Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (29)
- Beitrag zu einem Tagungsband (4)
- Buchkapitel (1)
- Forschungsbericht (1)
Schlagworte
- NEXAFS (3)
- ToF-SIMS (3)
- XPS (3)
- Ablation (2)
- Aluminium (2)
- Electron backscattered diffraction (2)
- Gesamtwasserprobe (2)
- Laser processing (2)
- Macrocycles (2)
- NEXAFS spectroscopy (2)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (3)
- 6 Materialchemie (2)
- 9 Komponentensicherheit (2)
- 9.0 Abteilungsleitung und andere (2)
- 9.2 Versuchsanlagen und Prüftechnik (2)
- 1.1 Anorganische Spurenanalytik (1)
- 1.4 Prozessanalytik (1)
- 1.5 Proteinanalytik (1)
- 1.6 Anorganische Referenzmaterialien (1)
- 6.3 Strukturanalytik (1)
- 6.6 Physik und chemische Analytik der Polymere (1)
- 7 Bauwerkssicherheit (1)
- 7.6 Korrosion und Korrosionsschutz (1)
Imaging Capability of Terahertz and Millimeter-Wave Instrumentations for NDT of Polymer Materials
(2006)
Darstellung und Charakterisierung von Nanopartikeln auf der Basis von [Ti2W10PO40]7- und Chitosan
(2005)
The Keggin type polyoxotungstate [Ti2W10PO40]7- forms stable associates with the biopolymer chitosan in the nanometer size range. The cluster compound crystallizes from aqueous solution as K4H3[Ti2W10PO40] · 15H2O having a tetragonal structure. Both, the cluster compound and the chitosan/[Ti2W10PO40] associates show a high hydrolytic stability at pH 7.4. The associates formed between the cluster anion [Ti2W10PO40]7- with the polyaminosaccharide chitosan have been characterized by photon correlation spectroscopy, scanning electron microscopy, filtration, centrifugation and zeta potential measurements. The size of the associates formed is in the range of ca. 5×101 to 5×102 nm. These particles have a defined stoichiometry with 56 cluster anions bound per molecule chitosan. The isoelectric point determined by zeta potential measurements was found for a cluster anion to chitosan molar ratio of 5.5, indicating the charge neutralization between protonated chitosan and [Ti2W10PO40]7- anions. Cellular uptake studies with [Ti2W10PO40]7- using tumor cell lines FaDu (human squamous carcinoma) and HT-29 (human adenocarcinoma) showed that the tungsten amount inside the cells is remarkably enhanced in the presence of chitosan.
The development of two metallizations based on the solid-phase regrowth principle is presented, namely Pd/Sb(Zn) and Pd/Ge(Zn) on moderately doped In0.53Ga0.47As (p=4×1018 cm-3). Contact resistivities of 23×10-7 and 67×10-7 ?cm2, respectively, have been achieved, where both systems exhibit an effective contact reaction depth of zero and a Zn diffusion depth below 50 nm. Exhibiting resistivities equivalent to the lowest values of Au-based systems in this doping range, especially Pd/Sb(Zn) contacts are superior to them concerning metallurgical stability and contact penetration. Both metallizations have been successfully applied for contacting the base layer of InP/In0.53Ga0.47As heterojunction bipolar transistors.
Structuring of thin-film photovoltaic modules requires basic knowledge of the laser – thin-film interaction in order to adapt the accessible laser parameters, like wavelength, power, repetition rate and scribing speed whilst taking into account the specific material properties of the layer. We have studied the nanosecond laserablation behavior of corresponding layers (i) of silicon based thin-film solar cells with a-Si/µc-Si tandem absorber type and (ii) of back contact and absorber layer of CIGSe solar cells. The respective ablation threshold fluences were determined as integrative parameters describing the specific laser – material interaction. For the threshold determination we used two different methods and developed a new analytical approach taking into account scribing through the glass substrate as it is preferred for most structuring processes. This was done by analyzing the thin film ablation results by means of optical microscopy, profilometry, scanning electron microscopy (SEM). Moreover, we determined the incubation coefficient of the regarded material layers which allows us to predict quantitatively the influence of the spot overlap on the scribing threshold.
Manufacturing of CIGSe thin film solar modules involves typically one laser structuring step (P1) and two mechanical structuring steps (P2 and P3) for serial interconnection. In our approach, complete laser structuring is successfully demonstrated by application of short nanosecond laser pulses (<10 ns) with a single, visible wavelength of 532 nm. The P1 and the P3 trenches are scribed by induced and direct ablation, respectively. For the P2 scribe, the thermal input of the ns laser pulses is used to transform the CIGSe absorber layer locally into a highly conductive compound to provide proper electrical interconnection. These findings promise further simplification and flexibility to thin film solar cell production.
