NaCl solution. The last one mainly contributes to the observed chronological sequence of electrochemical characteristics of the samples.
Microstructure of a steel-alumo-sol-coating-system after heat treatment in an oxyfuel atmosphere
(2015)
In November 2007, OECD’s Working Party on Manufactured Nanomaterials (WPMN) launched the Sponsorship Programme for the Testing of Manufactured Nanomaterials (hereafter the Testing Programme). The objective was to conduct specific tests, relevant to human health and environmental safety endpoints, on a variety of manufactured nanomaterials (MN). The outcomes of the Testing Programme were intended to assess the applicability of the existing test guidelines1 to nanomaterials, as well as to provide useful information on any intrinsic properties of MNs, which are different from the same bulk material with greater external dimensions. Understanding the properties of NMs is crucial to choose appropriate strategies for hazard identification, risk assessment or risk management measures. The Testing Programme involved delegations from OECD member countries, some non-member economies and other stakeholders. The broad international representation, from a range of delegations enabled the programme to pool expertise and resources without which this programme would not have been possible.