The tribological profile of alumina (99.7%) mated against rotating disks made in binder-less niobium carbide (NbC) and cobalt-bonded NbC were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22 °C and 400 °C) as well as in oscillation tests (f = 20 Hz, Δx = 0.2 mm, 2/50/98% rel. humidity, n = 105/106 cycles) under unlubricated (dry) conditions. In addition, the microstructure and mechanical properties of binderless NbC and NbC bonded with 8% cobalt were determined as well. The reason for testing hot-pressed NbC was to avoid side effects generated by sintering additives and/or second phases. The tribological data obtained were benchmarked with different ceramics, cermets and thermally sprayed coatings. NbC and cobalt-bonded NbC exhibited low wear rates under dry sliding associated with high load carrying capacity. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references, such as WC, Cr3C2 and (Ti,Mo)(C,N).
The approaching CO2 targets have now enforced automotive OEMs to engage R&D efforts also in powertrain to reduce friction, increase lifetime properties, and load carrying capacities of running systems. Martensitic steels such as 36NiCrMoV1-5-7 have a great potential to be used in automotive powertrain applications due to its favorable mechanical properties. In order to realize lightweight strategies, it is essential that steels with improved fracture toughness values and higher annealing temperatures with regard to higher contact pressures and possible thin film coating application be considered. State-of-the-art steels, like 16MnCr5, 21NiCrMo, 30CrMoV9, and 100Cr6 are not able to sustain a further increase in torque or load during operating time as well as annealing effects under higher oil or deposition temperatures. Therefore, the recent research on the slip-rolling resistance, frictional, and wear behavior of steels such as 36NiCrMoV1-5-7, Cronidur 30 (AMS 5898), 20MnCr5 (SAE 4820 or 5120), and 100Cr6H (SAE E52100) showed that possible lean alloying concept alternatives with promising performance characteristics are already available.
Das triboiogische Profil von binderlosem NbC und mit 8% bzw. mit 12% Cobalt oder 12% FeaAl gebundenem NbC wird unter unidirektionaler Gleitreibung (v= 0,1-10 m/s, T= 22°C und 400°C) und unter oszillierender Gleitreibung vergleichend gegenüber Ingenieurkeramiken und Hartmetallen dargestellt. Zusätzlich werden die 4-Punkt-Biegebruchfestigkeit, elastische Eigenschaften (E,G) bis 1.000°C die lastabhängige Mikrohärte sowie die Phasenzusammensetzung und Gefügestrukturen vorgestellt.
Die Verschleißkoeffizienten des binderlosen NbC lagen bei T unterhalb von 10'6mm31 / *N* m, während diejenigen der cobaltgebundenen NbCs mit ansteigender Gleitgeschwindigkeit von 2-4 10‘6 mm3/Nm bei 0,1 m/s auf 5-7 10"7 mm3/Nm bei 10 m/s abnahmen. Die Verschleißkoeffizienten bei 400°C lagen für die NbCs generell unterhalb von 10‘6 mm3/Nm. Das triboiogische Lasttragevermögen im Trockenlauf, ausgedrückt als PV-Wert, nimmt mit ansteigender Gleitgeschwindigkeit auf 100 W/mm2 zu. Bedingt durch die geringe Löslichkeit von NbC in Legierungen offenbarten erste Zerspanversuche mit verschiedenen Stählen eine gegenüber WC-basierten Schneidstoffen signifikant angehobene Zerspanungsvolumina. Somit offenbart NbC in offenen und geschlossenen Tribosystemen Anwendungspotentiale.
Das tribologische Profil von binderlosem NbC und mit 8% bzw. mit 12% Cobalt oder 12% Fe3Al gebundenem NbC wird unter unidirektionaler Gleitreibung (v= 0,1-10 m/s, T= 22°C und 400°C) und unter oszillierender Gleitreibung vergleichend gegenüber Ingenieurkeramiken und Hartmetallen dargestellt. Zusätzlich werden die 4-Punkt-Biegebruchfestigkeit, elastische Eigenschaften (E,G) bis 1.000�C die lastabhängige Mikrohärte sowie die Phasenzusammensetzung und Gefügestrukturen vorgestellt. Die Verschleißkoeffizienten des binderlosen NbC lagen bei T unterhalb von 10-6 mm³/N?m, während diejenigen der cobaltgebundenen NbCs mit ansteigender Gleitgeschwindigkeit von 2-4 10-6 mm³/N?m bei 0,1 m/s auf 5-7 10-7 mm³/N.m bei 10 m/s abnahmen. Die Verschleißkoeffizienten bei 400°C lagen für die NbCs generell unterhalb von 10-6 mm³/N.m. Das tribologische Lasttragevermögen im Trockenlauf, ausgedrückt als PV-Wert, nimmt mit ansteigender Gleitgeschwindigkeit auf 100 W/mm² zu. Bedingt durch die geringe Löslichkeit von NbC in Legierungen offenbarten erste Zerspanversuche mit verschiedenen Stählen eine gegenüber WC-basierten Schneidstoffen signifikant angehobene Zerspanungsvolumina. Somit offenbart NbC in offenen und geschlossenen Tribosystemen Anwendungspotentiale.
