The glassy dynamics of poly(propylene glycol) (PPG) and poly(dimethyl siloxane) (PDMS) confined to a nanoporous host system revealed by dielectric spectroscopy, temperature-modulated DSC and neutron scattering is compared. For both systems the relaxation rates estimated from dielectric spectroscopy and temperature-modulated DSC agree quantitatively indicating that both experiments sense the glass transition. For PPG the segmental dynamics is determined by a counterbalance of adsorption and confinement effect. The former results form an interaction of the confined macromolecules with the internal surfaces. A confinement effect originates from an inherent length scale on which the underlying molecular motions take place. The increment of the specific-heat capacity at the glass transition vanishes at a finite length scale of 1.8 nm. Both results support the conception that a characteristic length scale is relevant for glassy dynamics. For PDMS only a confinement effect is observed which is much stronger than that for PPG. Down to a pore size of 7.5 nm, the temperature dependence of the relaxation times follows the Vogel-Fulcher-Tammann dependence. At a pore size of 5 nm this changes to an Arrhenius-like behaviour with a low activation energy. At the same pore size vanishes for PDMS. Quasielastic neutron scattering experiments reveal that also the diffusive character of the relevant molecular motions --found to be characteristic above the glass transition-- seems to disappear at this length scale. These results gives further strong support that the glass transition has to be characterised by an inherent length scale of the relevant molecular motions.
Dielectric spectroscopy and temperature-modulated differential scanning calorimetry are employed to study the molecular dynamics of oligomeric poly(propylene glycol) (PPG) melts of different molecular weights confined to nanoporous glasses (pore sizes 2.5, 5.0, 7.5 and 20 nm). Moreover, the results obtained for the polymers are compared with those for the corresponding monomer. The experimental results are discussed in the framework of the interplay of confinement and adsorption effects. For large pore sizes (> 5 nm) a speeding up of the molecular dynamics is observed (the confinement effect), whereas for small pore sizes (< 5 nm) a slowing down of the segmental fluctuations is found (the adsorption effect). In addition, a minimal length scale for the glass transition of 1.6 nm is estimated for PPG confined in nanoporous glasses. This supports the idea that the molecular motions responsible for the glassy dynamics must be describable by a characteristic length scale.
Polarized Raman scattering investigations are carried out to investigate the conformations of the macromolecules inside the pores. These experiments show that the confined polymer chains are locally stretched. This effect increases with decreasing pore size.
A broadband dielectric study of the dispersions of silica spheres (Aerosil 380) in octylcyanobiphenyl (8CB) with densities between 0.083 and 10 g of silica per 1 cm3 of liquid crystal (LC) is reported. High values of silica densities were achieved for the first time to observe the behaviour of the LC monolayer on the surface of the silica particles. The relaxation characteristic of the bulk LC is noticed especially for the samples with low silica densities. Additionally, a slow relaxation was detected, even at temperatures for which the bulk LC is in the crystalline state. It was assigned to the surface layer of LC molecules. Remarkably, the temperature dependence of the relaxation rates for this slow process shows a behaviour typical for glass-forming liquids.
Dielectric spectroscopy and temperature modulated DSC are employed to study the molecular dynamics of oligomeric poly(propylene glycol) (PPG) melts of different molecular weights confined to nanoporous glasses (pore sizes 2.5, 5.0, 7.5 and 20 nm). Moreover the results obtained for the polymer are compared with the corresponding monomer. For large pore sizes an acceleration of the segmental dynamics compared to the bulk state is observed which is already known for low molecular-weight glass forming liquids. For smaller pore sizes the molecular dynamics is slower than in the bulk. The observed behavior is nearly independent of the molar mass of the polymer and of the treatment of internal glass surfaces. The experimental results are discussed in the frame of an interplay of confinement and adsorption effects. Moreover a length scale of about 1.6 nm is estimated as a minimal length scale for the cooperativity for the glass transition. In addition to the ?-relaxation the whole chain dynamics (normal mode relaxation) can be measured by dielectric spectroscopy because PPG has a dipole component parallel to the chain. For virgin internal surfaces the relaxation rate of the normal mode relaxation is shifted dramatically to lower relaxation rates. That can be explained by adsorption effects. For treated surfaces this effect is strongly reduced and it is concluded that also in this case the chain dynamics are influenced by geometric (confinement) effects.
The glassy dynamics of poly(propylene glycol) (PPG) and poly(methyl phenyl siloxane) (PMPS) confined to nanoporous glasses (pore sizes 2.520 nm) investigated by dielectric spectroscopy, temperature modulated DSC and neutron scattering is compared. For both systems the relaxation rates estimated from dielectric spectroscopy and temperature modulated DSC agree quantitatively indicating that both experiments sense the glass transition.
For PPG the glassy dynamics in nanopores is determined by a counterbalance of an adsorption and a confinement effect where the temperature dependence of the relaxation times obeys the Vogel/Fulcher/Tammann (VFT-) equation. The former effect results from an interaction of the confined macromolecules with the internal surfaces which in general slows down the molecular dynamics. A confinement effect leads to an acceleration of the segmental dynamics compared to the bulk state and points to an inherent length scale on which the glassy dynamics takes place. The step of the specific heat capacity Deltacp at the glass transition vanishes at a finite length scale of 1.8 nm. This result supports further the conception that a characteristic length scale is relevant for glassy dynamics.
