Single walled carbon nanotubes (SWNT) have been produced in an electric arc discharge by using a graphite rod as anode which is filled with a powder mixture of graphite and metallic catalysts like nickel and yttrium. The soot material containing approximately a third of SWNT was collected from the cathode region as a soft, voluminous material. The main by-products in this process are amorphous carbon and graphitic nanoparticles which have to be removed by an appropriate purification process. The as-produced soot material was purified by gas phase oxidation in air at 355 °C. The oxidation of amorphous carbon in air is advantageous against wet chemical methods because it is better controllable. Thermogravimetric analysis and electron microscopy were used to investigate the oxidation behavior of the different kinds of carbon. Oxidation of SWNT and amorphous carbon occurs simultaneously even at moderate temperatures, whereas amorphous carbon is more rapidly oxidized than SWNT. For optimizing the purification procedure by gas phase oxidation, kinetic studies were used to determine the oxidation time for each component in the soot at a given temperature. So it is possible to remove the amorphous carbon quantitatively with minimal losses of SWNT. But it was found that graphitic nanoparticles have the highest stability against oxidation and could therefore not be quantitatively removed by this method without the complete destruction of SWNT. Therefore, the electric arc discharge process has to be a controlled process for minimum production of graphitic nanoparticles to obtain a material with a high content of SWNT.
Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.
T92 steel was oxidized at 650 °C for 1000 h in dry and wet oxyfuel gases. The microstructure of inner oxide layer was investigated using scanning transmission electron microscopy and energy dispersive spectroscopy on thin lamellas of oxide cross-sections. The oxides were composed of fine equiaxed grains and separated into Fe-rich and Cr-rich regions. Fe-rich regions were wustite and iron sulphide while Cr-rich regions consisted of Fe-Cr spinel with different stoichiometries. Precipitates of (W,Mo)-rich oxides were formed within the oxide scale and beneath the oxide/alloy interface. Often iron sulphide and (W,Mo)-rich oxide were surrounded by Cr-rich spinel.