Sol-Gel-Aluminiumoxidschichten für den Oxidationsschutz von Hochtemperaturlegierungen, Teil 2
(2009)
Sol-Gel-Aluminiumoxidschichten für den Oxidationsschutz von Hochtemperaturlegierungen, Teil 1
(2009)
Inconel 718 was spin coated twice and fourfold with a sol to obtain 200- and 400-nm-thick transition alumina films on the surface. Bare and solgel alumina-coated Inconel 718 samples were exposed to NaCl solution to study their corrosion behavior by means of electrochemical impedance spectroscopy. In combination with scanning electron microscopy, it was shown that bare Inconel 718 is after initial passivation prone to pitting corrosion. For the coated Inconel 718 samples, an improvement in the protective effect of the coatings with time was observed. This observation is in contradiction to the results of other authors who observed degradation of alumina coatings exposed to NaCl solution with time. Transmission electron microscopy revealed a formation of (1) a compacted region at the coating surface as well as (2) a chromium-rich region at the interface between coating and alloy during the contact with a NaCl solution. The last one mainly contributes to the observed chronological sequence of electrochemical characteristics of the samples.
The need for a more efficient coal power plant generation (e.g. oxyfuel technology) results in modified process parameters and enhanced corrosion. To reach the necessary service life of high temperature parts protective coatings may be a sufficient technical solution. A modified Yoldas sol (Al2O3 based) was used to coat X20CrMoV12-1 by spin coating. After appropriate heat treatments transition alumina coatings being about 400 nm thick were obtained. Oxidation studies were carried out in laboratory air at temperatures up to 650 °C for up to 500 h exposure time. In case of the uncoated sample a rough oxide layer formed on the surface and a remarkable weight gain (2.62 mg/cm²) were detected. The sol–gel alumina layer (mainly δ-Al2O3) demonstrated a high protection, i.e. a very low weight gain (0.05 mg/cm²). Diffusion of alloying elements into the coating was observed. No indication of spallation of the coating occurred. Local defects (2 µm–30 µm) in the coating led to the formation of iron-oxide islands.
Future coal power plants will in case of oxyfuel combustion be operated with altered atmospheres. Hence, corrosion attack might become more severe and steels have to be protected. An alumina-sol was used to coat X20CrMoV12-1 (X20) with alumina to test the protection. Testing was performed at 600 °C in flowing H2O–CO2–O2 and static laboratory air for 1000 h. Oxidation under air is minor compared to exposure in oxyfuel atmosphere. In both cases a multilayered oxide (hematite, magnetite, spinel) was formed on uncoated steels. Carburization appeared on uncoated X20 in H2O–CO2–O2. The coating demonstrates a high protection.