The tribological profile of alumina (99,7%) mated against binderless niobium Carbide (NbC) rotating disks under under unlubricated (dry) friction and the type of motions of unidirectional sliding (0.1 m/s to 7.5 m/s; 22°C and 400°C) and oscillation (f= 20 Hz, Ax= 200 mm, 2/50/98% rel. humidity, n= 105/106 cycles) was determined including the microstructure and mechanical properties. The obtained tribological data were benchmarked with different ceramics, cermets and thermally sprayed coatings. The established tribological profile revealed a strong position of NbC under tribological considerations and for closed tribosystems against traditional references, like WC, Ci‘3C2, (Ti,Mo)(C,N), etc..
The tribological profile of rotating disks made of binder-less niobium carbide (hot-pressed NbC) and cobalt-bonded NbC (NbC-8Co) mated against alumina (99.7%) were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22°C and 400°C) as well as in oscillation tests (f= 20 Hz, Δx= 0.2 mm, 2/50/98% rel. humidity, n= 105/106 cycles) under un-lubricated (dry) conditions. In addition, the microstructure and mechanical properties of NbC and NbC bonded with 8% cobalt were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where the NbC-8Co presented above 7 m/s the lowest wear rates so far in such a bench mark. NbC and NbC-8Co exhibited low wear rates under dry sliding associated with P·V high load carrying capacity. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references.
Substitution of tungsten carbide by niobium carbide as cutting materials and for wear protection
(2016)
Several phases, like Nb₄ C₃ , Nb₆C₅ and other short and long range ordered phases occur in the region of homogeneity of NbCₓ (0.75 ≤ x ≤ 1.0) in the binary phase diagram. Properties, like micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, the addition of secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of these tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results.
Niobium is today largely available. NbC can be synthesized by carbothermal conversion of Nb₂O₅ or be metallurgically grown and leached out, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb₂O₅ have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO₃ and Co₃ O₄ .
In the present work it was shown that the addition of VC or a combination of VC + Ti(C0.7N0.3) was efficient in reducing the NbC grain growth during liquid phase sintering, when compared to NbC-Ni equivalents. A finest NbC grain size of 1.48 µm was obtained in the NbC-15 Ti(C0.7N0.3)-10 Ni-7.5 VC cermet, exhibiting a hardness of 1486 +/- 7 kg/mm2 and a fracture toughness of 8.7 +/- 0.1 MPa m 1/2.
The tribological profile of alumina (99.7%) mated against binder-less niobium carbide (NbC) rotating disks were determined unidirectional sliding tests (0.17.5 m/s; 22 °C and 400 °C) as well as in oscillation tests (f=20 Hz, Δx=0.2 mm, 2/50/98% rel. humidity, n=105/106 cycles) under un-lubricated (dry) conditions. In addition, the microstructure and mechanical properties of NbC were determined as well. The reason for testing hot-pressed NbC was to avoid side effects generated by sintering additives and/or second phases. The tribological data obtained were benchmarked with different ceramics, cermets and thermally sprayed coatings. NbC exhibited low wear rates under dry sliding associated with high load carrying capacity. The tribological profile established revealed a strong position of NbC under tribological considerations and for closed tribo-systems against traditional references, such as WC, Cr3C2, (Ti,Mo)(C,N), etc.
Full densification of Fe, Co and Ni bonded NbC based cermet’s was achieved by pressure less liquid phase sintering in vacuum for one hour at 1420°C. The hardness and toughness of the NbC matrix cermet’s can be mainly tailored by the binder composition and secondary carbide additions. Ni binder based NbC cermet’s allow the combination of high hardness and improved toughness. The addition of lesser amounts of VC/Cr3C2 in a NbC partially substituted WC-Co cemented carbide increased significantly the hardness in combination with a moderate fracture toughness.
Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components.
The current study reports on the influence of the Addition of 5–15 vol% VC or/and Mo2C carbide on the microstructure and mechanical properties of nickel bonded NbC cermets, which are compared to cobalt bonded NbC cermets. The NbC, Ni and secondary carbides powder mixtures were liquid phase sintered for 1 h at 1420 °C in vacuum. The fully densified cermets are composed of a cubic NbC grains matrix and an evenly distributed fcc Ni binder. NbC grain growth was significantly inhibited and a homogeneous NbC grain size distribution was obtained in the cermets with VC/Mo2C additions. The mechanical properties of the NbC-Ni matrix cermets are strongly dependent on the carbide and Ni binder content and are directly compared to their NbC-Co equivalents.
