Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (14)
- Beitrag zu einem Tagungsband (6)
- Vortrag (3)
Schlagworte
- Acidity (2)
- Band shape analysis (2)
- Infrared spectroscopy (2)
- Surface layer (2)
- Al substitution (1)
- Beanspruchung, thermisch (1)
- Bronsted acidity (1)
- Catalysis (1)
- Clinoptilolite (1)
- Confined liquid crystals (1)
Organisationseinheit der BAM
- 6 Materialchemie (1)
- 6.3 Strukturanalytik (1)
Eingeladener Vortrag
- nein (3)
The influence of the aluminum contents of MCM-41 (Si/Al ratio varied between 2.7 and 69) on the coordination of Al, on the acidity, and on the catalytic properties is studied by 27Al MAS NMR, temperature programmed desorption of ammonia, and the conversion of acetone. Based on TPDA results, an assignment of the peaks of desorption of ammonia is proposed. With low Al contents, the concentration of strong Brønsted acid sites, which are attributed to tetrahedral aluminum, increases with growing Al amounts. At higher Al contents, however, the number of strong acid sites decreases again. Besides usual strong Brønsted sites, TPDA reveals the existence of weak Brønsted and Lewis sites and of Lewis sites of a high acidic strength. Separation between the two types of sites of weak acidity is incomplete.
In the temperature programmed decomposition of NH4-exchanged MCM-41 samples, strong Lewis acid sites temporarily re-adsorb ammonia generated by the thermal decomposition of the NH4+ ions located at the Brønsted sites. Ammonia re-adsorption at Lewis sites results in a shift of the maximum of the TPDA peak to a higher temperature. Calcination of samples leads to the formation of strong Lewis sites at the expense of Brønsted sites. To evaluate the acidity of Al-MCM-41, recording of decomposition profiles has been extended to Ga- and Fe-MCM-41.
Catalytic activity in the conversion of acetone reaches its maximum with the sample based on Al-MCM-41 with the molar Si/Al ratio of 6.85. Highly favored formation of isobutene points to a comparably high acidic strength of the active sites.
Composites containing 4-n-octyl-4?-cyanobiphenyl (8CB) either confined to nanopores of molecular sieves with very large pores or coating silica nanoparticles of aerosil type at high silica-to-8CB ratios are investigated by IR spectroscopy. Band shape analysis was performed in wavenumber regions in which the peaks due to CN stretching, CH stretching and CH out-of-plane vibrations appear. Some of molecules confined to molecular sieves show spectroscopic features characteristic to a bulk-like 8CB matter located in the centre of the pores or in the inter-grain space. Other features of the IR spectra are due to 8CB molecules located in the surface layer, mostly forming hydrogen bonds between their CN groups and surface OH groups. Another part of the 8CB molecules in the surface layer may also interact by ? electrons of the aromatic rings. Hydrogen bonding is less hindered for the molecules of the surface layers onto aerosil particles than inside pores of the molecular sieves. Comparison is also made with the case of composites based on molecular sieves with small pores.
Thermal analysis measurements were applied to study the behavior of composite systems containing a nematic liquid crystal (LC), 4-n-octyl-4?-cyanobiphenyl (8CB) and aerosil particles. The silica density ?s (g of silica per 1 cm3 of LC) was varied from 0.20 to 12 g/cm3 in order to approach the monomolecular structure of the surface layer. Thus, thermogravimetric (TG) measurements were performed to get information on the LC content of the samples. Moreover, they allowed an unusual application, to characterize the interaction of 8CB molecules with aerosil surface because the corresponding curves show multistep processes the temperatures of which depend on the silica density. Differential thermal analysis (DTA) also indicates several processes. Some of them, mostly due to desorption, are endothermal. Other processes are exothermal, and these are assigned to chemical transformations. The sample with silica density of 12 g/cm3 has no endothermal desorption peak at low temperatures, and has the highest shift for the DTA peaks. It was supposed that its surface layer has a monomolecular structure. For representative samples, TGDTA studies were supported by FTIR investigations. Thus conventional TGDTA techniques have provided new tools to characterize the nanocomposites. Differential scanning calorimetry gives the behavior of the phase transitions. Samples with low silica density exhibit a depression of the phase transition temperatures characteristic for the bulk 8CB while those with high silica densities do not show any phase transitions.
