Filtern
Erscheinungsjahr
- 2019 (16) (entfernen)
Dokumenttyp
- Beitrag zu einem Tagungsband (6)
- Vortrag (5)
- Zeitschriftenartikel (4)
- Forschungsbericht (1)
Schlagworte
- Alkali-activated materials (9)
- Abwasserinfrastruktur (2)
- Acoustic emission (2)
- Alkaliaktivierte Bindemittel (2)
- Biogene Schwefelsäurekorrosion (2)
- Blended cements (2)
- Bond strength (2)
- Brick clays (2)
- Calcined clays (2)
- Hygric deformations (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (5)
Materials with a high acid resistance are required in different important infrastructures. Examples include repair systems for sewer structures, where biogenic sulfuric acid corrosion is the major degradation mechanism. Low-calcium alkali-activated materials (AAMs) have been repeatedly observed to exhibit high acid resistance. However, the reasons for the high acid resistance of these materials were not fully under¬stood until recently, and the use of highly alkaline activator solutions to produce AAMs appears to hamper their commercial uptake. These issues have been tackled by characterising one-part AAMs and studying their alteration when exposed to sulfuric acid.
One-part AAMs were synthesized by mixing blends of solid silica and sodium aluminate with water, and subsequent curing at 60–80 °C. Acid resistance testing was performed according to DIN 19573, i.e. exposure to sulfuric acid at pH = 1 for 70 days. Characterisation of the cured and the acid-exposed materials was done by XRD, ATR-FTIR, SEM as well as 29Si, 27Al and 1H MAS NMR spectroscopy, including cross-polarisation and double-resonance methods.
Materials synthesized from industrial silicas were gel-zeolite composites, containing a substantial amount of unreacted ‘excess’ silica, while materials synthesized from rice husk ash were fully amorphous, containing ‘excess’ hydrous alumina. The sulfuric acid resistance of mortars based on these binders conformed to the requirements of DIN 19573 for sewer repair applications. The high acid resistance was caused by precipitation of silica gel at the mortar–solution interface, inhibiting further degradation. The presence of alumina gel may inhibit bacterial activity, potentially further improving performance in sewer environments.
The phase assemblage of silica/sodium aluminate-based one-part AAMs can be adjusted via choice of the silica starting material. Properly designed materials exhibit excellent acid resistance, caused by precipi¬tation of silica gel which protects subjacent regions, and they may also inhibit bacterial activity.
Additive manufacturing of alkali-activated materials currently attracts a lot of attention, because of the possibility to produce customized high-performance elements for a range of applications, potentially being more resource-efficient than conventionally produced parts. Here, we describe a new additive manufacturing process for alkali-activated materials that is based on selective laser-heating of lithium aluminate/microsilica slurries. The new process-material combination allows to manufacture elements with complex geometries at high building rates and high accuracy. The process is versatile and transferrable to structures of sizes differing by orders of magnitude. The mechanical strength of the obtained materials was in the range of values reported for conventional metakaolin-based geopolymers, and superior to what has been hitherto reported for alkali-activated materials produced by additive manufacturing. This mechanical performance was obtained despite the fact that the degree of reaction of the lithium aluminate and the microsilica was low, suggesting that significant reactions took place only at the surface of the microsilica particles.
Einkomponentige alkaliaktivierte Bindemittel (AAB), d. h. AAB, bei denen der Aktivator als Feststoff im Bindemittel vorliegt, weisen Vorteile hinsichtlich der praktischen Anwendung im Bauwesen gegenüber konventionellen AAB auf. Einkomponentige AAB lassen sich als Gemische aus reaktiver Silica und Natriumaluminat herstellen, wobei die Reaktionsprodukte von der eingesetzten Silica und den Verhältnissen Na2O/Al2O3/SiO2/H2O abhängen: Während Mikrosilica und ähnliche Reststoffe zu zeolithreichen Produkten führen, erhält man aus Reisschalenasche vollständig amorphe Gele (sog. «Geopolymere »). Mörtel auf Basis solcher Bindemittel entsprechen den Anforderungen von DIN 19573:2016-03 hinsichtlich des Widerstands gegen Schwefelsäureangriff (Prüfung bei pH = 1 für 70 d) und sind damit potentiell als Reparatursysteme für Abwasserinfrastruktur geeignet. Untersuchungen mittels 29Si-MAS-NMR und 1H-29Si-Kreuzpolarisations(CP)-MAS-NMR sowie REM-Aufnahmen von erhärteten und dem Schwefelsäureangriff ausgesetzten AAB zeigen, dass der hohe Säurewiderstand v. a. auf die Fällung von Silicagel an der Grenzfläche Mörtel/Säure zurückzuführen ist, wodurch der Korrosionsfortschritt in darunterliegenden Schichten verlangsamt wird.
Einkomponentige alkaliaktivierte Bindemittel (AAB), d. h. AAB, bei denen der Aktivator als Feststoff im Bindemittel vorliegt, weisen Vorteile hinsichtlich der praktischen Anwendung im Bauwesen gegenüber konventionellen AAB auf. Einkomponentige AAB lassen sich als Gemische aus reaktiver Silica und Natriumaluminat herstellen, wobei die Reaktionsprodukte von der eingesetzten Silica und den Verhältnissen Na2O/Al2O3/SiO2/H2O abhängen: Während Mikrosilica und ähnliche Reststoffe zu zeolithreichen Produkten führen, erhält man aus Reisschalenasche vollständig amorphe Gele (sog. «Geopolymere»). Mörtel auf Basis solcher Bindemittel entsprechen den Anforderungen von DIN 19573:2016-03 hinsichtlich des Widerstands gegen Schwefelsäureangriff (Prüfung bei pH = 1 für 70 d) und sind damit potentiell als Reparatursysteme für Abwasserinfrastruktur geeignet. Untersuchungen mittels 29Si-MAS-NMR und 1H-29Si-Kreuzpolarisations(CP)-MAS-NMR sowie REM-Aufnahmen von erhärteten und dem Schwefelsäureangriff ausgesetzten AAB zeigen, dass der hohe Säurewiderstand v. a. auf die Fällung von Silicagel an der Grenzfläche Mörtel/Säure zurückzuführen ist, wodurch der Korrosionsfortschritt in darunterliegenden Schichten verlangsamt wird.
