Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (40)
- Beitrag zu einem Tagungsband (7)
- Posterpräsentation (3)
- Beitrag zu einem Sammelband (2)
- Sonstiges (1)
- Forschungsbericht (1)
Sprache
- Englisch (54) (entfernen)
Schlagworte
- TEM (9)
- Alumina (4)
- Transmission electron microscopy (4)
- Alumina coatings (3)
- Coatings (3)
- Corrosion protection (3)
- Nanoparticles (3)
- Oxidation (3)
- Sol-gel (3)
- Third body (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (7)
- 5.1 Mikrostruktur Design und Degradation (7)
- 5.6 Glas (3)
- 6 Materialchemie (3)
- 6.7 Materialsynthese und Design (3)
- 6.1 Oberflächen- und Dünnschichtanalyse (2)
- 6.3 Strukturanalytik (2)
- 9 Komponentensicherheit (2)
- 9.5 Tribologie und Verschleißschutz (2)
- 6.2 Material- und Oberflächentechnologien (1)
The transformation of doped or seeded pseudoboehmite to corundum was studied by combining thermal analysis, X-ray diffraction, transmission electron microscopy, and electron paramagnetic resonance spectroscopy. The temperature of phase transformation to corundum was lowered by about 130 °C when Fe3+ or corundum seeds were added to the sols. Action of Fe3+ ions depends on the actual degree of thermally induced transformation of pseudoboehmite via transition aluminas to corundum and the ability of these alumina phases to incorporate Fe3+ ions. These ions tend to aggregate with increasing iron concentration of the alumina phases and can work as nucleation centers. Small (not, vert, similar20 nm) corundum particles act as active nucleation sites whereas larger grains (200400 nm) also present in the samples are less effective. For the first time trapping and stabilization of NO2 molecules in transition aluminas formed by a solgel route was shown.
Up to ~ 3 µm thick alumina coatings on corundum ceramic, sodalimesilica glass and Inconel718 were produced from mixtures of boehmite sols and corundum suspensions.
Transmission electron micrographs in combination with electron diffraction and energy dispersive X-ray spectroscopy served to identify crystallographic phases and to characterize the microstructure of the coatings. Using corundum ceramic as substrate the initially deposited boehmite transforms via transition aluminas to corundum while heating to 1200 °C. In the cases of glass and Inconel718 thermal treatments up to 520 °C and 1100 °C, respectively, cause diffusion of ions from the substrates into the coatings. Thus additional oxide phases were formed.
All coatings are free of cracks or delaminations and do not show any directed crystal growth.
Modified Yoldas sols can be used to prepare crack-free well adherent layers on different substrate materials such as sodalime glass, corundum and metal (IN-718). These layers having thicknesses of 0.6 µm are strain tolerant and withstand thermal cycling between 810 °C and room temperature. Introducing alpha-Al2O3 filler particles into modified Yoldas sols allows the preparation of thicker layers of 1.6 µm, which as well can be thermally cycled without noticeable delaminations. Chemical bonding seems to be the predominant layer bonding mechanism.
Alumina coatings with differing phase compositions were deposited on Inconel-718 (IN-718) Ni-base
superalloy substrates using solgel processing. Mass gain measurements served for studying the oxidation
behavior of coated metal surfaces if exposed to 800°C and 900°C for up to 4000 h in static air. Itwas found, that
alumina coatings significantly reduce the oxidation related mass gain of IN-718 even after heating to 900°C
for 4000 h. Transmission electron microscopy (TEM) studies revealed diffusion of elements from the metal
substrate (IN-718) into the alumina coatings and to a much lower degree from the coating into the
substrate. These diffusion processes are greatly influenced by the phase composition of the coatings, especially
by the presence of alpha-alumina.