The liquid phase sintered NbC-12 vol% Ni cermet had a modest Vickers hardness (HV30) of 1077 ± 22 kg/mm2 and an indentation toughness of 9.1 ± 0.5 MPa·m1/2. With the addition of 10–15 vol% VC, the hardness increased to 1359 ± 15 kg/mm2, whereas the toughness increased to 11.3 ± 0.1 MPa·m1/2. Addition of 5 and 10 vol% Mo2C into a NbC-12 vol% Ni mixtures generated the same values in HV30 and KIC when compared to VC additions. A maximum flexural strength of 1899 ± 77 MPa was obtained in the cermet with 20 vol% Ni binder and 4 vol% VC+4 vol% Mo2C addition, exhibiting a high fracture toughness of 15.0 ± 0.5 MPa·m1/2, but associated with a loss in hardness due to the high Ni content. The dry sliding wear behaviour was established at room temperature and 400 °C from 0.1 to 10 m/s.
NbC has a relatively high hardness (19.6 GPa) and melting temperature (3600 °C) and is usually applied as a grain growth inhibitor in WC–Co hardmetals. The current study reports on the influence of the sintering technology and overall chemical composition on the microstructure and mechanical properties of NbC-based hardmetals, using Co as a binder. The partial replacement of NbC by 5 wt.% WC, Mo2C, VC or TiC allows one to significantly improve the hardness and toughness of the NbC–Co materials. The influence of different binders, i.e., Co, 316L stainless steel and Fe3Al on the microstructure and mechanical properties of NbC-based hardmetals was also investigated. The powder mixtures were sintered in the solid state by PECS and liquid state by conventional vacuum sintering. Detailed microstructural analysis was conducted by EPMA elemental mapping and WDS point analysis. Mechanical properties, including Vickers hardness and indentation toughness were assessed.
The tribological profile of rotating disks made in binder-less niobium Carbide (hot-pressed NbC) and cobalt-bonded NbCs (NbC-8Co and NbC-12Co) mated against alumina (99.7%) were determined under unidirectional sliding tests (0.1 m/s to 8.0 m/s; 22°C and 400°C) as well as in oscillation tests (f= 20 Hz, Ax= 0.2 mm, 2/50/98% rel. humidity, n= 105/l 06 cycles) under unlubricated (dry) conditions. In addition, the microstructure and mechanical properties of HPNbCl and NbC bonded with 8 vol.-% and 12 vol.-% cobalt were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where the NbCs bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a bench mark. HP-NbCl, NbC-8Co and NbC-12Co exhibited low wear rates under dry sliding associated with PV high load carrying capacities. The tribological profile established revealed a strong position of NbC bearing materials under tribological considerations and for closed tribo-systems against traditional references.
The tribological and mechanical properties of niobium carbides (NbC) bonded with cobalt of Fe3Al
(2014)
The tribological and mechanical properties of niobium carbide bonded with 8 vol.-% (NbC-8Co), 12 vol.-% of cobalt (NbC-12Co) or 12 vol.-% of Fe3Al (NbC-12Fe3Al) are presented. Rotating discs made of metal-bonded niobium carbide were mated against alumina (99.7%) under unlubricated (dry) unidirectional sliding tests (0.1 m/s to 12.0 m/s; 22 °C and 400 C) as well as in oscillation tests (f=20 Hz, Δx=0.2 mm, 2/50/98% rel. humidity, n=105/106 cycles). Microstructure and phase compositions were determined as well. The tribological data obtained were benchmarked with different ceramics, cermets, hard metals and thermally sprayed coatings, where NbC bonded with 8% and 12% Co presented above 7 m/s the lowest wear rates so far in such a benchmark. Binderless NbC (HP-NbC1) and the metal-bonded NbCs exhibited low wear rates under dry sliding associated with P·V high load carrying capacities. NbC-based hard metal bonded with 12 vol.-% of Fe3Al resulted in a higher hardness level than for 12 vol.-% cobalt. The tribological profile established revealed a strong position of NbC-bearing materials under tribological considerations and for closed tribosystems against established reference tribo-couples.
In this present study, the mechanical properties (strength, hardness, moduli) and the dry sliding properties of stoichiometric and sub-stoichiometric NbC were compared. Microhardness and elastic properties of NbC depend from the C/Nb ratio, because the binary phase diagram Nb-C shows a region of homogeneity of NbCx of 0,72≤ x ≤1.0. At RT, hard metals of stoichiometric NbC have an elastic modulus E of ~440 GPa, those of substochiometric NbC0,88 an E of 405 GPa. The hot hardness of sub-stoichiometric NbC is above 600°C higher than of WC. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC0,94 with ~61 vol.-% NbC as hard phase was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks of the Fe3Al-NbC composite (MMC), as a metallurgical interphase was formed between matrix and NbC grains. Stoichiometric and sub-stoichiometric niobium carbides have at RT and 400°C under dry sliding a prone intrinsic wear resistance more or less independent from sliding speed, either as hardmetal or as hard phase in metal matrix composite, associated with an exceptional high load carrying capacity.