The aim of RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories.
The use of calcined clays as supplementary cementitious materials (SCMs) has been identified as a viable option to decrease the CO2 emissions related to cement production. However, while extensive data is available about kaolinitic clays in this context, other clays such as illitic clays appear to be under-studied. Therefore, in the present study, two illitic clays were compared to two low-grade kaolinitic clays in terms of transformations in the calcination temperature range 650–900 °C, and performance of the calcined clays in blended cement pastes as measured by strength evolution, heat release, hydrated phase formation and portlandite consumption. The illitic clays required a higher calcination temperature for complete dehydroxylation of their illite than what is necessary for dehydroxylation of kaolinite. These higher calcination temperatures also led to particle sintering, significantly decreasing the specific surface area of the illitic clays, particularly for the clay with the higher Fe2O3 content. Nevertheless, while the kaolinitic clays generally exhibited the best performance as SCM, the illitic clay with lower Fe2O3 content performed similar to the kaolinitic clays when calcined at optimum temperature and applied at a moderate substitution rate. These findings demonstrate that several different clays have the potential to be used as SCM and indicate possible routes to identify suitable deposits for this purpose.
Der kritische, Korrosion auslösende Chloridgehalt für die Beurteilung der Korrosions-beständigkeit von Betonstahl in Geopolymerbetonen ist von großer Bedeutung für die Dauerhaftigkeitsprognose für bewehrte Elemente aus solchen Materialien. Es sind kaum experimentelle Daten in der Fachliteratur vorhanden und die vorliegenden Werte unterscheiden sich zwischen den Studien erheblich. In diesem Projekt wurde der kritische, Korrosion auslösende Chloridgehalt für Betonstahl (BSt 500) in flugaschebasierten (Ca-armen) Geopolymermörtel für verschiedene Beaufschlagungskombinationen bestimmt: Chloridbeaufschlagung mit 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser und anschließende Chloridbeaufschlagung im 1 M NaCl-Lösung; Auslaugen in entionisiertem Wasser, Carbonatisierung in Luft bei 20 °C und natürlicher CO2 Konzentration und anschließende Chloridbeaufschlagung mit 1 M NaCl-Lösung. Für Referenz-Zwecke wurde zusätzlich der Korrosion auslösende Chloridgehalt für eine Portland-Zement Mischung bei Auslagerung in 1 M NaCl-Lösung bestimmt.
Mixing and curing of geopolymers and related alkali-activated materials without storage and handling of highly alkaline solutions possesses advantages regarding safety and economic viability. One possible approach is to produce these materials from solid silica feedstocks and solid sodium aluminate, and subsequent mixing with water. We present a comparison between geopolymers and aluminosilicate gel-zeolite composites synthesized by this route from different silica feedstocks (by-product silica from chlorosilane production, microsilica, rice husk ash) and with different SiO2/Al2O3 ratios, using results from XRD, NMR, SEM, thermal analysis, mechanical and acid resistance testing. The use of rice husk ash favors formation of a fully amorphous geopolymer with high strength. Utilization of the other silica feedstocks leads to formation of aluminosilicate gel-zeolite composites, the amount and kind of zeolites depending on the feedstock and the SiO2/Al2O3 ratio. These composites show beneficial dehydration behavior, viz. no distinct dehydration step of thermal strain, with the phase assemblage after heating to 1000°C controlled by the starting composition. Mortars produced from both, the geopolymers as well as the composites, exhibit high resistance to sulfuric acid attack, making them promising materials for the construction and the repair of industrial and sewer structures.
Der Einsatz von calcinierten Tonen als Zementhauptbestandteil ist ein vielversprechender Weg, die mit der Zementherstellung und -verwendung verbundenen CO2-Emissionen zu senken. Im Vortrag werden die Randbedingungen hierfür sowie Ergebnisse eines aktuellen Vorhabens zur Calcinierung von illitreichen Tonen (Ziegeltonen) und anderen Tonen vorgestellt.
This study aims at investigating the use of coal fly ash-based alkali activated mortars as passive fire protection system for steel structures. These systems are used to slow down the temperature rise of the steel substrate in case of fire. In addition, the protective system should guarantee the ability to prevent and/or mitigate steel corrosion phenomena. The behavior of a light-weight mortar was compared to that of a normal-weight mortar. Density and porosity were measured to better characterize the physical properties of the mortars. The degree of protection in case of fire was assessed by performing medium-scale fire tests. Acoustic emission measurements were conducted to analyze cracking phenomena during the high temperature exposure. The corrosion process was evaluated using an electrochemical approach in order to monitor the durability of the developed material. Preliminary results show that a 20 mm-thick layer of light-weight mortar is able to protect the steel substrate from reaching the critical temperature of 500 °C for 38 minutes in case of cellulosic fire. In addition, alkali activated mortars provide protection for carbon steel in presence of aggressive environment (i.e. presence of chlorides). The corrosion resistance is strictly related to the physical properties of the developed mortars.