The need for a more efficient coal power plant generation (e.g. oxyfuel technology) results in modified process parameters and enhanced corrosion. To reach the necessary service life of high temperature parts protective coatings may be a sufficient technical solution. A modified Yoldas sol (Al2O3 based) was used to coat X20CrMoV12-1 by spin coating. After appropriate heat treatments transition alumina coatings being about 400 nm thick were obtained. Oxidation studies were carried out in laboratory air at temperatures up to 650 °C for up to 500 h exposure time. In case of the uncoated sample a rough oxide layer formed on the surface and a remarkable weight gain (2.62 mg/cm²) were detected. The sol–gel alumina layer (mainly δ-Al2O3) demonstrated a high protection, i.e. a very low weight gain (0.05 mg/cm²). Diffusion of alloying elements into the coating was observed. No indication of spallation of the coating occurred. Local defects (2 µm–30 µm) in the coating led to the formation of iron-oxide islands.
The paper presents the microstructure, chemical and phase composition of thin scale, obtained as a result of high temperature corrosion of X20Cr13 stainless steel. Samples were exposed to gas atmosphere of the following composition: 0.25 vol.% of SO2 and 99.75 vol.% of Ar at 600 °C for 5 h. As a consequence, thin compact scale was formed on steel surface.
This scale consisted of three different zones. An amorphous zone was formed close to steel surface. Then, nanocrystalline Zone could be observed. Finally, larger grains were formed during the corrosion process. The analysis of the chemical composition revealed higher concentration of chromium near steel surface. In contrast, to chromium, the content of iron, increased near the scale surface. It was found out that the (Cr, Mn, Fe)5O12 phase appeared in the thin scale.
Thin Sol-Gel Alumina Coating as Protection of a 9% Cr Steel Against Flue Gas Corrosion at 650 °C
(2018)
Samples of sol-gel alumina coated and uncoated P92 steel were exposed to flue gas at 650 °C for 300 h. As result of this treatment a 50 µm thick bi-layered oxide scale had formed on the surface of the uncoated sample. Below the scale a 40 µm thick inner oxidation zone was detected. In contrast, the porous, micron thick alumina coating enabled the formation of a chromium oxide scale with a thickness of some nanometers at the interface between steel substrate and coating. In this case high temperature corrosion of the steel was prevented so far.
Technically relevant P92 steel (9% Cr) was coated with a micron-thick porous alumina layer prepared by sol-gel technique and treated with flue gas (60 CO2-30 H2O-2 O2-1 SO2-7 N2 (mole fraction in %)) at 650 ° to mimic an oxyfuelcombustion process. Local defects in the coating were marked using focused ion beam (FIB) technique and were inspected after exposition to hot flue gas atmosphere at 300, 800, and 1300 h, respectively. Local defects like agglomerated alumina sol particles tend to spall off from the coating uncovering the underlying dense chromia scale. Re-coating was found to restore the protection ability from oxidation when repeatedly treated with hot flue gas. Cracks and voids did not promote the local oxidation due to the formation of crystalline Mn/S/O species within and on top of the coating. The protective character of the steel-coating system is a result of (i) the fast formation of a dense chromia scale at the surface of sol-gel alumina-coated P92 steel bars in combination with (ii) the porous alumina coating acting as diffusion barrier, but also as diffusion partner in addition with (iii) fast Mn outward diffusion capturing the S species from flue gas.
T92 steel was oxidized at 650 °C for 1000 h in dry and wet oxyfuel gases. The microstructure of inner oxide layer was investigated using scanning transmission electron microscopy and energy dispersive spectroscopy on thin lamellas of oxide cross-sections. The oxides were composed of fine equiaxed grains and separated into Fe-rich and Cr-rich regions. Fe-rich regions were wustite and iron sulphide while Cr-rich regions consisted of Fe-Cr spinel with different stoichiometries. Precipitates of (W,Mo)-rich oxides were formed within the oxide scale and beneath the oxide/alloy interface. Often iron sulphide and (W,Mo)-rich oxide were surrounded by Cr-rich spinel.
Microstructure, smoothening effect, and local defects of alumina sol-gel coatings on ground steel
(2017)
Porous alumina films with thicknesses of a few microns were prepared via a dip-coating technique on steel P92. The coating is shown to protect the steel against massive corrosion, which is typical in the hot reactive environment of coal fired power plants. To mimic real conditions ground steel plates were coated with a boehmite-sol. This leads to an overall smoothing of the formerly rough surface. In the following short annealing step the inner porous construction with worm-like particles consisting of nano-crystallites and amorphous alumina is formed. Due to the simultaneous diffusion of chromium and iron ions out of the bulk steel material into the porous alumina coating, a dense interface with satisfactory adhesion is formed. However, the film exhibits few local defects like cracks or dense alumina nodules caused by steep edges in the ground surface or agglomeration of boehmite-sol components, respectively. Cracks especially have to be avoided. This problem can be overcome so far by slight modifications in the sol preparation process and surface treatment of the substrates. Nevertheless the results demonstrate the potential of sol-gel based alumina coatings as a time- and cost-saving protection type for commercial steel P92.
