Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (21)
- Vortrag (8)
- Sonstiges (5)
- Posterpräsentation (4)
- Beitrag zu einem Tagungsband (3)
- Beitrag zu einem Sammelband (1)
Sprache
- Englisch (42) (entfernen)
Schlagworte
- Mechanical properties (8)
- IIT (4)
- Nanoindentation (4)
- ISO 14577 (3)
- Instrumented indentation testing (3)
- Calibration (2)
- Dynamic testing (2)
- Friction (2)
- Instrumented Indentation Testing (2)
- Multilayer (2)
Organisationseinheit der BAM
- 6 Materialchemie (6)
- 6.7 Materialsynthese und Design (5)
- 6.2 Material- und Oberflächentechnologien (2)
- 9 Komponentensicherheit (2)
- 9.5 Tribologie und Verschleißschutz (2)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
- 6.6 Physik und chemische Analytik der Polymere (1)
Eingeladener Vortrag
- nein (8)
Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.
Nowadays the Instrumented Indentation Testing (IIT) is one of the most commonly used methods to determine the mechanical properties of materials in the nano range. This method is already extensive standardized in EN ISO 14577 part 1-4. Because of the great interest of researchers and industries in investigations of time depending material behavior mostly all suppliers of IIT equipment are offering the possibility of dynamic testing. Realizing this development ISO/TC 164/SC3 Hardness Testing has proposed to start the new standardization project “Linear elastic dynamic instrumented indentation testing DIIT”. The development of this standard is accompanied by the first international intercomparing exercise comparing results of dynamic instrumented indentation testing from testing machines using different hardware solutions and different models for data evaluation.
The draft of part 5 of ISO 14577 “Linear elastic dynamic instrumented indentation testing DIIT” specifies verification and calibration of testing machines for carrying out the measurement of the dynamic material response when an oscillatory force or displacement, with amplitudes small in comparison to the prescribed target values, is imparted to the indenter while the indenter is continuously loaded to a prescribed target load or target depth or while the load or displacement is held constant at a prescribed target value. In case of a material showing plastic-elastic behavior, the measured dynamic response is used for continuous evaluation of the dynamic stiffness of the contact as a function of depth and frequency. Using the dynamic stiffness of the contact a reduced dynamic modulus will be calculated. In case of a material showing visco-elastic behavior from the measured dynamic response also the dynamic contact damping coefficient as function of depth and frequency is evaluated continuously. Using dynamic contact stiffness and dynamic contact damping coefficient reduced lost and storage modulus for visco-elastic materials will be calculated.
The main normative requirements of the draft will be presented and discussed in the light of the first results of the intercomparing excise.
Ti/TiN multilayer coatings with multilayer periods in the range 550 nm and a final thickness of 2 µm were deposited on steel substrates by cyclic modulation of nitrogen gas flow into the chamber of a PVD sputtering device. Coating characterization was performed by cross-sectional transmission electron microscopy, glancing-angle X-ray diffraction and instrumental indentation testing. Individual a-titanium and titanium nitride layers were always observed, although for the finer microstructures, the TiN layers were thicker than the Ti layers by a factor three. The plastic hardness of the films increased steadily with decreasing layer spacing, following a HallPetch relationship. Finally, a hardness value of 42 GPa was reached, which is similar to that of a thick TiN monolayer, prepared under the same coating conditions.
A calibration procedure for the detection efficiency of energy dispersive X-ray spectrometers (EDS) used in combination with scanning electron microscopy (SEM) for standardless electron probe microanalysis (EPMA) is presented. The procedure is based on the comparison of X-ray spectra from a reference material (RM) measured with the EDS to be calibrated and a reference EDS. The RM is certified by the line intensities in the X-ray spectrum recorded with a reference EDS and by its composition. The calibration of the reference EDS is performed using synchrotron radiation at the radiometry laboratory of the Physikalisch-Technische Bundesanstalt. Measurement of RM spectra and comparison of the specified line intensities enables a rapid efficiency calibration on most SEMs. The article reports on studies to prepare such a RM and on EDS calibration and proposes a methodology that could be implemented in current spectrometer software to enable the calibration with a minimum of operator assistance.
Thin polybutadiene/polystyrene blend films were deposited on glass substrates by spin-coating. The two polymers were chosen, as they are immiscible and differ strongly in their mechanical properties. The blend was characterized with Tapping Mode and force–distance curves. Several advantages of force–distance curves measurements compared to Tapping Mode are shown, most of all the capability of yielding quantitative information about several properties, such as Young's modulus and adhesion. Also the aging behaviour of the blend exposed to air could be observed, in particular the increase of the Young's modulus due to cross-linking and dewetting processes. Additionally, the sample was used to improve the resolution of force–distance curves up to 6 nm, which is to date the best resolution achieved with force–distance curves. Such an improvement resolves the major disadvantage of force–distance curves, compared to other scanning mode, i.e. its inferior resolution.