The rotational molecular dynamics of water confined to nanoporous molecular sieves of a regular hexagonal (SBA-15) and of a foamlike pore structure was studied by dielectric spectroscopy in the frequency range from 10-2 to 109 Hz and in a broad temperature interval. Two relaxation processes were observed: the process at lower frequencies is related to water molecules forming a layer, which is strongly adsorbed at the pore surface, whereas the relaxation process at higher frequencies is assigned to fluctuations of water molecules situated close to the center of the pore. The relaxation times of the low-frequency process for both materials and of the high-frequency process for the SBA-15 material have an unusual saddlelike temperature dependence, reported here for the first time. To describe this temperature dependence, a model developed for water confined to nanoporous glasses by Ryabov et al. [J. Phys. Chem. B 2001, 105, 1845] was applied, which considers two competing effects. The characteristic features of these two competing processes were compared with those reported for other porous systems.
A series of AlMCM-41 molecular sieves was prepared with constant composition (Si/Al = 14.7) and presumably same pore structure but different pore diameters (from 2.3 to 4.6 nm). The pore size distribution is narrow for each sample. The rotational fluctuations of water molecules confined inside the pores were investigated applying broadband dielectric spectroscopy (10-2107 Hz) over a large temperature interval (213333 K). A relaxation process, slower than that expected for bulk water, was observed which is assigned to water molecules forming a surface layer on the pore walls. The estimated relaxation time has an unusual non-monotonic temperature dependence, which is rationalized and modeled assuming two competing processes: rotational fluctuations of constrained water molecules and defect formation (Ryabov model). This paper focuses on the defects and notably the influence of the hydroxyl groups of the pore walls. The Ryabov model is fitted to the data and characteristic parameters are obtained. Their dependence on pore diameter is considered for the first time. The found results are compared with those obtained for other types of molecular sieves and related materials.
The molecular mobility of a MOF-5 metal–organic framework was investigated by broadband dielectric spectroscopy. Three relaxation processes were revealed. The temperature dependence of their relaxation rates follows an Arrhenius law. The process observed at lower temperatures is attributed to bending fluctuations of the edges of the cages involving the Zn–O clusters. The processes ('region II') at higher temperatures were assigned to fluctuations of phenyl rings in agreement with the NMR data found by Gould et al. (J. Am. Chem. Soc. 2008, 130, 3246). The carboxylate groups might also be involved. The rotational fluctuations of the phenyl rings leading to the low frequency part of relaxation region II might be hindered either by some solvent molecules entrapped in the cages or by an interpenetrated structure and have a broad distribution of activation energies. The high frequency part of region II corresponds nearly to a Debye-like process: This is explained by a well-defined structure of empty pores.
Unusual relaxation behavior of water inside the sodalite cages of faujasite-type molecular sieves
(2002)
Broad-band dielectric spectroscopy (10-2 to 109 Hz) is applied to investigate the molecular dynamics of NaY, a zeolite of faujasite structure. A dc conductivity contribution and three relaxation processes were revealed in the dielectric spectra. The relaxation process in the high-frequency range ascribed to orientational fluctuations of water molecules inside the sodalite cages is studied in detail. As a main result it is found that its mean relaxation time has an unusual saddle-like temperature dependence, which obeys neither an Arrhenius nor a Vogel-Fulcher-Tammann law. A quantitative description was given on the basis of a model recently developed by Feldman et al. (J. Phys. Chem. B 2001, 105, 1845) to analyze the dynamics of water confined in nanoporous glasses. Reasonable values for the activation energies of orientational fluctuations and of defect formation as well as for the defect concentration were obtained.