This work aims to predict the microstructure of recrystallized medium and high-entropy alloys (MEAs and HEAs) with a face-centered cubic structure, in particular the density of annealing twins and their thickness. Eight MEAs and five HEAs from the Cr-Mn-Fe-Co-Ni system are considered, which have been cast, homogenized, cold-worked and recrystallized to obtain different grain sizes. This work thus provides a database that could be used for data mining to take twin boundary engineering for alloy development to the next level. Since the stacking fault energy is known to strongly affect recrystallized microstructures, the latter was determined at 293 K using the weak beam dark-field technique and compared with ab initio simulations, which additionally allowed to calculate its temperature dependence. Finally, we show that all these data can be rationalized based on theories and empirical relationships that were proposed for pure metals and binary Cu-based alloys.
The isothermal high‐temperature oxidation behavior of the equiatomic CrFeNi medium‐entropy alloy is a key issue that determines whether this material is suited for high‐temperature application. In this view, the understanding of the long‐term behavior is even more crucial than short‐term corrosion effects. Herein, a single‐phase CrFeNi alloy of the face‐centered‐cubic structure is exposed to synthetic air at 1000, 1050, and 1100 °C for 24, 100, and 1000 h and its oxidation behavior is systematically compared to that of 316L steel, which shows a surprising initial oxidation stabilization during early stages. The oxidation rate of CrFeNi is parabolic at 1000 °C (with a parabolic constant kp = 1.4·10−5 mg−2 cm−4 s−1) and 1050 °C (kp = 2.7·10−5 mg−2 cm−4 s−1), but breakaway oxidation occurs at 1100 °C after 4 h of exposure. In all cases, the oxide scales are found to (at least) partially spall off. Chromium diffuses outward to form a Cr2O3 layer at the gas/oxide interface, and a thin layer of (Cr, Fe, Ni)3O4 is identified at the oxide/alloy interface. Unlike the 316L alloy, which contains more Mn and Fe, the CrFeNi alloy does not show any catastrophic oxidation behavior at the investigated conditions.