Silica coatings filled with nanoscaled inorganic fullerene-like tungsten disulphide (IF-WS2) have been prepared through a solgel process on stainless steel substrates, and the structure and mechanical properties have been investigated. The precursor was prepared from a mixture of colloidal silica, 3-glycidoxypropyltrimethoxysilane (GLYMO), water and ethanol, adjusted to pH 4 with HNO3. In this solution WS2 is dispersed and in some cases immediately before coating ethylenediamine (ED) is added. The stainless steel substrates are dip-coated, dried in air and heat-treated in the temperature range of either 150360 °C in air or up to 900 °C in vacuum. The solidification process is followed by differential thermal analysis (DTA). The resulting brown coloured coatings have a thickness of 1.54 µm. Scanning electron microscopy investigations (SEM) show that the WS2 nanoparticles are embedded as small aggregates in a hybrid silica matrix. X-ray diffraction (XRD) measurements prove that most of the tungsten disulphide embedded in the matrix can be protected against oxidation even after curing the samples at temperatures up to 900 °C. Hardness and modulus of the hybrid silica films were measured through an instrumented indentation test. Increasing the temperature of the heat treatment yields an increase of hardness from 0.3 to 1 GPa and of modulus from 3 to 17 GPa. The amount of up to 10 wt.% WS2 in the coatings has no remarkable influence on hardness and modulus of the samples.
Modified Yoldas sols can be used to prepare crack-free well adherent layers on different substrate materials such as sodalime glass, corundum and metal (IN-718). These layers having thicknesses of 0.6 µm are strain tolerant and withstand thermal cycling between 810 °C and room temperature. Introducing alpha-Al2O3 filler particles into modified Yoldas sols allows the preparation of thicker layers of 1.6 µm, which as well can be thermally cycled without noticeable delaminations. Chemical bonding seems to be the predominant layer bonding mechanism.
Polycrystalline Ni materials with grain sizes less than 100 nm (nano crystalline NC) and with grain sizes in the micrometer range (micro crystalline MC) in form of thin films have become important in many technologies due to their improved physical, chemical and mechanical properties. Usual the mechanical properties of such coatings are described by a Hardness value and a Young´s modulus measured by Instrumented Indentation Testing (IIT).The behavior of such coatings during indentation test is influenced by different size effects having their representative length scale – grain size, coating thickness, length that characterizes the depth dependence of the hardness (Indentation Size Effect ISE). To estimate realistic values for the intrinsic coating Hardness and Young´s modulus all size effects have to be considered.
For this work thin nano crystalline Ni – coatings (average grain size 30 nm) with thickness from 1 μm to 5 μm were electrodeposited on brass substrates. Indentation tests in the continuous stiffness measurement (CSM) mode were provided on as prepared Ni – coatings using a G200 Nanoindentation system (Fa. Keysight). For estimation of the intrinsic hardness of the coatings from composite hardness values calculated from the measured force –displacement curve using the Oliver & Pharr method, the model described by Z.S. Ma [1] was used.
It was found that the experimental data can be well described by the model. The fitted values for the intrinsic hardness and the fitting parameters will be given. The different values of intrinsic hardness and of length characterizing depth dependence of the hardness for different coating thickness are discussed as results of changes in the coating structure because of changes in deposition parameters.
[1] Z.S. Ma, Y.C. Zhou, S.G. Long, C. Lu: On the intrinsic hardness of a metallic film/substrate system: Indentation size and substrate effects. International Journal of Plasticity 34 (2012) 1-11.
This work is supported by European Metrology Program for Innovation and Research (EMPIR)
(JRP 14IND03 Strength – ABLE)
A Round Robin (RR) exercise on selected coated materials has been carried out with the aim of finding the optimal conditions for the analysis of nitride layers with GD-OES. Such pre-normative work is necessary for the evaluation of parallel development of the production of nitride layers as certified reference materials (CRMs). Two types of samples, TiN layer and VN layer, respectively, with chemical compositions close to stoichiometry and a thickness of ~3 µm, deposited on a steel substrate, have been provided to the RR participants. Additionally, another type of sample, a (100 nm CrNi/100 nm Cu) multilayer (ML) stack deposited on silicon wafer has also been included in the RR. This sample can be used as a CRM for checking GD spectrometer conditions and it has been proved helpful in further development of GDS instrumentation and methodology. The RR exercise has been performed in the frame of the EC Thematic Network on Glow Discharge Spectroscopy for Spectrochemical Analysis (GDS-Net).