Nanocomposites with a predominantly exfoliated morphology were prepared by melt blending of organically modified doubled layered hydroxide (LDH) and low density polyethylene (PE). The prepared materials were investigated by differential scanning calorimetry (DSC) and in detail by dielectric spectroscopy. The DSC experiments show that the degree of crystallinity decreases linearly with increasing content of the LDH. The extrapolation of this dependence to zero results in a limiting concentration of ca. 50 wt % LDH were the crystallization of PE is completely suppressed by the nanofiller. The dielectric response of pure polyethylene shows different weak relaxation processes. The intensity of dynamic glass transition (β-relaxation) increases with the concentration of LDH. This is attributed to the increasing concentration of the exchanged anion dodecyl benzene sulfonate (SDBS). The SDBS molecules are strongly adsorbed at the exfoliated LDH layers. Therefore, a detailed analysis of the β-relaxation provides information about the structure and the molecular dynamics in the interfacial region between the exfoliated LDH layers and the polyethylene matrix. This analysis shows that the β-relaxation region consists of two processes: both of them obey glassy dynamics. The difference in corresponding Vogel (ideal glass transition) temperatures is about 30 K. The relaxation process at lower frequency is assigned to polyethylene segments with a reduced molecular mobility close to LDH layers. The process at higher frequencies is related to polyethylene segments in a farer distance for the surface of the nanofiller. In the nanocomposite materials an additional process due to Maxwell-Wagner-Sillars (MWS) polarization was observed. The time constant of this MWS process can be correlated with characteristic length scales in nanocomposites and therefore provides additional information on dispersion and delamination/exfoliation of the LDH layers in these materials.
Dielectric spectroscopy and temperature-modulated differential scanning calorimetry are employed to study the molecular dynamics of oligomeric poly(propylene glycol) (PPG) melts of different molecular weights confined to nanoporous glasses (pore sizes 2.5, 5.0, 7.5 and 20 nm). Moreover, the results obtained for the polymers are compared with those for the corresponding monomer. The experimental results are discussed in the framework of the interplay of confinement and adsorption effects. For large pore sizes (> 5 nm) a speeding up of the molecular dynamics is observed (the confinement effect), whereas for small pore sizes (< 5 nm) a slowing down of the segmental fluctuations is found (the adsorption effect). In addition, a minimal length scale for the glass transition of 1.6 nm is estimated for PPG confined in nanoporous glasses. This supports the idea that the molecular motions responsible for the glassy dynamics must be describable by a characteristic length scale.
Polarized Raman scattering investigations are carried out to investigate the conformations of the macromolecules inside the pores. These experiments show that the confined polymer chains are locally stretched. This effect increases with decreasing pore size.
A broadband dielectric study of the dispersions of silica spheres (Aerosil 380) in octylcyanobiphenyl (8CB) with densities between 0.083 and 10 g of silica per 1 cm3 of liquid crystal (LC) is reported. High values of silica densities were achieved for the first time to observe the behaviour of the LC monolayer on the surface of the silica particles. The relaxation characteristic of the bulk LC is noticed especially for the samples with low silica densities. Additionally, a slow relaxation was detected, even at temperatures for which the bulk LC is in the crystalline state. It was assigned to the surface layer of LC molecules. Remarkably, the temperature dependence of the relaxation rates for this slow process shows a behaviour typical for glass-forming liquids.
Nanocomposites were prepared by solution blending of polyhedral oligomeric silsesquioxane with phenethyl substituents (PhenethylPOSS) into poly(bisphenol A carbonate) (PBAC). The nanocomposites were investigated by dielectric spectroscopy, differential scanning calorimetry (DSC) and density measurements. PhenethylPOSS shows one relaxation process, the α-relaxation, confirmed by DSC investigations. PBAC shows a β-relaxation at lower and an α-relaxation at higher temperatures. With increasing PhenethylPOSS content the α-relaxation of the composites shifts to lower temperatures. Thus, incorporation of PhenethylPOSS leads to a plasticization of PBAC due to a decrease of the packing density which is rationalized by density measurements. For higher concentrations of PhenethylPOSS (>10 wt %) the α-relaxation of the polycarbonate matrix splits into two peaks. Moreover, close to the α-relaxation of PhenethylPOSS a third process is observed. These results indicate a phase separation into a PBAC matrix with a few percents of molecularly solved POSS and POSS-rich domains. These POSS-rich domains are surrounded by an interfacial layer of PBAC having a higher concentration of POSS than the matrix. A phase diagram is deduced providing a miscibility criterion. For the phase separated nanocomposites an interfacial polarization phenomena is observed. Using a simplified model the time constant of this process is correlated with the size of the PhenethylPOSS-rich domains and theire increasing size with the increase of the concentration of POSS.
A composite prepared from aerosil A380 and the liquid crystal (LC) 4-hexyl-4'-cyanophenyl benzoate (CP6B) was investigated by broadband dielectric spectroscopy in a large temperature range. The selected high silica density (ca. 7 g aerosil/1 g of CP6B) allows the observation of a thin layer (two-monolayer structure) adsorbed on the surface of the silica particles. For the composite one relaxation process is observed at frequencies much lower than that of the processes found for bulk CP6B. It is assigned to the dynamics of the molecules in the surface layer. The temperature dependence of its relaxation rates obeys the Vogel-Fulcher-Tammann law, which is characteristic for glass-forming liquids. The quasi 2D character of the observed glassy dynamics in the surface layer is discussed. The temperature dependence of the CP6B relaxation in the composite is compared with that of related hexylcyanobiphenyl molecules in the surface layer of aerosil composite with a similar concentration.