For PMPS down to a pore size of 7.5 nm the temperature dependence of the relaxation times follows the VFT-dependence and a confinement effect is observed like for PPG. At a pore size of 5 nm this changes to an Arrhenius-like behavior with a low activation energy. At the same pore size Deltacp vanishes for PMPS. This points to a dramatic change in the character of molecular motions responsible for glassy dynamics and supports further the relevance of a characteristic length scale on which it takes place.
Quasielastic neutron scattering experiments on PMPS reveal that the microscopic dynamics characterized by the mean square displacement depends on confinement above the glass transition. The diffusive character of the relevant molecular motions seems to disappear at a length scale of about 1.6 nm.
Dielectric spectroscopy in combination with temperature modulated differential scanning calorimetry and quasielastic/inelastic neutron scattering are employed to investigate the molecular (glassy) dynamics of poly(dimethyl siloxane) (PDMS) and poly(methyl phenyl siloxane) (PMPS) confined to random nanoporous glasses with nominal pore sizes between 2.5 nm and 20 nm. Inside the pores PDMS and PMPS have faster molecular dynamics than in the bulk state. Down to a pore size of 7.5 nm the temperature dependence of the relaxation times (or rates) obeys the Vogel/Fulcher/Tammann (VFT) equation where the data obtained from dielectric and thermal spectroscopy agree quantitatively. At a pore size of 5 nm this VFT-like temperature dependence changes to an Arrhenius behavior. At the same confining length scale the increment of the specific heat capacity at Tg normalized to the weight of the confined polymer vanishes. The results indicate that a minimal length scale seems to be relevant for glassy dynamics in both polymers although the estimated length scale of about 5 nm seems to a bit too large in comparison to other experimental results and theoretical approaches. Neutron scattering is employed to investigate methyl group reorientation and the fast segmental dynamics of both polymers in confinement. Although the methyl group rotation is a localized process these experiments show that a part of the methyl groups is immobilized by the confinement whereas the effects for PDMS are much more pronounced than for PMPS. With regard to the segmental dynamics, neutron scattering reveals a big difference in the behavior of both polymers. Whereas the data obtained for PMPS are in accord with a boundary layer formed at the surfaces of the nanopores, for PDMS a considerable amount of elastic scattering is observed. To explain this result it is assumed that some structure formation of PDMS takes place in the nanopores, although the thermal data show no crystallization or melting effects.
Dielectric Study of Molecular Mobility in Poly(propylene-graft-maleic anhydride)/Clay Nanocomposites
(2005)
Polymer/clay nanocomposite materials based on poly(propylene-graft-maleic anhydride) (PPgMAH) and two different organophilic modified clays were investigated by dielectric relaxation spectroscopy (DRS). In contrast to ungrafted polypropylene (PP), PPgMAH shows a dielectrically active relaxation process which can be assigned to localized fluctuations of the polar maleic anhydride groups. Its relaxation rate exhibits an unusual temperature dependence, which could be attributed to a redistribution of water molecules in the polymeric matrix. This is confirmed by a combination of Raman spectroscopy and thermogravimetric experiments (TGA) with real-time dielectric measurements under controlled atmospheres. In the nanocomposites this relaxation process is shifted to higher frequencies up to 3 orders of magnitude compared to the unfilled polymer. This indicates a significantly enhanced molecular mobility in the interfacial regions. In the nanocomposite materials a separate high-temperature process due to Maxwell-Wagner-Sillars (MWS) polarization was observed. The time constant of this MWS process can be correlated with characteristic length scales in nanocomposites and therefore provides additional information on dispersion and delamination/exfoliation of clay platelets in these materials. These properties also influence the diffusivity of the water molecules as revealed by real-time dielectric investigations.
The effect of a nanometer confinement on the molecular dynamics of poly(methyl phenyl siloxane) (PMPS) was studied by dielectric spectroscopy (DS), temperature modulated DSC (TMDSC) and neutron scattering (NS). Nanoporous glasses with pore sizes of 2.520 nm have been used. DS and TMDSC experiments show that for PMPS in 7.5 nm pores the molecular dynamics is faster than in the bulk which originates from an inherent length scale of the underlying molecular motions. For high temperatures the temperature dependence of the relaxation rates for confined PMPS crosses that of the bulk state. Besides finite states effects also the thermodynamic state of nano-confined PMPS is different from that of the bulk. At a pore size of 5 nm the temperature dependence of the relaxation times changes from a Vogel/Fulcher/Tammann like to an Arrhenius behavior where the activation energy depends on pore size. This is in agreement with the results obtained by NS. The increment of the specific heat capacity at the glass transition depends strongly on pore size and vanishes at a finite length scale between 3 and 5 nm which can be regarded as minimal length scale for glass transition to appear in PMPS.