Niobium is today largely available. The initial NbC grade was substoichiometric, SPS sintered and cobalt bonded (NbC0.88-12Co SPS). The NiMo-bonded stoichiometric NbC1.0 grades enable the subtituion of cobalt by nickel, SPS by conventional sintering and NbC0.88 by NbC1.0 in view of functional properties. Nickel bonded NbC grades have improved toughnesses versus cobalt bonded NbC grades, but lose hardness. NiMo and NiMo2C bonded NbC1.0 grades compensated the loss in hardness while keeping the toughness.
The current study reports on the effect of the sintering temperature and secondary carbide (VC, Mo2C and TiC) additions on the microstructure and concommitant Vickers hardness (HV30) and fracture toughness of Ni-bonded NbC cermets. All cermets were prepared by pressureless sintering in vacuum. Detailed microstructural investigation was performed by electron probe microanalysis (EPMA) and X-ray diffraction (XRD) analysis. Sintering results indicated that both the sintering temperature and secondary carbide additions had a significant effect on the properties of NbC-Ni cermets. Nickel pools and residual pores were observed in the cermets sintered at temperatures ≤ 1340 °C. Increasing of the sintering temperature up to 1420 or 1480 °C resulted in fully densified NbC-Ni based cermets composed of homogeneous contrast cubic NbC grains for the single carbide (VC or Mo2C) modyfied system, whereas core-rim structured NbC grains were observed with the additon of TiC + VC or TiC+Mo2C. The secondary carbide doped cermets with 5–10 vol.% VC/Mo2C and 10 vol.% TiC showed a significantly improved hardness and fracture toughness, as compared to the plain NbC-Ni cermets.
The tribological behavior under dry sliding of a Fe3Al-NbC composite prepared by pyro-metallurgical synthesis is compared to different SPS sintered NbC-based hardmetals bonded by cobalt or Fe3AI. The dry sliding wear resistance (0. 1-7 /10 m/s) of the present Fe3Al-NbC with -60 % NbC was close to those known ofNbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks of the Fe3Al-NbC composite, as a metallurgical interphase was formed between matrix and NbC grains. The physical prope1ties of melt grown NbC match those known from powder metallurgically sintered NbC using powders converted from Nb205.
Thc tribological behavior under dry sliding of a Fe3Al-NbC composite prepared by pyrometallurgical synthesis is compared to NbC-based hard metals bonded by cobalt or Fe3Al. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC with 60% NbC was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks, as a metallurgical interphase was formed between matrix and NbC grains.
The origin of the intrinsic wear resistance of NbC-based materials is investigated through an assessment of the tribological performance of fully dense, crack-free spark plasma sintered Nb2O5 (here as a reduced polymorph: monoclinic Nb12O29 or NbO2.416). The most likely wear mechanism on NbC is the tribo-oxidation to Nb2O5. The unlubricated (dry) friction and wear behavior of alumina (99.7%) mated against rotating disks of crack-free niobium(V)oxide (Nb2O5) under unidirectional sliding (0.03–10m/s; 22°C and 400°C) and oscillation (f=20 Hz, dx=200 mm, 2/50/98% rel. humidity, n=105/106 cycles) will be presented. The microstructure and mechanical properties of the crack-free Nb2O5 are assessed. The tribological data obtained are benchmarked with different NbC grades, ceramics, cermets and thermally sprayed coatings.
Niobium carbide for wear protection - tailoring its properties by processing and stoichiometry
(2016)
Niobium carbide is a hardly explored carbide but its functional profile shows a high potential for wear protection and tribological applications, which are currently dominated by tungsten carbide. Surprisingly little information is available on niobium carbide (NbC). Niobium carbide can be either synthesized by carbothermal conversion of Nb2O5 or be metallurgically grown and leached out. Furthermore, NbC hardmetal grades can be bonded by all known metallic binders and processed and sintered in exactly the same way as WC-based hardmetals. Niobium is today largely available. NbC can be efficiently produced, provides comparably low friction in many relevant tribo-contacts and displays low wear. NbC and Nb2O5 have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO3 and Co3O4. This contribution demonstrates the key characteristics of NbC and discusses its sustainability and reliable value chain.
The sales of niobium carbide (NbC) have grown in the last years, but NbC is still a hidden carbide and mainly used as grain growth inhibitor in hard metals. In the present work it was shown that the progress in the key properties, like HV30, KIC and strength, followed by machining and tribological results of the respective NbC grades.