The reduction of the chromate contents in cements affects the electrochemical reactions of galvanized reinforcing steels in fresh concrete. By means of electrochemical measurements and bar pull-out tests the effect of chromates on the formation of protective coatings at the zinc and the bond behaviour have been investigated using chromate-containing and chromate-reduced cements. The results have shown that the bond zone was affected as a result of chromate reduction for cement types CEM I and CEM II. The disturbance to the bond zone should be considered as long-term in relation to the pore structure which is formed. The effects on the bond are largely compensated for as the concrete ages. The results of the related bond strength with displacement paths of 0.1 and 0.5?mm, respectively, are still within the range of expected figures for non-galvanized reinforcing steel despite the structural disturbance. Under practical aspects it is not necessary that the existing structural disturbance with respect to bond strength is taken into consideration.
Bei der Brücke Altstädter Bahnhof handelte es sich um eine große Spannbetonkonstruktion, die einen elementaren Verkehrsknotenpunkt in der Stadt Brandenburg an der Havel bildete. Entgegen üblichen Spannbetonkonstruktionen mit kleinen Bündelspanngliedern kamen beim Haupttragwerk in Längsrichtung großformatige Spannblockspannglieder zum Einsatz. Im Fall der vorliegenden Brücke setzte sich das Spannglied aus 392 ovalen Einzeldrähten aus Hennigsdorfer Produktion zusammen, welche als spannungsrisskorrosionsgefährdet gelten. Bei Bauwerkserkundungen wurde ein hoher Versprödungsgrad der Spannstähle festgestellt, sodass die Brücke am 19.05.2021 gesprengt werden musste. Zuvor traten im Bereich detektierter Spanndrahtbrüche von außen erkennbare Längsrisse in den Stegen anstatt von üblicherweise quer gerichteten Biegerissen an der gezogenen Randfaser auf. Die abweichende Schadensäußerung im Falle einer Spannstahlschädigung brachte das Bundesministerium für Digitales und Verkehr (BMDV) dazu, weitergehende Untersuchungen durchzuführen. In Zusammenarbeit mit dem Landesbetrieb Straßenwesen Brandenburg, der Hochschule für Technik und Wirtschaft Dresden sowie der Bundesanstalt für Materialforschung und prüfung (BAM) wurden experimentelle Untersuchungen insitu konzipiert und durchgeführt. Im Konkreten wurde an zwei Messstellen eine gezielte Schädigung des großformatigen Spannglieds vorgenommen, um das zuvor vorgefundene Schadensbild nachzuvoll ziehen und validieren zu können. Konzept, Ergebnisse aus den Untersuchungen und Erkenntnisse für gleichartig ausgeführte Bauwerke sind Gegenstand des ersten Beitrags (Teil 1). Der zweite Teil [1] wird sich im Schwerpunkt den verwendeten Messverfahren und Monitoringsystemen widmen, welche die Durchführung des Versuchs begleiteten.
Die B 1-Brücke am Altstädter Bahnhof war der wichtigste Verkehrsknotenpunkt in Brandenburg an der Havel. Im Dezember 2019 wurden die überführte Bundesstraße und die Straßenbahnlinie für den Verkehr gesperrt. Grund für die Sperrung war eine einsetzende Rissbildung in den Längsträgerstegen in Verbindung mit Hohlstellen, die letztlich auf gerissene Spanndrähte zurückgeführt werden. Um eine Sperrung der hoch frequentierten unterführten Verkehrswege zu verhindern, wurde ein umfangreiches Überwachungskonzept erforderlich. Wesentlicher Bestandteil dieses Konzepts war ein auf der Schallemissionsanalyse basierendes Monitoringsystem, mit dessen Hilfe Spanndrahtbrüche aufgezeichnet und lokalisiert werden konnten. Auf Grundlage der so gewonnenen Ergebnisse konnten Schwerpunkte für die Bauwerksprüfung abgeleitet werden. In diesem Bericht werden die gewonnenen Erkenntnisse zum messtechnisch erfassten Schadensfortschritt und den damit verbundenen visuell festgestellten Schäden beschrieben. Dabei werden die Besonderheit des verbauten konzentrierten Spannglieds (Spannblockverfahren nach TGL 173-33) und des Spannstahls in Bezug auf die Schadensbilder dargestellt. Die gewonnenen Erkenntnisse sollten bei der Beurteilung anderer Bauwerke mit vergleichbarer Bauart berücksichtigt werden.
The critical chloride content C(crit) is an indicator for the corrosion resistance of reinforcing steels in concrete. In this article, several experimental methods for determining the critical chloride content C(crit) of mild and an alloyed (12% Cr) steel in cementitious materials are compared. The methods used include accelerated polarization tests and tests using more natural (unpolarized) conditions in which chloride ingress occurs by diffusion and capillary uptake. The advantages and disadvantages of the methods are discussed, in particular, with the objective of reaching a compromise between applicability to practice and feasibility in laboratory testing.
