Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (21)
- Beitrag zu einem Tagungsband (6)
- Beitrag zu einem Sammelband (4)
- Vortrag (4)
- Posterpräsentation (4)
Schlagworte
- BAM-List (6)
- Dangerous goods (6)
- Compatibility evaluations (5)
- Corrosion tests (5)
- Glass (5)
- High-alloyed metallic tank materials (5)
- Water content (4)
- Water speciation (4)
- Borosilicate glass (3)
- Internal friction (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (12)
- 5.6 Glas (12)
- 6 Materialchemie (1)
- 6.3 Strukturanalytik (1)
Eingeladener Vortrag
- nein (4)
The structural investigation of hydrated borate glasses provides new insights on the influence of water on boron speciation using spectroscopic methods. In the present study three soda–lime–borate glasses (NCBx with x = 5, 15 and 25 corresponding to xNa2O, 10CaO, 90 - xB2O3 in mol%) were prepared with water content up to 8 wt.%. The water speciation in the glasses was derived by near-infrared (NIR) spectroscopy while boron speciation was investigated by 11B MAS NMR (Magic Angle Spinning Nuclear Magnetic Resonance). For the three glasses effective molar absorption coefficients were determined experimentally for the bands at 5200 cm- 1 and 4600 cm- 1, corresponding to combination modes of H2O molecules and OH-groups, respectively. In contrast to silicate glasses, in which at most ~ 2 wt.% H2O are dissociated to OH-groups, the amount of dissociated H2O may even exceed 5 wt.% in borate glasses. The fraction of tetrahedral to total boron (N4 = BIV / BIV + BIII) is predominantly controlled by the ratio of Na2O + CaO / B2O3, but only weakly affected by the water content of the glasses. When increasing the H2O content from 0 to 8 wt.%, N4 increases from 25% to 26% for NCB5 and from 42% to 47% for NCB25 glasses.
In the present study we have investigated whether the effect of water on properties of borate glasses resembles that of alkali oxide. Soda-lime-borate glasses with nominal compositions of x Na2O, 10 CaO, (90-x) B2O3 (x = 5, 15 and 25 mol%) were doped with up to 8 wt.% H2O by processing glass powder + distilled water in platinum capsules in an internally heated gas pressure vessel at 1523 K and 500 MPa. The water content of hydrous glasses was determined by Karl-Fischer titration and near-infrared spectroscopy. The glass transition temperature T-g. was derived from DTA and micropenetration experiments for which the effect of water loss at the surface of the hydrous glasses was studied. Heating glass samples at 10 K min(-1) in the DTA resulted in T-g values which are close to T-12 isokom temperatures confirming the equivalence of enthalpy relaxation and viscous relaxation for borate glasses. For all three glass series it is shown that T-g strongly decreases whereas the liquid fragility strongly increases upon the addition of water. These findings reveal that H2O primarily causes breaking of B-O-B bonds rather than supporting 4-fold coordinated boron as it is well-known for alkali oxides in this concentration range. (C) 2015 Elsevier B.V. All rights reserved.
To understand the influence of water and alkalis on aluminosilicate glasses, three polymerized glasses with varying ratios of Na/K were synthesized [(22. 5-x)Na2O-xK2O-22.5 Al2O3-55 SiO2 with x = 0, 7.5, and 11.25]. Subsequently, these glasses were hydrated (up to 8 wt% H2O) in an internally heated gas pressure vessel. The density of hydrous glasses linearly decreased with water content above 1 wt%, consistent with the partial molar volume of H2O of 12 cm3/mol. Near-infrared spectroscopy revealed that hydroxyl groups are the dominant species at water content of <4 wt%, and molecular water becomes dominating at water content of >5 wt%. The fraction of OH is particularly high in the pure Na-bearing glass compared to the mixed alkali glasses. 27Al magic angle spinning-NMR spectroscopy shows that aluminum is exclusively fourfold coordinated with some variations in the local geometry. It appears that the local structure around Al becomes more ordered with increasing K/Na ratio. The incorporation of H2O reinforces this effect. The differential thermal analysis of hydrous glasses shows a significant mass loss in the range of glass transition already during the first upscan, implying the high mobility of water in the glasses. This observation can be explained by the open structure of the aluminosilicate network and by the low dissociation enthalpy of H2O in the glasses (≈ 8 kJ/mol). The effect of the dissolved H2O on the glass transition temperature is less pronounced than for other aluminosilicate glasses, probably because of the large fraction of Al in the glasses.
