Towards an industrial laser doping process for the selective emitter using phosphoric acid as dopant
(2011)
Different laser supported approaches have already been realized, proving the great potential of laserdoped selective emitters (LDSE). However, it is challenging to establish a low-cost process by using pulsed laser tools. So far a single-step process only leads to satisfying results utilizing cw-lasers. In this paper we have examined a two-step process to produce laser-doped selective emitters on multicrystalline textured standard silicon photovoltaic wafers (90-Ω/sq-Emitter, SiN-antireflection coating (ARC)). The precise ARC removal by near-infrared fs-laser pulses (30 fs, 800 nm), and the doping of uncoated silicon wafers by ns-laser pulses (8 ns, 532 nm) were systematically investigated. In the fs-experiment, optimum conditions for ARC removal were identified. In the nsexperiments under suitable conditions (melting regime), the phosphorous concentration underneath the wafer surface was significantly increased and the sheet resistance was reduced by nearly a factor of two. Moreover, electrical measurements on fired metallization fingers deposited on the laser processed wafers showed low contact resistances. Hence, wafer conditioning with combined fs-laser- and ns-laser-processes are expected to be a promising technology for producing selective emitters.
High-power optical multimode fibers are essential components for materials processing and surgery and can limit the performance of expensive systems due to breakdown at the end faces. The aim of this paper is the determination of laser-induced damage thresholds (LIDT) of fibers (FiberTech) and preforms (Heraeus Suprasil F300). Preforms served as models. They were heated up to maximum temperatures of 1100, 1300 and 1500°C and cooled down to room temperature at rates of 10 K min-1 (oven) and ~105 K min-1 (quenched in air) to freeze in various structural states simulating different conditions similar to a drawing process during the production of fibers. Single- and multi-pulse LIDT measurements were done in accordance with the relevant ISO standards. Nd:YAG laser pulses with durations of 15 ns (1064 nm wavelength) and 8.5 ns (532 nm) at a repetition rate of 10 Hz were used. For the preforms, LIDT values (1-on-1) ranged from 220 to 350 J/cm² (1064 nm) and from 80 to 110 J/cm² (532 nm), respectively. A multi-pulse impact changed the thresholds to lower values. The LIDT (1064 nm wavelength) of the preforms can be regarded as a lower limit for those of the fibers.
Optical multimode fibers are applied in materials processing (e.g. automotive industry), defense, aviation technology, medicine and biotechnology. One challenging task concerning the production of multimode fibers is the enhancement of laser-induced damage thresholds. A higher damage threshold enables a higher transmitted average power at a given fiber diameter or the same power inside a thinner fiber to obtain smaller focus spots.
In principle, different material parameters affect the damage threshold. Besides the quality of the preform bulk material itself, the drawing process during the production of the fiber and the preparation of the fiber end surfaces influence the resistance. Therefore, the change of the laser-induced damage threshold of preform materials was investigated in dependence on a varying thermal treatment and preparation procedure.
Single and multi-pulse laser-induced damage thresholds of preforms (F300, Heraeus) were measured using a Q-switched Nd:YAG laser at 1064 nm wavelength emitting pulses with a duration of 15 ns, a pulse energy of 12 mJ and a repetition rate of 10 Hz. The temporal and spatial shape of the laser pulses were controlled accurately.
Laser-induced damage thresholds in a range from 150 J cm-2 to 350 J cm-2 were determined depending on the number of pulses applied to the same spot, the thermal history and the polishing quality of the samples, respectively.
For pulse laser materials processing often optical step index and gradient index multimode fibers with core diameters ranging from 100 to 600 μm are used. The design of a high power fiber transmission system must take into account limitations resulting from both surface and volume damage effects. Especially, breakdown at the fiber end faces and self-focusing in the fiber volume critically influence the fiber performance. At least operation charts are desirable to select the appropriate fiber type for given laser parameters.
In industry-relevant studies the influence of fiber core diameter and end face preparation on laser-induced (surface) damage thresholds (LIDT) was investigated for frequently used all-silica fiber types (manufacturer LEONI). Experiments on preform material (initial fiber material) and compact specimens (models of the cladding and coating material) accompanied the tests performed in accordance with the relevant LIDT standards ISO 21254-1 and ISO 21254 2 for 1-on-1 and S-on-1 irradiation conditions, respectively. The relation beam diameter vs. LIDT was investigated for fused silica fibers. Additionally, laser-induced (bulk) damage thresholds of fused silica preform material F300 (manufacturer Heraeus) in dependence on external mechanical stress simulating fiber bending were measured. All experiments were performed with 10-ns laser pulses at 1064 and 532 nm wavelength with a Gaussian beam profile.
High-power optical multimode fibers are essential components for materials processing
and surgery and can limit the reliability of expensive systems due to breakdown at the end faces.
The breakdown threshold of fibers is determined by intrinsic materials properties and parameters of
the technology applied. The aim of this paper is the identification of technological parameters that
are crucial for the fiber quality.
Fibers were drawn from preforms of Heraeus SWU with core material F300 and a low amount of
OH-. Both, the cladding (fluorine doped SiO2) to core diameter ratio (CCDR) and the drawing speed
were varied. CCDR values between 1.05 and 1.4 were used. Afterwards, the laser-induced damage
thresholds (LIDT) of the fibers were determined. For comparison, also samples from preforms,
which underwent different thermal treatments above the transition temperature, were tested with
respect to their damage resistivity. Single and multi pulse LIDT measurements were done in
accordance with the relevant ISO standards. Nd:YAG laser pulses with durations of 15 ns (1064 nm
wavelength) and 8.5 ns (532 nm) at a repetition rate of 10 Hz were utilized. For the fibers, LIDT
values (1-on-1, 1064 nm and 532 nm) increased with growing CCDR and with decreasing drawing
velocities.
Optical multimode fibers made of fused silica are widely used for transmission of high power laser pulses. Bending of fibers creates mechanical stress inside the material. The bend stress of a fiber can be calculated from bend radius, geometrical fiber parameters and Young's Modulus of the fiber core material and reaches typically values of 220 MPa. A thermo-elastic model of Kusov et al. predicts a quadratic dependence of laser-induced damage threshold fluence with applied stress.
In the present study, fiber preform material F300 (Heraeus) was loaded mechanically with pressures up to 220 MPa representing 20% of the pressure resistance of fused silica. Bulk laser-induced damage thresholds (LIDT) were evaluated using a longitudinal multimode Q-switched Nd:YAG laser (1064 nm) at a pulse duration of 12 ns with polarization states parallel and perpendicular to the stress direction. LIDT of fused silica samples of about 700 J/cm2 were found. LIDT did not show a dependence on mechanical pressure and polarization state which is a consequence of the small ratio of maximum applied stress (220 MPa) to Young's Modulus of fused silica (72.5 GPa).
Single and multi pulse laser-induced damage thresholds (LIDT) of core, cladding, and coating materials of high-power
optical multimode fibers were determined in accordance with ISO 11254 for 532 nm and 1064 nm wavelength in the 10-ns
pulse duration regime with spatial Gaussian beam shape. For all-silica fibers, LIDT increases with rising core diameter in a range between 100-600 µm for a constant cladding-core ratio of 1.2. The damage resistance of the low refracting cladding (0.3 % fluorine doped fused silica) is comparable to the undoped SiO2 core. Coating materials show significantly lower LIDT than light-guiding parts of the fibers.