Nanoparticulate networks as fillers for polymer based nanocomposites offer an optimized, surfactant free distribution of the inorganic component. Additionally, their non-aggregated but interconnected nanoparticulate subunits can lead to new properties owing to special inherent solid state properties and/or spacial restrictions to the polymeric parts. In particular, polymer nanocomposites based on poly(methyl methacrylate) (PMMA) or poly(hydroxyethyl methacrylate) (PHEMA), filled with different nanoparticulate networks of AlOOH were synthesized using two advanced synthesis techniques. An ex situ method, in which a preformed AlOOH-gel was solvent exchanged by methyl methacrylate (MMA) and an in situ method, in which the AlOOH scaffold was prepared within hydroxyethyl methacrylate (HEMA), have been used to produce the materials described here through polymerization. On the MMA based composites the particles were removed by etching, yielding porous polymers. Promising for a broad variety of crystallisable networks within polymers, the phase transition of amorphous AlOOH within PMMA towards crystalline boehmite was performed using a hydrothermal method. The materials were characterized using transmission electron microscopy, X-ray diffraction, gel permeation chromatography, differential scanning calorimetry, IR-spectroscopy, UV/Vis spectroscopy and hardness measurements. Special material properties were investigated using thermogravimetry, thermomechanical analysis and dynamic mechanical analysis. Furthermore, interactions between PMMA segments and the AlOOH network were detailed studied using dielectric spectroscopy.
Dielectric spectroscopy in combination with temperature modulated differential scanning calorimetry and quasielastic/inelastic neutron scattering are employed to investigate the molecular (glassy) dynamics of poly(dimethyl siloxane) (PDMS) and poly(methyl phenyl siloxane) (PMPS) confined to random nanoporous glasses with nominal pore sizes between 2.5 nm and 20 nm. Inside the pores PDMS and PMPS have faster molecular dynamics than in the bulk state. Down to a pore size of 7.5 nm the temperature dependence of the relaxation times (or rates) obeys the Vogel/Fulcher/Tammann (VFT) equation where the data obtained from dielectric and thermal spectroscopy agree quantitatively. At a pore size of 5 nm this VFT-like temperature dependence changes to an Arrhenius behavior. At the same confining length scale the increment of the specific heat capacity at Tg normalized to the weight of the confined polymer vanishes. The results indicate that a minimal length scale seems to be relevant for glassy dynamics in both polymers although the estimated length scale of about 5 nm seems to a bit too large in comparison to other experimental results and theoretical approaches. Neutron scattering is employed to investigate methyl group reorientation and the fast segmental dynamics of both polymers in confinement. Although the methyl group rotation is a localized process these experiments show that a part of the methyl groups is immobilized by the confinement whereas the effects for PDMS are much more pronounced than for PMPS. With regard to the segmental dynamics, neutron scattering reveals a big difference in the behavior of both polymers. Whereas the data obtained for PMPS are in accord with a boundary layer formed at the surfaces of the nanopores, for PDMS a considerable amount of elastic scattering is observed. To explain this result it is assumed that some structure formation of PDMS takes place in the nanopores, although the thermal data show no crystallization or melting effects.
Dielectric spectroscopy and temperature modulated DSC are employed to study the molecular dynamics of oligomeric poly(propylene glycol) (PPG) melts of different molecular weights confined to nanoporous glasses (pore sizes 2.5, 5.0, 7.5 and 20 nm). Moreover the results obtained for the polymer are compared with the corresponding monomer. For large pore sizes an acceleration of the segmental dynamics compared to the bulk state is observed which is already known for low molecular-weight glass forming liquids. For smaller pore sizes the molecular dynamics is slower than in the bulk. The observed behavior is nearly independent of the molar mass of the polymer and of the treatment of internal glass surfaces. The experimental results are discussed in the frame of an interplay of confinement and adsorption effects. Moreover a length scale of about 1.6 nm is estimated as a minimal length scale for the cooperativity for the glass transition. In addition to the ?-relaxation the whole chain dynamics (normal mode relaxation) can be measured by dielectric spectroscopy because PPG has a dipole component parallel to the chain. For virgin internal surfaces the relaxation rate of the normal mode relaxation is shifted dramatically to lower relaxation rates. That can be explained by adsorption effects. For treated surfaces this effect is strongly reduced and it is concluded that also in this case the chain dynamics are influenced by geometric (confinement) effects.