Ein wesentlicher Vorteil der Dünnschichtphotovoltaik gegenüber der waferbasierten Photovoltaik liegt in der monolithischen Serienverschaltung. Bei der Herstellung von Chalkopyrit(CIGSe) -Dünnschicht-Solarmodulen erfolgen dafür typischerweise ein Laser-Strukturierungsschritt (P1) und zwei mechanische Strukturierungsschritte (P2, P3). In diesem Beitrag wird gezeigt, dass die Strukturierung von CIGSe-Solarmodulen vollständig mit kurzen Laserpulsen (<10 ns Pulsdauer) und einer einzigen Wellenlänge (532 nm) möglich ist. Der P1- und P3-Schnitt erfolgen durch direkte induzierte Ablation. Für den P2-Schnitt wird gezielt der hohe Wärmeeintrag der ns-Laserpulse genutzt, um die CIGSe-
Absorberschicht lokal aufzuschmelzen und strukturell so zu verändern, dass eine elektrisch gut leitende Verbindung zwischen Front- und Rückkontakt entsteht.
One wavelength fits all
(2011)
Structuring of Thin-film Solar Cells with a Single Laser Wavelength Structuring of a PV module into a number of cells is necessary to lower the current and to increase the voltage, and is typically accomplished with nanosecond laser pulses of different wavelengths. Duetothe many available laser sources, complex and expensive scribing Setups are necessary. To overcome this a concept for laser structuring of thin-film PV modules using a single wavelength allows prediction ofthe ablation behaviourfor a given laser pulse energy.
Copolyesters with an alternating sequence of terephthalic acid and aliphatic dicarboxylic acids were prepared with three different methods. First, dicarboxylic acid dichlorides were reacted with bis(2-hydroxyethyl)terephthalate (BHET) in refluxing 1,2-dichlorobenzene. Second, the same monomers were polycondensed at 0-20 °C in the presence of pyridine. Third, dicarboxylic acid dichlorides and silylated BHET were polycondensed in bulk. Only this third method gave satisfactory molecular weights. Matrix-assisted laser desorption/ionization time-of-flight mass spectrometry revealed that the copolyesters prepared by the pyridine and silyl methods might have contained considerable fractions of cyclic oligoesters and polyesters despite the absence of transesterification and backbiting processes. The alternating sequences and thermal properties were characterized with 1H NMR spectroscopy and differential scanning calorimetry measurements, respectively. In agreement with the alternating sequence, all copolyesters proved to be crystalline, but the crystallization was extremely slow [slower than that of poly(ethylene terephthalate)]. A second series of alternating copolyesters was prepared by the polycondensation of silylated bis(4-hydroxybut- yl)terephthalate with various aliphatic dicarboxylic acid dichlorides. The resulting copolyesters showed significantly higher rates of crystallization, and the melting temperatures were higher than those of the BHET-based copolyesters. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3371-3382, 2001
An ethynylterpyridine was 'clicked' to an azide-terminated self-assembled monolayer on gold and characterized by synchrotron radiation based surface analysis as NEXAFS and XPS. The detection of azide and terpyridine signatures confirmed a partial click reaction at room temperature. The absence of the azides after reaction at 50 °C indicates an almost complete conversion. For the latter case successful Pd(II) coordination has been proven. The Au–S interface of the SAMs has been characterized by S 1s and S 2p XPS.
The deposition of palladium on a novel, reversibly protonatable, pyridyl-terminated self-assembled monolayer on gold substrates has been studied by X-ray photoelectron spectroscopy (XPS), near-edge X-ray absorption fine structure spectroscopy (NEXAFS spectroscopy) and time of flight-secondary ion mass spectrometry (ToF-SIMS). For this purpose, 12-(pyridin-4-yl)dodecane-1-thiol, consisting of a surface-active head group, an unfunctionalized hydrocarbon backbone and a terminal pyridyl group, has been synthesized and deposited on gold surfaces. Coordination of Pd(II) ions to the pyridyl group was examined. Furthermore, a reversible protonation/deprotonation cycle has been applied, and the relation between protonation and the amount of complexed palladium was studied. Investigation of the SAM by angle-resolved NEXAFS spectroscopy revealed the aliphatic backbone to be preferentially upright oriented with the aromatic head group being not preferentially oriented. The palladium layer was further coordinated with a CF3-labeled terpyridine ligand in order to prove the accessibility of the Pd(II) ions to further complexation and the platform useful for deposition of further layers toward a multi-layered system.
Experimental N K-edge NEXAFS data of surface immobilized azide, 1,2,3-triazole and terpyridyl groups are interpreted with the help of DFT spectrum simulations. Assignments of π* resonances in experimental N K-edge NEXAFS spectra to nitrogen atoms within these functional groups have been made. The azide was immobilized on gold as the head group of a thiol SAM, 1,2,3-triazole was formed on this SAM by click reaction and terpyridyl groups were introduced as substituents of the acetylene used for the click reaction. For azide-terminated molecules, DFT spectrum simulations are found to be useful to find measurement conditions delivering experimental N K-edge NEXAFS data with negligible X-ray damage. The 1,2,3-triazole group is found to be rather stable under X-ray irradiation.
