In the area of hydrogen safety, research facilities are essential for the experimental investigation of relevant phenomena, for testing devices and safety concepts, as well as for the generation of validation data for the various numerical codes and models. Within the framework of the European HySafe Network of Excellence (NoE), the 'Integration of Experimental Facilities (IEF)' activity has provided basic support for joint experimental work. Even beyond the funding period of the HySafe NoE in the 6th Framework Program, IEF represents a long-lasting effort for the sustainable integration of experimental research capacities and expertise of the partners from different research fields. In order to achieve a high standard in the quality of experimental data provided by the partners, emphasis was put on the know-how transfer between the partners. On the one hand, documentation on the experimental capacities was prepared and analyzed. On the other hand, a wiki-based communication platform was established, supported by biannual workshops covering topics ranging from measurement technologies to safety issues. Based on the partners' contributions, a working document was created on best practice including the joint experimental knowledge of all partners with regard to experimental set-ups and instrumentation. The paper gives an overview of the IEF partners and the network activities over the last five years.
The use of supplementary cementing materials (SCMs) added to concrete mixtures can avoid the alkali-silica reaction. Such materials have a wide range of composition and therefore the inhibition mechanisms can be very differently.
The effectiveness of SCMs which provide silica and alumina into the alkaline solution cannot only be explained by reducing the OH--concentration of the pore solution. From dissolution experiments in potassium hydroxide solutions, an interaction was noted between the aggregate and five SCMs via the alkaline solution. Under specific conditions, no silica is released from the aggregate grains.
Mineralogical investigations (XRD, SEM+EDX) of the grain surfaces confirm that quartz is the main source of silica. In the presence of alumina providing SCMs, the quartz dissolution is strongly reduced or even sometimes stopped. On surfaces of grains a very thin layer can be observed which is probably responsible for reduction or stopping of the silica dissolution and therefore for the inhibition of ASR.