Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (22)
- Beitrag zu einem Tagungsband (7)
- Sonstiges (1)
Schlagworte
- Ellipsometry (7)
- Gas sensing (4)
- Optical properties (4)
- Ellipsometrie (3)
- Thin films (3)
- Doped tin oxide (2)
- Haftfestigkeit (2)
- Kohlenstoffschichten (2)
- Oberflächentechnik (2)
- Qualitätssicherung (2)
Organisationseinheit der BAM
Thin films of MgF2 have been deposited on silicon wafers in optical quality with a novel sol-gel deposition process at temperatures as low as 100 °C. The properties of the fluoride layers are compared to bulk MgF2 with respect to the optical constants. By employing spectroscopic mapping ellipsometry, the uniformity of the thickness of fluoride layers is confirmed to be within acceptable limits for optical applications. The optical constants are close to the bulk data. High-quality low-index films of suitable and homogeneous thickness have already been produced on a laboratory scale.
Embedding of information on surfaces is state of the art for identification testing in which public, hidden and forensic features are used. In many instances, the legal authentication of a product, a material or a document is required. Among the surface-based encoded labels, bar codes and data matrices are most frequently applied. They are publicly visible. The material itself is irrelevant, only a sufficient optical contrast is required.
However, a strong material dependence of the label can be achieved by means of Fabry-Perot layer stacks. Stack designs are described with regard to all three security levels: public features (e.g. color and tilt effect) perceptible by the human eye, hidden features (e.g. optical response in a given spectral range) detectable by commonly available instruments and forensic features (ellipsometric quantities Ψ and Δ as a function of wavelength λ and angle of incidence AOI) only detectable by sophisticated instruments.
Regarding material-correlated authentication, ellipsometric quantities Ψ and Δ are used as encoded forensic features for the first time. Hence, Fabry-Perot layer stacks as information carriers in combination with imaging ellipsometry as optical read-out system provide all-in-one anti-counterfeiting capabilities.
MgF2 and TiO2 single layers and layer stacks were produced by a spin-coating sol-gel process. The final temperature treatment was carried out at 100 °C. The layers were deposited onto silicon and fused silica substrates and were analysed by means of atomic force microscopy, X-ray photoelectron spectroscopy, transmission electron microscopy, ellipsometry, and UV-vis transmission spectroscopy. MgF2 and TiO2 single layers have morphological and optical properties comparable with physical vapour deposited layers. By using spectroscopic mapping ellipsometry, a good inter- and intra-sample homogeneity was confirmed. Multiple deposition steps result in a linear increase of layer thickness. Various films were deposited with thicknesses between 25 nm and 350 nm.
It was shown that the low temperature sol-gel process results in films of optical quality. Anti-reflective and high reflective layer stacks consisting of MgF2 and TiO2 were designed and can be produced now by a sol-gel process, whereas the MgF2 layers in the layer stacks contains also traces of MgF2-2xOx.
Standardisation of ellipsometry is mainly based on three documents: pioneering work at NIST [1] on film standards, a publicly available specification and stan-dard testing procedure [2] for real-world samples by BAM and a standard specification for integrated metrology by SEMI [3]. Other activities refer to inter-laboratory comparisons for selected layer/substrate systems and analytical methods including ellipsometry [4] and the development of combined standards for thickness d and step height h [5].
Generally, precision of ellipsmetry in terms of raw data Ψ and Δ meets the major demands for all ellipsometric principles (RPE, RAE, PME, RCE, NE).
As a result, fingerprint capabilty is al-most perfect for various layer/substrate systems. However, this is not true for accuracy in terms of physical quantities such as thickness d, optical (n, k) and dielectric constans (ε1, ε2,) as modelling is required. Hence, the layer/substrate and material dependent validation of models is nowadays a key issue.
In contrast to the sub-nanometer sensi-tivity in vertical direction, the effective lateral resolution of almost all ellipso-metric principles except for imaging null
ellipsometry is rather poor, usually be-yond 100 µm.
Hence, nanometer-scaled homogeneity testing and the measurement of micro- and nanopatterned structures is not feasible by standard configurations.
Hydrogenated amorphous carbon layers were deposited on BK7 glass in a plasma-assisted chemical vapor deposition
process. Low and high refracting films with thicknesses d ranging from 11 nm to 5.8 µm were produced having refractive
indices n between 1.68 and 2.41 and linear absorption coefficients of α~100 cm-1 and α~20000 cm-1 at 800 nm wavelength as a result of different plasma modes. Laser ablation thresholds Fth in dependence on d were determined using 30-fs laser pulses. Low absorbing layers show a constant Fth while Fth increases with rising d up to the optical penetration depth of light α-1 for high absorbing films.
