Evaluation of high spatial resolution imaging of magnetic stray fields for early damage detection
(2017)
The paper discusses the evaluation of elastic and plastic strain states in two low-carbon steels of the same steel group with high spatial resolution GMR (giant magneto resistance) sensors. The residual stress distributions of tungsten inert gas welded plates were determined by means of neutron diffraction as a reference. The normal component of local residual magnetic stray fields arise in the vicinity of the positions of maximum stress. The experiments performed on flat tensile specimen indicate that the boundaries of plastic deformations are a source of stray fields. The spatial variations of magnetic stray fields for both the weld and the tensile samples are in the order of the earths magnetic field.
Diffuse ultrasonic measurements are used to monitor progressive stress-induced damage in a number of concrete specimens. Each specimen was subjected to uniaxial compression, applied in small steps over one or several load cycles. At each step, the loading was held constant and a series of ultrasonic measurements parallel and perpendicular to the loading were obtained. The measurements were taken during both the loading and unloading phases. The time scale of the signals was chosen such that the diffuse ultrasonic regime could be recorded. Using Coda Wave Interferometry (CWI), the corresponding changes in the velocity of diffuse ultrasonic waves were monitored. The evolution of the slope of the CWI velocity-stress curve with the increased level of damage in concrete is demonstrated.
For the first time we present direct 2D imaging of refracted X-rays without any discrimination of the Primary radiation. X-refraction works in analogy to visible light optics: X-rays are entirely deflected at interfaces where discontinuities of (electron) density occur. This is demonstrated at the example of inner and outer surfaces of model samples of well-defined geometry (fibres, capillaries, and monodisperse micro particles). The samples are scanned through a 50 μm monochromatic (20 keV) pencil beam. In order to warrant a sufficient angular resolution a 2D detector (pixel size 7 μm) is placed 3 m downstream of the sample. Scanning the sample in micron steps allows for detecting local changes of interface / surface orientation directly in two dimensions. At the actual angular resolution of about 3 seconds of arc (scattering vector increments Δk = 10-3 nm-1) and 50 μm spatial resolution (scanning) the material’s inner surfaces (with nanometer separation) can be characterized even at sampling rates below 1 second per frame. Moreover, our technique is suited to directly determine particle diameters of up to 250 nm by means of diffraction fringes. Some potential applications to technical submicron structures are discussed.
Additive Manufacturing (AM) through the Selective Laser Melting (SLM) route offers ample scope for producing geometrically complex parts compared to the conventional subtractive manufacturing strategies. Nevertheless, the residual stresses which develop during the fabrication can limit application of the SLM components by reducing the load bearing capacity and by inducing unwanted distortion, depending on the boundary conditions specified during manufacturing. The present study aims at characterizing the residual stress states in the SLM parts using different diffraction methods. The material used is the nickel based superalloy Inconel 718. Microstructure as well as the surface and bulk residual stresses were characterized. For the residual stress analysis, X-ray, synchrotron and neutron diffraction methods were used. The measurements were performed at BAM, at the EDDI beamline of -BESSY II synchrotronand the E3 line -BER II neutron reactor- of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results reveal significant differences in the residual stress states for the different characterization techniques employed, which indicates the dependence of the residual state on the penetration depth in the sample. For the surface residual stresses, longitudinal and transverse stress components from X-ray and synchrotron agree well and the obtained values were around the yield strength of the material. Furthermore, synchrotron mapping disclosed gradients along the width and length of the sample for the longitudinal and transverse stress components. On the other hand, lower residual stresses were found in the bulk of the material measured using neutron diffraction. The longitudinal component was tensile and decreased towards the boundary of the sample. In contrast, the normal component was nearly constant and compressive in nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers. Further investigations are planned to study the phenomenon in detail.