Mechanically interlocked molecules (MIMs) such as rotaxanes and catenanes are capable of mechanical motion on the nanoscale and are therefore promising prototypes for molecular machines in recent nanotechnology. However, most of the existing examples are isotropically distributed in solution, which prohibits concerted movement and with it the generation of macroscopic effects. Thus, arranging them in ordered arrays is of huge interest in recent research. We report the deposition of quite densely packed multilayers of tetralactam macrocycles on gold surfaces by metal-coordinated layer-by-layer self-assembly. Linear dichroism effects in angle-resolved NEXAFS spectra indicate a preferential orientation of the macrocycles. The sequence of the metal ions can be programmed by the use of different transition metal ions at each deposition step. Additionally, reversible on-surface pseudorotaxane formation was successfully realized by repeated uptake and release of axle molecules inside the macrocycles cavities.
The deposition of tetralactam macrocycles and the corresponding benzyl ether rotaxanes on gold substrates is investigated for the first time exploiting metallo-supramolecular chemistry. Two pyridine-terminated self-assembled monolayers (SAMs) are developed that are used as well-ordered template layers. The two SAMs differ with respect to the rigidity of the terminal pyridines as shown by angle-resolved near-edge X-ray absorption fine structure (NEXAFS) spectroscopy. The template layers are then used for the metal-mediated self-assembly of macrocylces and rotaxanes on solid supports. The SAM with the more rigid terminal pyridine shows a higher coverage with the macrocycles and is therefore preferable. Angle-resolved NEXAFS spectroscopy also shows the deposited supramolecules to be oriented preferentially upright. This order is only achieved for the macrocycles through the deposition on the more rigid SAM template, whereas rotaxanes form oriented layers on both SAMs. Time-of-flight secondary-ion mass spectrometry analysis was used to determine the deposition time required for the self-assembly process.
Aiming at the functionalization of surfaces with terpyridine anchors for the coordinative deposition of additional layers, mixed self-assembled monolayers (SAMs) were prepared from binary solutions of 12-(2,2':6',2''-terpyridine-4'-yl)dodecane-1-thiol (TDT) and 1-decanethiol (DT). The SAMs and the order of the constituting molecules were analyzed by X-ray photoelectron spectroscopy (XPS), near-edge X-ray absorption fine structure spectroscopy (NEXAFS), and time-of-flight-secondary ion mass spectrometry (ToF-SIMS). The composition of the (TDT/DT)-SAMs and with it the surface density of terpyridyl groups correlates linearly with the relative concentrations of the two compounds in the solution used for depositing them. In marked contrast, the amount of terpyridine-coordinated PdII ions significantly deviates from this trend with an optimum at a 1:3 ratio of TDT/DT. This indicates a major fraction of the terpyridines in TDT-rich SAMs not to be accessible for PdII ion coordination. In agreement, NEXAFS spectroscopy reveals the alkyl backbones in TDT-rich SAMs not to be ordered, while they are preferentially upright oriented in the optimal 1:3-(TDT/DT)-SAMs. We interpret this in terms of terpyridine backfolding in TDT-rich SAMs, while they are located in accessible positions on top of the SAM in the 1:3-(TDT/DT)-SAM. While the alkyl backbones in the 1:3-(TDT/DT)-SAM are ordered, NEXAFS spectroscopy shows the terpyridyl groups not to have a preferential orientation in this SAM and thus retain enough flexibility to adjust to molecules that are deposited on top of the mixed SAM. In conclusion, the novel SAM does not undergo phase separation and consists predominantly of intermixed phases with adjustable surface density of quite flexible terpyridine anchor groups. The terpyridine–PdII anchors are not only available for a future deposition of the next layer, but the metal ions also represent a sensitive probe for the accessibility of the terpyridyl groups.
This work explores the feasibility of producing bead-on-plate welds of a CrCoNi medium entropy alloy and a CrMnFeCoNi high entropy alloy using electron beam welding. The alloys were welded in two states: one in an as-cold-rolled condition and the other in an annealed condition. In addition, the materials are welded with two different parameters. The FCC microstructure of the welds is investigated using scanning electron microscopy assisted by energy-dispersive X-ray spectroscopy and electron-backscattered diffraction. The impact of the weld on the microstructure is discussed. The heat-affected zone is negligible for the annealed condition of both medium and high entropy alloys since there is no driving force for recrystallisation and the exposure time to high temperature is insufficient for grain coarsening. The texture formed in the fusion zone is also discussed and compared to the texture in the base metal and the heat-affected zone. Although the grain growth along the (100) crystallographic direction is preferential in all cases, the crystallographic texture type differs from each weld. Higher hardness values are measured in the medium entropy alloy’s base metal and fusion zone than in the high entropy alloy.
The production of high-quality self-assembled monolayers (SAMs) followed by layer-by-layer (LbL) self-assembly of macrocycles is essential for nanotechnology applications based on functional surface films. To help interpret the large amount of data generated by a standard ToF-SIMS measurement, principal component analysis (PCA) was used. For two examples, the advantages of a combination of ToF-SIMS and PCA for quality control and for the optimization of layer-by-layer self-assembly are shown. The first example investigates how different cleaning methods influence the quality of SAM template formation. The second example focuses on the LbL self-assembly of macrocycles and the corresponding stepwise surface modification.