The synthesis of polymerlike amorphous carbon (a-C:H) thin-films by microwave excited collisional hydrocarbon plasma process is reported. Stable and highly aromatic a-C:H were obtained containing significant inclusions of poly(p-phenylene vinylene) (PPV). PPV confers universal optoelectronic properties to the synthesized material. That is a-C:H with tailor-made refractive index are capable of becoming absorption-free in visible (red)-near infrared wavelength range. Production of large aromatic hydrocarbon including phenyl clusters and/or particles is attributed to enhanced coagulation of elemental plasma species under collisional plasma conditions. Detailed structural and morphological changes that occur in a-C:H during the plasma synthesis are also described.
Iron-doped SnO2 coatings were deposited in a 50 kHz DC-pulsed magnetron sputtering discharge. The pulses had a duration of 4 µs in selected gas mixtures from pure argon up to
60% of oxygen at a constant total pressure of 0.2 Pa. A single target of SnO2 with Fe inset was used. The mass spectrometry study detected the gas-related ions Ar+, O2+ and O+, where the last one becomes the dominant positive ion at higher oxygen contents. Atomic oxygen ions had a higher energy as it resulted from the collision-caused dissociation on the target surface. The tin-related species were detected as Sn+ and SnO+. SnO2+ species were not detected. The deposition rate decreased by using gas mixtures with oxygen as well as the corresponding amount of Sn-related species in the plasma. The increase of oxygen also increased significantly the sheet resistance of the films. The XPS study showed that the iron concentration decreased by using additional oxygen. But the O/Sn ratio in the coatings was constant, contrary to the increased FeO/Fe ratio in the films. An additional analysis of the coatings by spectroscopic ellipsometry has shown a dependence of the polarizability and the permittivity on the amount of oxygen used during the deposition. In contrast, the study has found no such dependence for the absorption of the layers.
Die Oberflächentechnik ist eine Schlüsseltechnologie in nahezu zu allen industriellen Branchen. Mit Ausnahme der mechanischen Stabilität, die das Substrat bereitstellt, werden verschiedenartigste Funktionen materialsparend, zum Teil hochintegriert mit maßgeschneiderten Schichtdesigns unter Ausnutzung von Nano- und Quanteneffekten auf Oberflächen appliziert. Ein Großteil der Fertigungskosten in der Mikro- und Nanotechnik wird durch Reinräume und die Umsetzung ausgeklügelter Reinigungsstrategien zur Vermeidung von Restverschmutzungen und partikulären Belegungen
verursacht, da diese unweigerlich zum Bauteilversagen führen. Die Validierung des Reinigungszustandes ist somit von zentraler Bedeutung für die Schichtqualität und Produktfunktionalität. Dies gilt in Abhängigkeit von der Applikation und den vertikalen Schicht- bzw. lateralen Strukturdimensionen sowohl für Fertigungsprozesse im Reinraum als auch für solche in robuster Umgebung. In der Praxis kommt es häufig vor, dass man mikroskopisch scheinbar saubere Substrate erst durch die Beschichtung „enttarnt" und dann Defekte oft mit bloßem Auge sichtbar werden. Noch problematischer ist der Einbau von Verunreinigungen während der Schichtabscheidung, die zunächst nicht sichtbar sind, dann aber zum Bauteilversagen führen.
The present study investigates the use of imaging and mapping ellipsometry to determine the properties of non-ideal and patterned thin film samples. Samples which are candidates for future references and standards were prepared for this purpose. The samples investigated were lithographically patterned SiO2 and photoresist layers. The thickness and the optical constants of the two materials were determined using spectroscopic ellipsometry in the visible spectral range. On a larger lateral scale of several mm lateral resolution, the homogeneity was investigated using a goniospectral rotating compensator ellipsometer. A nulling imaging ellipsometer was used to determine the properties of the sample on a smaller scale of 25–150 µm.
Coatings deposited by magnetron co-sputtering from a single RF magnetron with a ceramic SnO2 target with iron inset in argon plasma were studied. The mass spectra of the process identified Sn+ and SnO+ species as the dominant species sputtered from the target, but no SnO2+ species were detected. The dominant positive ions in argon plasma are Ar+ species. The only detected negative ions were O-. Sputtered neutral tin related species were not detected. Iron related species were also not detected because their concentration is below the detection limit.