Future coal power plants will in case of oxyfuel combustion be operated with altered atmospheres. Hence, corrosion attack might become more severe and steels have to be protected. An alumina-sol was used to coat X20CrMoV12-1 (X20) with alumina to test the protection. Testing was performed at 600 °C in flowing H2O–CO2–O2 and static laboratory air for 1000 h. Oxidation under air is minor compared to exposure in oxyfuel atmosphere. In both cases a multilayered oxide (hematite, magnetite, spinel) was formed on uncoated steels. Carburization appeared on uncoated X20 in H2O–CO2–O2. The coating demonstrates a high protection.
In Kohlekraftwerken mit Oxyfuel-Technologie erfolgt die Verbrennung unter Zufuhr von reinem Sauerstoff. Damit steht für die Abscheidung und Speicherung von CO2 ein Rauchgas mit hohem CO2-Anteil zur Verfügung (CCS-Technologie). Aufgrund dieses Verbrennungsprozesses ändert sich im Wesentlichen die Rauchgaszusammensetzung hin zu hohem H2O- und SO2 -Anteil. Deshalb wurden in verschiedenen Laboratorien kommerzielle Kraftwerksstähle unter den entsprechenden korrosiven Bedingungen getestet. Im Vergleich zur herkömmlichen Verbrennungsmethode zeigten die ferritisch-martensitischen Stähle schon nach 1000 h Auslagerungszeit unter Oxyfuel-Bedingungen eine durch einen deutlich erhöhten Materialverlust gekennzeichnete Korrosion. Eine Möglichkeit um dennoch die Lebensdauer dieser Stähle zu gewährleisten, besteht im Aufbringen geeigneter Schutzschichten auf die Stahloberfläche. Die vorliegende Arbeit befasst sich mit der Herstellung und Bewertung von Sol-Gel-Aluminiumoxidschichten als Schutz vor Korrosion in Oxyfuel-Rauchgas-Atmosphäre. Diese wurden auf den warmfesten Stahl X20CrMoV12-1 (X20) mittels der Tauchmethode aufgebracht. Anschließend erfolgte eine Auslagerung der beschichteten Proben für 1000 h bei 600 °C in einer H2O-CO2-O2-SO2 -Atmosphäre.
Im Vergleich zum unbeschichteten Stahl X20 war der Materialverlust des beschichteten Stahls deutlich geringer. Insbesondere konnte durch die Aluminiumoxidschicht der Transport von CO2 und SO2 zur Stahloberfläche verhindert werden.
In Kohlekraftwerken mit Oxyfuel-Technologie erfolgt die Verbrennung unter Zufuhr von reinem Sauerstoff. Damit steht für die Abscheidung und Speicherung von CO2 ein Rauchgas mit hohem CO2-Anteil zur Verfügung (CCS-Technologie). Aufgrund dieses Verbrennungsprozesses ändert sich im Wesentlichen die Rauchgaszusammensetzung hin zu hohem H2O- und SO2 -Anteil. Deshalb wurden in verschiedenen Laboratorien kommerzielle Kraftwerksstähle unter den entsprechenden korrosiven Bedingungen getestet. Im Vergleich zur herkömmlichen Verbrennungsmethode zeigten die ferritisch-martensitischen Stähle schon nach 1000 h Auslagerungszeit unter Oxyfuel-Bedingungen eine durch einen deutlich erhöhten Materialverlust gekennzeichnete Korrosion. Eine Möglichkeit um dennoch die Lebensdauer dieser Stähle zu gewährleisten, besteht im Aufbringen geeigneter Schutzschichten auf die Stahloberfläche. Die vorliegende Arbeit befasst sich mit der Herstellung und Bewertung von Sol-Gel-Aluminiumoxidschichten als Schutz vor Korrosion in Oxyfuel-Rauchgas-Atmosphäre. Diese wurden auf den warmfesten Stahl X20CrMoV12-1 (X20) mittels der Tauchmethode aufgebracht. Anschließend erfolgte eine Auslagerung der beschichteten Proben für 1000 h bei 600 °C in einer H2O-CO2-O2-SO2 -Atmosphäre.
Im Vergleich zum unbeschichteten Stahl X20 war der Materialverlust des beschichteten Stahls deutlich geringer. Insbesondere konnte durch die Aluminiumoxidschicht der Transport von CO2 und SO2 zur Stahloberfläche verhindert werden.