In paper recycling large amounts of waste sludge, containing organics as well as inorganic fillers of the recycled paper, are produced. A large fraction of these sludges is incinerated; the ashes generated in this process, often referred to as wastepaper sludge ash (WSA), have the potential to be used as binder material, either alone or as supplementary cementitious material. However, ashes from different paper mills differ in their Chemical and mineralogical composition, thus, the reaction products and the properties of the hardened binders may vary s i gn i fi cantley.
In the present study, a calcite-rich WSA was analyzed for reaction products and strength development. The WSA contained, besides calcite, hydraulic phases such as tricalcium aluminate (C3A) and belite (C2S), lime as well as inert phases. When activated with water, the WSA yielded a compressive strength of up to 12.3 MPa and the major hydration product was monocarboaluminate (C4A CO2 IIH2O or C4ACH11). Activation with 2M NaOH or 2M KOH solution caused a more rapid strength gain until one day of curing, but afterwards the strength development slowed down and the strength afiter 28 days was significantly lower than for the water-activated pastes. From TG analyses it is apparent that the higher strength of the alkaliactivated pastes after one day of curing was caused by a more rapid consumption of calcite and associated formation of C4ACH11. At later curing times the amount of calcite did not change substantially and consequently strength development almost ceased.
The results demonstrate the complex influence of alkaline conditions on the hydration of WSA and show that the reaction products, which determine the durability properties of the hardened pastes (and materials made from it), of the calcite-rich WSA differ from the products of other WS As, as discussed in the article.
Alkali-activated slag materials are known for their high Chloride penetration resistance. This makes them potentially applicable as repair systems for damaged steel-reinforced concrete structures, which are exposed to chloride attack. For this purpose, the influence of the activator composition, i.e. the SiO2 and Na2O concentration of the alkaline solution on a) the compressive strength, b) shrinkage and mass change and c) the resistance against chloride penetration of four alkali-activated slag mortars (AASM) were studied. An ordinary Portland cement-based mortar was used as the reference sample. Increasing SiO2 and Na2O concentrations increased the strength, shrinkage and mass loss of the AASMs. The resistance of the mortars against chloride penetration was evaluated using the non-steady-state migration coefficient Dnssm obtained from NT BUILD 492. The results indicate that the Dnssm is related to differences in the pore solution of the AASMs rather than to differences in their microstructure. An upcoming study of the authors is going to evaluate this hypothesis by the accelerated chloride penetration (diffusion) test.