Filtern
Dokumenttyp
- Posterpräsentation (3)
- Beitrag zu einem Tagungsband (2)
- Vortrag (1)
Sprache
- Englisch (6)
Schlagworte
- Extended Interim Storage (3)
- Long-Term Safety Assessment (3)
- Metal Seal Aging (3)
- Restoring Force Degradation (3)
- Temperature-Dependent Performance (3)
- Interim storage (2)
- Metal seal (2)
- Aging (1)
- Metal seals (1)
- Numerical simulation (1)
Organisationseinheit der BAM
Eingeladener Vortrag (wissenschaftliche Konferenzen)
- nein (1)
For bolted casks for used fuel and high level waste the sealing system has an important impact of ensuring safe enclosure of the inventory The used metal seals show some changes over time which have been addressed for nearly 15 years in running experiments at BAM The observed changes are temperature de pendent and therefore it is expected that test s at higher temperature allow for an acceleration of the effects and ideally the proposal of an ageing model covering the expected time of use . Nevertheless, questions concerning the influence of the experimental approach on the results and effects taking place at the initial days of ageing remain. To address these a new project was launched to give a better understanding of the seal behavior.
In Germany, spent fuel and heat generating radioactive waste is stored in casks for transport and storage (DPCs). The storage licenses were granted for up to 40 years. Due to the delay in identifying a final repository site for such radioactive waste, the storage periods are to be extended significantly. The objective of our research work is to collect additional material data for metal seals in order to be able to better assess the long-term safety of the sealing system of the casks for a period of up to 100 years.
A principal safety consideration for the DPCs is the long-term performance of bolted lid sealing systems utilizing metal seals to ensure the safe enclosure of the radioactive inventory during interim storage. To assess the sealing behavior, it is necessary to examine the aging-dependent residual restoring force for the metal seals and the usable resilience. By investigating the change in these values as a function of time and temperature, further insight can be gained into the assessment of long-term safety for extended interim storage.
In the present study, the restoring force of metal seals with an outer aluminum jacket and a torus diameter of 9.9 mm was measured continuously. For this purpose, a specially designed device equipped with a load cell was used under isothermal conditions. As part of the investigation, the level and rate of decrease of the restoring seal force were recorded over test periods of one and two months. The seal temperature was set to 35 °C, 75 °C, 100 °C, 125 °C, and 150 °C, respectively. A direct correlation was observed between the temperature of the seal, the level of the restoring force after compressing and heating the seal, and the drop-off characteristics of the restoring force. It was found that in our test device the force level immediately after reaching the respective temperature is lower for higher seal temperatures, while the drop rate of the restoring force is higher. This paper describes the experimental setting and discusses first results in comparison with our long-term discontinuous measurements.
In Germany, the search for a disposal site for heat-generating radioactive waste will take decades longer than originally assumed. Transport and storage casks must therefore ensure safe containment for extended interim storage periods, possibly over 100 years. In order to maintain the required leak tightness, spring core metal seals with aluminum or silver cladding are used. As sealing force decreases over time, BAM has been conducting tests for over 15 years to prove their long-term reliability. This work - a joint project of BASE and BAM - aims to obtain additional material data using a new device for continuous measurement of compression force over time and temperature for lifetime prediction models and is supported by FEM simulations. Initial tests on aluminum and silver seals have been completed, and first results are presented.
In Germany, spent fuel and heat generating radioactive waste is stored in casks for transport and storage (DPCs). The storage licenses were granted for up to 40 years. Due to the delay in identifying a final repository site for such radioactive waste, the storage periods are to be extended significantly. The objective of our research work is to collect additional material data for metal seals in order to be able to better assess the long-term safety of the sealing system of the casks for a period of up to 100 years.
A principal safety consideration for the DPCs is the long-term performance of bolted lid sealing systems utilizing metal seals to ensure the safe enclosure of the radioactive inventory during interim storage. To assess the sealing behavior, it is necessary to examine the aging-dependent residual restoring force for the metal seals and the usable resilience. By investigating the change in these values as a function of time and temperature, further insight can be gained into the assessment of long-term safety for extended interim storage.
In the present study, the restoring force of metal seals with an outer aluminum jacket and a torus diameter of 9.9 mm was measured continuously. For this purpose, a specially designed device equipped with a load cell was used under isothermal conditions. As part of the investigation, the level and rate of decrease of the restoring seal force were recorded over test periods of one and two months. The seal temperature was set to 35 °C, 75 °C, 100 °C, 125 °C, and 150 °C, respectively. A direct correlation was observed between the temperature of the seal, the level of the restoring force after compressing and heating the seal, and the drop-off characteristics of the restoring force. It was found that in our test device the force level immediately after reaching the respective temperature is lower for higher seal temperatures, while the drop rate of the restoring force is higher. This paper describes the experimental setting and discusses first results in comparison with our long-term discontinuous measurements.
In Germany, spent fuel and heat generating radioactive waste is stored in casks for transport and storage (DPCs). The storage licenses were granted for up to 40 years. Due to the delay in identifying a final repository site for such radioactive waste, the storage periods are to be extended significantly. The objective of our research work is to collect additional material data for metal seals in order to be able to better assess the long-term safety of the sealing system of the casks for a period of up to 100 years.
A principal safety consideration for the DPCs is the long-term performance of bolted lid sealing systems utilizing metal seals to ensure the safe enclosure of the radioactive inventory during interim storage. To assess the sealing behavior, it is necessary to examine the aging-dependent residual restoring force for the metal seals and the usable resilience. By investigating the change in these values as a function of time and temperature, further insight can be gained into the assessment of long-term safety for extended interim storage.
In the present study, the restoring force of metal seals with an outer aluminum jacket and a torus diameter of 9.9 mm was measured continuously. For this purpose, a specially designed device equipped with a load cell was used under isothermal conditions. As part of the investigation, the level and rate of decrease of the restoring seal force were recorded over test periods of one and two months. The seal temperature was set to 35 °C, 75 °C, 100 °C, 125 °C, and 150 °C, respectively. A direct correlation was observed between the temperature of the seal, the level of the restoring force after compressing and heating the seal, and the drop-off characteristics of the restoring force. It was found that in our test device the force level immediately after reaching the respective temperature is lower for higher seal temperatures, while the drop rate of the restoring force is higher. This paper describes the experimental setting and discusses first results in comparison with our long-term discontinuous measurements.
In Germany, the search for a disposal site for heat-generating radioactive waste will take decades longer than originally assumed. Transport and storage casks must therefore ensure safe containment for extended interim storage periods, possibly over 100 years. In order to maintain the required leak tightness, spring core metal seals with aluminum or silver jacket are used. As sealing force decreases over time, BAM has been conducting tests for over 15 years to study their long-term reliability. This work - a joint project of BASE and BAM - aims to obtain additional material data using a new device for continuous measurement of compression force over time and temperature for lifetime prediction models and is supported by FEM simulations. After successful testing of the new test device, tests at different temperature levels with aluminum and silver seals have been completed, and preliminary results are presented.