A major international inter-comparison exercise on strain-controlled thermo-mechanical fatigue (TMF) has been undertaken to validate a new European Code of Practice for TMF Testing and to provide underpinning information for an ISO Standard. This paper focuses on (a) distribution of samples of Nimonic 90, (b) the establishment of a protocol for testing and reporting results, and (c) the analysis of the results. Participants in the inter-comparison exercise comprised eight inner-circle partners who primarily used test pieces which were all manufactured at the same workshop, albeit of three different test piece geometries, and ten outer-circle participants who manufactured their own test pieces, of their own in-house geometry. Each participant undertook three repeat in-phase (IP) tests and three repeat out-of-phase (OP) tests. The tests were conducted at temperatures cycling between 400 °C and 850 °C, with a strain range selected to give a failure life of approximately 1000 cycles, resulting in a stress range of up to ~1000 MPa. The testing conditions were chosen following a preliminary evaluation of critical testing parameters. Results from solid circular and solid flat test piece geometries, together with hollow tubular test pieces have been compared. The influence of temperature measurement using different types of temperature sensors has also been investigated. In-house repeatability has been assessed, together with inter-laboratory reproducibility. The results have been correlated with modulus and thermal expansion data for individual tests. Initially, the largest contribution to scatter in the results was attributed to human errors in reporting the results, compounded by computer assisted cut-and-paste errors. Once these obvious discrepancies had been corrected, it was possible to use the data sets to point to some recommendations regarding testing procedures that can be incorporated into the Code of Testing Practice [Hähner P et al. Code of practice for thermo-mechanical fatigue testing TMF-Standard-Work Package 6 Report, September 2005] and provide technical underpinning for the ISO Standard. The results and the procedures used for analysis are presented.
Thermo-mechanical fatigue (TMF) testing plays an increasingly important role in the design, the reliability assessment and the lifecycle management of safety critical components used, for instance, for power generation, in the process industry and in aeronautical and automotive applications, with a view to increasing the fuel efficiency, safety and service intervals, while reducing production (and material) costs. In a European Commission funded research project (acronym: TMF-Standard) of the 5th Framework Programme, 20 European laboratories have undertaken a joint research effort to establish a validated code-of-practice (CoP) for strain-controlled TMF testing. Starting from a survey of the testing protocols and procedures previously used by the partners, a comprehensive pre-normative research activity into various issues has been completed, addressing the dynamic temperature control, the effects of deviations in nominal temperatures and phase angles, the influences of temperature gradients, as well as the practicalities of test interruption and restart procedures. Meaningful allowable tolerances for the various test parameters were identified and practical recommendations as to the test techniques were formulated. From this a preliminary CoP was compiled and used to guide an extensive round robin exercise among the project partners. From the statistical analysis of that exercise, a validated CoP was derived dealing with strain-controlled constant amplitude TMF of nominally homogeneous metallic materials subjected to spatially uniform temperature fields and uniaxial mechanical loading. It is intended to give advice and guidance on the appropriate test setup, testing procedures and the analysis of results, in particular for newcomers in the field of strain-controlled TMF. This paper highlights some of the results of the TMF-Standard project. Moreover, commonalities and differences of the present CoP with respect to the standard documents for strain-controlled TMF, which have been developed at ISO and ASTM levels, are presented in this paper.
The uniaxial, torsional and axial-torsional thermomechanical fatigue (TMF) behavior of the near-γ TiAl-alloy TNB-V5 was investigated. TMF tests were performed at 400-800 °C with mechanical strain amplitudes ranging from 0.15% to 0.7%. The tests were conducted thermomechanically in-phase (IP) and out-of-phase (OP).
For the same lifetimes, uniaxial IP tests required the highest strain amplitudes, while OP test conditions were most damaging and needed the lowest strain amplitudes. The Mises equivalent mechanical strain amplitudes of pure torsional tests were found in between uniaxial in-phase and out-of-phase tests for the same lifetimes. The non-proportional multiaxial out-of-phase test showed a lower lifetime at the same equivalent mechanical strain amplitude compared to the other types of tests.
The microstructure has been characterized applying electron microscopy and microstructural parameters such as fraction of twinned grains, grain size, lamellar distance and dislocation density have been quantified.