Eingeladener Vortrag
- nein (2)
Linear segmented polyurethanes based on poly(butylene adipate)s (PBA) of different molecular weight (Mn 2000, 1000, and 600), 4,4-diphenylmethane diisocyanate (MDI) and the mesogenic diol 4,4-bis-(6-hydroxyhexoxy)biphenyl (BHHBP) as well as the unsegmented polyurethane consisting of MDI/BHHBP units have been synthesized and characterized by elemental analysis, 13C-NMR and SEC. The thermal behavior and the morphology were studied by DSC, polarizing microscopy, and DMA. The properties of the MDI-polyurethanes were discussed in relation to the BHHBP chain extended 2,4-TDI-polyurethanes and common 1,4-butanediol chain-extended MDI products. MDI polyurethanes based on PBA (Mn 2000) exhibit a glass transition temperature Tg of about -40°C independent of the hard segment content up to 50% hard segments. At higher hard segment contents increasing Tgs were observed. Polyurethanes, based on the shorter polyester soft segments PBA (Mn 1000 or 600), reveal an increase in the glass transition temperatures with growing hard segment content. The thermal transitions caused by melting of the MDI/BHHBP hard segment domains are found at 50 K higher temperatures in comparison with the analogous TDI products with mesogenic BHHBP/TDI hard segments. Shortening of the PBA chain length causes a shift of the thermal transitions to lower temperatures. Polarizing microscopy experiments indicate that liquid crystalline behavior is influenced by both the content of mesogenic hard segments and the chain length of the polyester. © 1996 John Wiley & Sons, Inc.
The glassy dynamics of poly(propylene glycol) (PPG) and poly(dimethyl siloxane) (PDMS) confined to a nanoporous host system revealed by dielectric spectroscopy, temperature-modulated DSC and neutron scattering is compared. For both systems the relaxation rates estimated from dielectric spectroscopy and temperature-modulated DSC agree quantitatively indicating that both experiments sense the glass transition. For PPG the segmental dynamics is determined by a counterbalance of adsorption and confinement effect. The former results form an interaction of the confined macromolecules with the internal surfaces. A confinement effect originates from an inherent length scale on which the underlying molecular motions take place. The increment of the specific-heat capacity at the glass transition vanishes at a finite length scale of 1.8 nm. Both results support the conception that a characteristic length scale is relevant for glassy dynamics. For PDMS only a confinement effect is observed which is much stronger than that for PPG. Down to a pore size of 7.5 nm, the temperature dependence of the relaxation times follows the Vogel-Fulcher-Tammann dependence. At a pore size of 5 nm this changes to an Arrhenius-like behaviour with a low activation energy. At the same pore size vanishes for PDMS. Quasielastic neutron scattering experiments reveal that also the diffusive character of the relevant molecular motions --found to be characteristic above the glass transition-- seems to disappear at this length scale. These results gives further strong support that the glass transition has to be characterised by an inherent length scale of the relevant molecular motions.
Single-walled carbon nanotubes (SWNT) and carbon nitride films are synthesized by a direct current (dc) arc discharge at slightly reduced pressure and by an inductively coupled r.f. plasma (ICP) at atmospheric pressure, respectively. By treatment with nitric acid SWNT are purified from by-products and characterized by scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), and Raman spectroscopy. ICP allows the deposition of carbon nitride films on steel substrate. The deposition of the films creates a relatively strong radial symmetric profile. The structure of the films are rather independent of the distance between substrate and plasma. Raman, Fourier transform infrared (FTIR), and energy dispersive X-ray (EDX) spectroscopy are used for analyzing the carbon nitride materials.
Dielectric spectroscopy and temperature-modulated differential scanning calorimetry are employed to study the molecular dynamics of oligomeric poly(propylene glycol) (PPG) melts of different molecular weights confined to nanoporous glasses (pore sizes 2.5, 5.0, 7.5 and 20 nm). Moreover, the results obtained for the polymers are compared with those for the corresponding monomer. The experimental results are discussed in the framework of the interplay of confinement and adsorption effects. For large pore sizes (> 5 nm) a speeding up of the molecular dynamics is observed (the confinement effect), whereas for small pore sizes (< 5 nm) a slowing down of the segmental fluctuations is found (the adsorption effect). In addition, a minimal length scale for the glass transition of 1.6 nm is estimated for PPG confined in nanoporous glasses. This supports the idea that the molecular motions responsible for the glassy dynamics must be describable by a characteristic length scale.
Polarized Raman scattering investigations are carried out to investigate the conformations of the macromolecules inside the pores. These experiments show that the confined polymer chains are locally stretched. This effect increases with decreasing pore size.