The concentration of iron dopant in the tin oxide coatings was controlled by the RF bias applied on the substrate holder while the discharge pressure also has some influence. The iron concentration was in the range from 0.9 at.% up to 19 at.% increasing with the substrate bias while the sheet resistivity decreases. The stoichiometry ratio of O/(Sn + Fe) in the coatings increased from 1.7 up to 2 in dependence on the substrate bias from floating bias (- 5 V) up to - 120 V of RF self-bias, respectively. The tin in the coatings was mainly bonded in Sn4 + state and iron was mainly in Fe2 + state when other tin bonding states were detected only in a small amounts. Iron bonding states in contrary to elemental compositions of the coatings were not influenced by the RF bias applied on the substrate.
The coatings showed high transparency in the visible spectral range. However, an increased metallic behavior could be detected by using a higher RF bias for the deposition. The X-ray diffraction patterns and electron microscopy pictures made on the coatings confirmed the presence of an amorphous phase.
Single Femtosecond Laser-Pulse-Induced Superficial Amorphization and Re-Crystallization of Silicon
(2021)
Superficial amorphization and re-crystallization of silicon in <111> and <100> orientation after irradiation by femtosecond laser pulses (790 nm, 30 fs) are studied using optical imaging and transmission electron microscopy. Spectroscopic imaging ellipsometry (SIE) allows fast data acquisition at multiple wavelengths and provides experimental data for calculating nanometric amorphous layer thickness profiles with micrometric lateral resolution based on a thin-film layer model. For a radially Gaussian laser beam and at moderate peak fluences above the melting and below the ablation thresholds, laterally parabolic amorphous layer profiles with maximum thicknesses of several tens of nanometers were quantitatively attained. The accuracy of the calculations is verified experimentally by high-resolution transmission electron microscopy (HRTEM) and energy dispersive X-ray spectroscopy (STEM-EDX). Along with topographic information obtained by atomic force microscopy (AFM), a comprehensive picture of the superficial re-solidification of silicon after local melting by femtosecond laser pulses is drawn.
Background: Gas sensors are very important in several fields like gas monitoring, safety and environmental applications. In this approach, a new gas sensing concept is investigated which combines the powerful adsorption probability of metal oxide conductive sensors (MOS) with an optical ellipsometric readout. This concept Shows promising results to solve the problems of cross sensitivity of the MOS concept.
Results: Undoped tin oxide (SnOx) and iron doped tin oxide (Fe:SnOx) thin add-on films were prepared by magnetron sputtering on the top of the actual surface plasmon resonance (SPR) sensing gold layer. The films were tested for their sensitivity to several gas species in the surface plasmon resonance enhanced (SPREE) gas measurement. It was found that the undoped tin oxide (SnOx) shows higher sensitivities to propane (C3H8) then to carbon monoxide (CO). By using Fe:SnOx, this relation is inverted. This behavior was explained by a change of the amount of binding sites for CO in the layer due to this iron doping. For hydrogen (H2) no such relation was found but the sensing ability was identical for both layer materials. This observation was related to a different sensing mechanism for H2 which is driven by the Diffusion into the layer instead of adsorption on the surface.
Conclusion: The gas sensing selectivity can be enhanced by tuning the properties of the thin film overcoating. A relation of the binding sites in the doped and undoped SnOx films and the gas sensing abilities for CO and C3H8 was found. This could open the path for optimized gas sensing devices with different coated SPREE sensors.
The 7th International Conference on Spectroscopic Ellipsometry (ICSE-7) was held in Berlin in June 2016, jointly organised by ICSE and BAM. The publication of the proceedings special issue in Applied Surface Science follows this event. In the special issue, about 100 articles on current topics of optics and surface science related to ellipsometry, polarimetry, and similar techniques are presented, underpinning the high significance of these techniques for many fields of materials science.
In this study, thickness related changes of the optical properties of doped tin oxide were studied. Two different sets of samples were prepared. The first set was doped with iron or nickel on silicon substrate with thicknesses of 29–56 nm, the second was iron doped on gold/glass substrate with 1.6–6.3 nm. The optical constants were determined by using spectral ellipsometry (SE) followed by modelling of the dielectric function with an oscillator model using Gaussian peaks. The analysis of the optical constants shows a dependence of the refraction and the absorption on the thickness of the doped tin oxide coating. In addition to the tin oxide absorption in the UV, one additional absorption peak was found in the near-IR/red which is related to plasmonic effects due to the doping. This peak shifts from the near-IR to the red part of the visible spectrum and becomes stronger by reducing the thickness, probably due to the formation of metal nanoparticles in this layer. These results were found for two different sets of samples by using the same optical model. Afterwards the second sample set was tested in the Surface Plasmon Resonance Enhanced Ellipsometric (SPREE) gas measurement with CO gas. It was found that the thickness has significant influence on the sensitivity and thus the adsorption of the CO gas. By increasing the thickness from 1.6 nm to 5.1 nm, the sensing ability is enhanced due to a higher coverage of the surface with the over coating. This is explained by the high affinity of CO molecules to the incorporated Fe-nanoparticles in the tin oxide coating. By increasing the thickness further to 6.3 nm, the sensing ability drops because the layer disturbs the SPR sensing effect too much.
