Filtern
Erscheinungsjahr
- 2015 (9) (entfernen)
Dokumenttyp
- Vortrag (4)
- Posterpräsentation (3)
- Zeitschriftenartikel (1)
- Beitrag zu einem Tagungsband (1)
Referierte Publikation
- nein (9) (entfernen)
Schlagworte
- Röntgenrefraktion (2)
- X-ray refraction (2)
- 3D Mikrostruktur (1)
- Aluminium alloy (1)
- Analyser based imaging (1)
- Analyser-based imaging (1)
- Analytical Science (1)
- CT (1)
- Computed tomography (CT) (1)
- Computertomographie (1)
Eingeladener Vortrag
- nein (4)
Hydrogen in metals can cause a degradation of the mechanical properties with possible subsequent hydrogen assisted cracking (HAC). Though, the mechanism of HAC is not completely understood yet and thus suitable methods for in situ investigations to characterise the crack formation are needed. X-ray computed tomography (CT) is a well-known tool for analysing these properties. However, the effective resolution of the detector system limits the detection of small defects by CT. Analyser based imaging (ABI) takes advantage of x-ray refraction at interfaces between volumes of different density, i.e. of cracks, pores, inclusions, etc., within the sample to detect defects smaller than the resolution of the detector system. In this study, measurements on an aluminium alloy weld showed that ABI allows us to resolve the 3D structure of cracks undetected by absorption based CT. Prospective investigations will analyse HAC in steels.
The combination of tomographic, microstructural data with other experimental techniques and with modeling is paramount, if we want to extract the maximum amount of information on material and component properties. In particular, quantitative image analysis, statistical approaches, direct discretization of tomographic reconstructions represent concrete possibilities to extend the power of the tomographic 3D representation to insights into the material and component performance. This logic thread holds equally for industrial and academic research, and valorizes expensive experiments such as those carried out at synchrotron sources, which cannot be daily repeated.
I will show a few examples of possible use of X-ray tomographic data for quantitative assessment of damage evolution and microstructural properties, as well as for non-destructive testing. Examples of micro-structured inhomogeneous materials will be given, such as Composites, Ceramics, Concrete, and Additively manufactured parts. I will also show how X-ray refraction computed tomography (CT) can be highly complementary to classic absorption CT, being sensitive to internal interfaces.
The effect of porosity and microcracking on the mechanical properties (strength, fracture toughness,Young’s modulus, and fracture energy) and thermal expansion of diesel particulate filter (DPF) gradecordierite materials has been investigated. A method to deconvolute the effect of porosity and microc-racking on Young’s modulus is proposed. In addition, the microcrack density and the pore morphologyfactor are calculated by applying a micromechanical differential scheme. The values of the investigatedmechanical properties are shown to decrease with an increase in porosity, but the thermal expansionvalues are insensitive to porosity. The variation in mechanical properties as a function of porosity leadsto distinct porosity dependence of thermal shock resistance for crack initiation and crack propagationfor DPF grade synthetic cordierite.
To better understand the mechanism of hydrogen assisted cracking (HAC), it is important to investigate the 3D structure of the cracks non-destructively. Since, cracks introduced by HAC are usually very small, conventional x-ray imaging methods often lack the required spatial resolution.
However, the detection of those cracks can be enhanced by taking advantage of refraction at interfaces within the sample.
To image this refractive deflection we employ analyser based imaging (ABI). In this work we aim at proving the enhanced crack detection of ABI by investigating an alluminum alloy weld.