The glassy dynamics of poly(propylene glycol) (PPG) and poly(dimethyl siloxane) (PDMS) confined to a nanoporous host system revealed by dielectric spectroscopy, temperature-modulated DSC and neutron scattering is compared. For both systems the relaxation rates estimated from dielectric spectroscopy and temperature-modulated DSC agree quantitatively indicating that both experiments sense the glass transition. For PPG the segmental dynamics is determined by a counterbalance of adsorption and confinement effect. The former results form an interaction of the confined macromolecules with the internal surfaces. A confinement effect originates from an inherent length scale on which the underlying molecular motions take place. The increment of the specific-heat capacity at the glass transition vanishes at a finite length scale of 1.8 nm. Both results support the conception that a characteristic length scale is relevant for glassy dynamics. For PDMS only a confinement effect is observed which is much stronger than that for PPG. Down to a pore size of 7.5 nm, the temperature dependence of the relaxation times follows the Vogel-Fulcher-Tammann dependence. At a pore size of 5 nm this changes to an Arrhenius-like behaviour with a low activation energy. At the same pore size vanishes for PDMS. Quasielastic neutron scattering experiments reveal that also the diffusive character of the relevant molecular motions --found to be characteristic above the glass transition-- seems to disappear at this length scale. These results gives further strong support that the glass transition has to be characterised by an inherent length scale of the relevant molecular motions.
The effect of a nanometer confinement on the molecular dynamics of poly(methyl phenyl siloxane) (PMPS) was studied by dielectric spectroscopy (DK), temperature modulated DSC (TMDSC) and neutron scattering (NS). DK and TMDSC experiments show that for PMPS in 7.5 nm pores the molecular dynamics is faster than in the bulk which originates from an inherent length scale of the underlying molecular motions. At a pore size of 5 nm the temperature dependence of the relaxations times changes from a Vogel-Fulcher-Tammann like behavior to an Arrhenius one. At the same pore size Dcp vanishes. These results give strong support that the glass transition has to be characterized by an inherent length scale of the relevant molecular motions. Quasielastic neutron scattering experiments reveal a strong change even in the microscopic dynamic.
The glassy dynamics of poly(propylene glycol) (PPG) and poly(methyl phenyl siloxane) (PMPS) confined to nanoporous glasses (pore sizes 2.520 nm) investigated by dielectric spectroscopy, temperature modulated DSC and neutron scattering is compared. For both systems the relaxation rates estimated from dielectric spectroscopy and temperature modulated DSC agree quantitatively indicating that both experiments sense the glass transition.
For PPG the glassy dynamics in nanopores is determined by a counterbalance of an adsorption and a confinement effect where the temperature dependence of the relaxation times obeys the Vogel/Fulcher/Tammann (VFT-) equation. The former effect results from an interaction of the confined macromolecules with the internal surfaces which in general slows down the molecular dynamics. A confinement effect leads to an acceleration of the segmental dynamics compared to the bulk state and points to an inherent length scale on which the glassy dynamics takes place. The step of the specific heat capacity Deltacp at the glass transition vanishes at a finite length scale of 1.8 nm. This result supports further the conception that a characteristic length scale is relevant for glassy dynamics.
For PMPS down to a pore size of 7.5 nm the temperature dependence of the relaxation times follows the VFT-dependence and a confinement effect is observed like for PPG. At a pore size of 5 nm this changes to an Arrhenius-like behavior with a low activation energy. At the same pore size Deltacp vanishes for PMPS. This points to a dramatic change in the character of molecular motions responsible for glassy dynamics and supports further the relevance of a characteristic length scale on which it takes place.
Quasielastic neutron scattering experiments on PMPS reveal that the microscopic dynamics characterized by the mean square displacement depends on confinement above the glass transition. The diffusive character of the relevant molecular motions seems to disappear at a length scale of about 1.6 nm.
The effect of a nanometer confinement on the molecular dynamics of poly(methyl phenyl siloxane) (PMPS) was studied by dielectric spectroscopy (DS), temperature modulated DSC (TMDSC) and neutron scattering (NS). Nanoporous glasses with pore sizes of 2.520 nm have been used. DS and TMDSC experiments show that for PMPS in 7.5 nm pores the molecular dynamics is faster than in the bulk which originates from an inherent length scale of the underlying molecular motions. For high temperatures the temperature dependence of the relaxation rates for confined PMPS crosses that of the bulk state. Besides finite states effects also the thermodynamic state of nano-confined PMPS is different from that of the bulk. At a pore size of 5 nm the temperature dependence of the relaxation times changes from a Vogel/Fulcher/Tammann like to an Arrhenius behavior where the activation energy depends on pore size. This is in agreement with the results obtained by NS. The increment of the specific heat capacity at the glass transition depends strongly on pore size and vanishes at a finite length scale between 3 and 5 nm which can be regarded as minimal length scale for glass transition to appear in PMPS.