Visualization of surface modifications may be very challenging for coating/substrate systems of either almost identical optical constants, e.g. transparent films on substrates of the same material, or minor film thickness, substance quantity and affected area, e.g. ultra-thin or island films. Methods for visualization are optical microscopy (OM), imaging ellipsometry (IE), and referenced spectroscopic ellipsometry (RSE). Imaging ellipsometry operates at oblique incidence near Brewster angle of the bare, clean or unmodified substrate. In this configuration, reflected intensities are rather weak. However, the contrast to add-on and sub-off features may be superior. Referenced spectroscopic ellipsometry operates in a two-sample configuration but with much higher intensities. In many cases, both ellipsometric techniques reveal and visualize thin films, printed-pattern, laser-induced changes, and impurities better than optical microscopy. In particular for stratified homogeneous modifications, ellipsometric techniques give access to modelling and hence thickness determination. Modifications under investigation are polymer foil residue on silicon, laser-induced changes of ta-C:H coatings on 100Cr6 steel, imperfections of ta-C:H on thermal silicon oxide, degradation of glass, thin film tin oxide pattern on silicon, printed and dried pattern of liquids such as deionized water, cleaning agents, and dissolved silicone. © 2016 Elsevier B.V. All rights reserved.
Auf dem Weg zu Industrie 4.0: Bestimmung von Messunsicherheitsbudgets in der Oberflächentechnik
(2019)
Vorgestellt wurde die Bestimmung von Messunsicherheitsbudgets für sehr unterschiedliche physikalische Größen, die in der Oberflächentechnik von hoher Relevanz sind: Stufenhöhe h, Schichtdicke d, Eindringhärte HIT und Haftfestigkeit. Die Unterschiede betreffen die Art der Prüfmethodik (optisch zerstörungsfrei vs. mechanisch invasiv/zerstörend), die laterale Größe des Integrationsgebietes der Messung (lokal: nano bis sub-mikro vs. global: mikro bis makro) und die Art der Bestimmung von Messunsicherheitsbudgets (physikalische Größen: direkt rückführbar; Werkstoffkenngröße: genormt; Systemkenngröße: genormt).
Im Rahmen von Industrie 4.0 werden ausgehend der geforderten Spezifikation des beschichteten Produkts (Mittelwert mit Vertrauensbereich oder Mindestwert) durchgehende Toleranzbänder zur Oberflächenmodifizierung/Beschichtung des Substrats, einhergehend mit Prozessfenstern, die diese Toleranzbänder garantieren, erforderlich, die zuverlässig erfasst werden müssen. Die Frage der anzuwendenden Mess- und Prüftechnik und die damit notwendige Betrachtung von Messunsicherheitsbudgets ist für die Digitalisierung von Konditionierungs-, Zustands-, Regel- und Steuergrößen unverzichtbar. Mit Blick auf die Einhaltung von Prozessfenstern und die dafür notwendige Prozessführung wird technologisches Kern-Know-how digitalisiert, das es unbedingt zu schützen gilt. Nur lokale Netze können diese Sicherheit garantieren, in globalen Netzen ist die Datensicherheit bestenfalls maximierbar
Most of the polymeric materials used are easy to ignite and show extensive flame spread along their surfaces. Apart from extensive heat release rates, their short time to ignition (tig), in particular, is a key fire hazard. Preventing ignition eliminates fire hazards completely. Protection layers that shift tig by more than an order of magnitude are powerful flame retardancy approaches presenting an alternative to the usual flame retardancy concepts.
Coatings are proposed that consist of a three-layer system to ensure adhesion to the substrate, acting as an infrared (IR) mirror and protecting against oxidation. The IR-mirror layer stack is realised by physical vapour deposition in the sub-micrometre (<1 µm) range, reducing heat absorption by up to an order of magnitude. Not only is the ease of ignition diminished (tig is increased by several minutes), the flame spread and fire growth indices are also remarkably reduced to as little as 1/10 of the values of the uncoated polymers open for further optimization. Sub-micrometre thin IR-mirror coatings yielding surface absorptivity <0.1 are proposed as a novel and innovative flame retardancy approach.