Reaction products and strength development of wastepaper sludge ash and the influence of alkalis
(2014)
Wastepaper sludge ash (WSA) from a newsprint paper mill was investigated for its mineralogical composition and its reaction products and strength development after activation with water and sodium and potassium hydroxide solutions. The results showed the WSA to consist of calcite, free lime, gehlenite, tricalcium aluminate, belite, talc, quartz and probably a glassy phase. The principle reaction product was monocarboaluminate (CO3–AFm) for the water- as well as for the alkali-activated WSA. Formation of monocarboaluminate and strength gain was more rapid for the alkali-activated WSA until 1 day of curing. However, afterwards reactions proceeded much slower when alkali solutions were used, leading to an about twice as high compressive strength for water-activated WSA mortars after 28 days of curing. The observed behavior is tentatively ascribed to a less uniform microstructure of the alkali-activated WSA. Significant differences between NaOH- and the KOH-activated WSA were not observed.
Gas separation is a key issue in various industrial fields. Hydrogen has the potential for application in clean fuel technologies. Therefore, the separation and purification of hydrogen is an important research subject. CO2 capture and storage have important roles in 'green chemistry'. As an effective clean technology, gas separation using inorganic membranes has attracted much attention in the last several decades. Membrane processes have many applications in the field of gas separation. Cement is one type of inorganic material, with the advantages of a lower cost and a longer lifespan. An experimental setup has been created and improved to measure twenty different cement membranes. The purpose of this work was to investigate the influence of gas molecule properties on the material transport and to explore the influence of operating conditions and membrane composition on separation efficiency. The influences of the above parameters are determined, the best conditions and membrane type are found, it is shown that cementitious material has the ability to separate gas mixtures, and the gas transport mechanism is studied.
The production and processing of ordinary Portland cement are responsible for nearly 5% of the world C02 emissions. Due to the world’s increasing requirement for building materials, this air pollution is growing up in the next decades. Alternative cement such as geopolymers can reduce these emissions effectively, Conventional geopolymer binders, produced ffom fly ash or metakaolin as aluminosilicate source and water-glass or alkali hydroxide Solutions as activator, are often used and studied. It is known that under appropriate conditions the starting materials form a three-dimensional aluminosilicate structure and create a gel-like matrix, In our case, a silica source from wastewater treatment of chlorosilane production and solid sodium aluminate as starting materials are initiated to harden by water. This procedure is known as “just add water” or “one-part” geopolymer formulation. These composites have significant advantages for use on construction site, but their Chemical structure is not extensively analyzed. In this work, a well known one-part geopolymer is investigated by 'H and 27A1 magic-angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy. Furthermore, it is shown that overlapping NMR lines can resolved with echo experiments and
The efficiency of wood gasification can be improved by applying membrane based gas separation operations in several of its sub-processes. In the present study the use of membranes made of hardened cement pastes for this purpose was investigated to provide a low cost alternative to conventional membrane materials. The pastes were tested for their diffusional properties in a Wicke-Kallenbach cell and analyzed with regard to their pore structure. The use of low water to binder ratios and slag and/or pozzolans led to a finer pore structure and higher separation factors; in particular, an approximately linear dependence of the separation factors on the threshold radii was observed. The results implicated that Knudsen diffusion is the prevailing diffusion mechanism in the membranes. Deviations from the theoretically expected separation factors were found, which may be ascribed to concentration polarization and channeling effects.
In paper recycling several types of waste sludges are produced, which contain organics as well as inorganic fillers of the recycled paper, e.g. kaolinite, calcite, talc, or titanium dioxide [1,2]. Part of these sludges is incinerated to recover energy and to reduce the volume of waste to be handled. The ashes generated in this process are commonly referred to as wastepaper sludge ash (WSA). The quantities of WSA produced are large and at present much of it is still landfilled or otherwise handled entailing costs.
Depending on the composition of the recycled paper and the conditions during processing and incineration, WSA can have cementitious properties. In the present investigation a CaC03-rich WSA was analyzed for reaction products and strength development after hydration with water, 2 M NaOH solution and 8 M NaOH solution. The rationale for activating the WSA with NaOH was to assess the behaviour of the WSA when alkalis are introduced to the System or when the WSA is used as addition in alkali-activated binders.
In paper recycling large amounts of waste sludge, containing organics as well as inorganic fillers of the recycled paper, are produced. A large fraction of these sludges is incinerated; the ashes generated in this process, often referred to as wastepaper sludge ash (WSA), have the potential to be used as binder material, either alone or as supplementary cementitious material. However, ashes from different paper mills differ in their Chemical and mineralogical composition, thus, the reaction products and the properties of the hardened binders may vary s i gn i fi cantley.
In the present study, a calcite-rich WSA was analyzed for reaction products and strength development. The WSA contained, besides calcite, hydraulic phases such as tricalcium aluminate (C3A) and belite (C2S), lime as well as inert phases. When activated with water, the WSA yielded a compressive strength of up to 12.3 MPa and the major hydration product was monocarboaluminate (C4A CO2 IIH2O or C4ACH11). Activation with 2M NaOH or 2M KOH solution caused a more rapid strength gain until one day of curing, but afterwards the strength development slowed down and the strength afiter 28 days was significantly lower than for the water-activated pastes. From TG analyses it is apparent that the higher strength of the alkaliactivated pastes after one day of curing was caused by a more rapid consumption of calcite and associated formation of C4ACH11. At later curing times the amount of calcite did not change substantially and consequently strength development almost ceased.
The results demonstrate the complex influence of alkaline conditions on the hydration of WSA and show that the reaction products, which determine the durability properties of the hardened pastes (and materials made from it), of the calcite-rich WSA differ from the products of other WS As, as discussed in the article.