Literature data on the effect of water on the glass transition in silicate melts are gathered for a broad range of total water content cw from 3 × 10-4 to 27 wt%. In terms of a reduced glass transition temperature Tg*=Tg/TgGN, where TgGN is Tg of the melt containing cw?0.02 wt% total water, a uniform dependence of Tg* on total water content (cw) is evident for silicate melts. Tg* decreases steadily with increasing water content, most strongly at the lowest water content where H2O is dominantly dissolved as OH. For water-rich melts, the variation of Tg* is less pronounced, but it does not vanish even at the largest water contents reported (?27 wt%). Tg* vs. cw is fitted by a three-component model. This approach accounts for different transition temperatures of the dry glass, hydroxyl and molecular water predicting Tg* as a weighted linear combination of these temperatures. The required but mostly unknown water speciation in the glasses was estimated using IR-spectroscopy data for hydrous sodium trisilicate and rhyolite.
Wasserdiffusion in Floatglas
(2005)
Crack growth velocity in alkali silicate glasses was measured in vacuum across 10 orders of magnitude with double cantilever beam technique. Measured and literature crack growth data were compared with calculated intrinsic fracture toughness data obtained from Young´s moduli and the theoretical fracture surface energy estimated from chemical bond energies. Data analysis reveals significant deviations from this intrinsic brittle fracture behavior. These deviations do not follow simple compositional trends. Two opposing processes may explain this finding: a decrease in the apparent fracture surface energy due to stress-induced chemical changes at the crack tip and its increase due to energy dissipation during fracture.
In Germany the BAM-List Requirements for Tanks for the Transport of Dangerous
Goods is the basis for substance-related prototype approvals for tank containers designed for
the carriage of dangerous goods. Such approval is undertaken by the Federal Institute for
Materials Research and Testing (BAM). Compatibility evaluations of selected metallic
material groups as well as of polymeric gasket and lining materials under the influence of
dangerous goods and water-polluting substances are published in section 5 of the BAM-List.
According to the relevant regulations for rail, road and sea transportation a compulsory
internal inspection after certain intervals is required. The required corrosion resistance
depends on the length of the inspection interval.
There is a large number of dangerous goods with a high corrosivity to metals, where the standard
steels are not corrosion resistant. Chemical companies, transportation providers and tank
producers need tanks made of corrosion-resistant materials in order to protect the tank shell
and prevent contamination of high-value cargo as well as the environment. One solution is to
line the tank with a polymeric material, an alternative solution to corrosion problems is the
application of high-alloyed materials.
Only a narrow limited number of corrosion test results of these high-alloyed materials under
the influence of corrosive dangerous goods are available. In order to change this situation and
include the superaustenitic steels X1NiCrMoCuN25-20-7 (Alloy 926), X1NiCrMoCu32-28-7
(Alloy 31) and the nickel-based alloy NiCr23Mo16Al (Alloy 59) in the BAM-List, BAM,
IKS Dresden and ThyssenKrupp VDM started an comprehensive test program with welded
specimens made. The program comprises corrosion resistance evaluations of the high-alloyed
materials in substances representing 12 major groups of corrosive dangerous goods (e.g.
inorganic halogenides, organic acidic halogenides, halogenic carbonic acids, chlorosilanes,
chlorates, perchlorates, chlorites, hypochlorites and hydrogen sulphates).
The test results, presented in this paper, will be included in the upcoming 8th edition of the
BAM-List and therefore available for the costumer.