Although zinc and zinc coatings have been widely used for corrosion protection for decades new zinc coatings are constantly being developed. Characterizing the corrosion protectiveness of these new coatings, however, should not be underestimated. While exposure tests are time intensive, cyclic tests can only be used for a very limited field of application. Thus, electrochemical measurements provide both an efficient and an effective alternative. Conventional aqueous bulk electrolytes influence the surface layers of a tested zinc coating and are therefore not reliable. Gel electrolytes, however, have evolved over the last few years, are minimally invasive and provide reliable results.
This work describes experiments with gel electrolytes made of agar. Unlike previous work, it proposes a composition of gel electrolyte for minimally invasive description of the protective power of naturally formed oxide layers on zinc and zinc coatings. Therefore, as a first part, the gel electrolyte made of agar is verified as a method for zinc and zinc-coated samples. Afterwards, this paper introduces the corrosion product layer resistance RL as a promising parameter to evaluate the protective power of zinc coatings. Results are verified with EIS and FTIR measurements. An example on a representative zinc coating demonstrates the practical application.
Investigation of chloride-induced pitting corrosion of steel in concrete with innovative methods
(2016)
The combination of electrochemical and 3D computed tomography (CT) investigations offers the possibility of verifying electrochemical measurements non-destructively. Determining the steel surfaces damaged by pitting corrosion allows developing specimens having damage pattern corresponding to practice. Corrosion phenomena like decoupled pitting corrosion cannot be verified by electrochemical measurements only, but with the combination of those two kinds of investigations it is possible. Another advantage is the minimization of the number of samples. The classical experimental procedure requires the destruction of samples after each damage step.This can be avoided by the use of 3D computed tomography. As long as the corrosion phenomena are completely within the examination zone shown by the 3D computed tomography, the electrochemical measurements can be calculated on an area basis to get the specific corrosion rate or polarization resistance.
Steel in concrete is protected by the alkaline pore water environment and the resulting formation of a protective passive layer against corrosion. Adverse environmental conditions due to carbonation or chloride ingress can destroy the passive layer on the steel surface. Corrosion processes starting in those areas lead to uniform corrosion or local corrosion like pitting corrosion. In comparison to uniform corrosion pitting corrosion is a form of increased local corrosion and thus leads to a progressive reduction in cross-section of the reinforcing steel. The corrosion products are first absorbed by the pores of the concrete matrix, without causing visible external changes at the concrete surface.
Carbon‐based conductive coatings are complex composites, consisting of an organic or inorganic binder and conductive carbon components, for application as anodes in impressed current cathodic protection systems of reinforced concrete structures. The electrochemical properties of three coatings at different humidity and in saturated calcium hydroxide solution were studied by electrochemical methods, such as electrochemical impedance measurement, measuring of open circuit potential over time and galvanostatic polarization. The dissolved organic and inorganic carbons in electrolyte solution were quantified by using a photometric method. The structures of the coatings were investigated before and after the electrochemical tests by microscopy and scanning electron microscope/EDX analysis. The results of the electrochemical impedance measurements show that the tested coatings all have a relatively low resistance, which is between 100 and 200V. The binder and the surface porosity influence the degradation behavior of those coatings. Especially the organic binder reacts with the strong alkaline medium under dissolving of organic carbon.
Die Potentialfeldmessung ist ein Standardverfahren zur Zustandserfassung von Stahlbetonbauwerken. Sie dient der zerstörungsfreien Detektion von aktiv korrodierenden Bereichen. Die Aussagegenauigkeit der Potentialfeldmessung ist von großer wirtschaftlicher Bedeutung, da deren Messergebnisse eine wichtige Entscheidungsgrundlage für die Erarbeitung von Instandsetzungsmaßnahmen bilden. Zur Ermittlung der Aussagegenauigkeit der Potentialfeldmessung wird ein numerisches Verfahren vorgestellt. Die wichtigsten Einflussgrößen auf die Potentialfeldmessung wie Anodengröße, Elektrolytwiderstand und Messraster wurden im Hinblick auf die Aussagegenauigkeit ausgewertet.
Korrosions- und Verbundverhalten verzinkter Betonstähle in Betonen mit chromatreduzierten Zementen
(2011)
Durch die Absenkung des Chromatgehalts der Zemente verändern sich die elektrochemischen Reaktionen von verzinkten Betonstählen in der Frischbetonphase. Mit Hilfe von elektrochemischen Messungen sowie Stabauszugsversuchen wurde an chromathaltigen und chromatreduzierten Zementen die Auswirkung des Chromats auf die Deckschichtbildung am Zink und auf das Verbundverhalten untersucht.
Mit den Ergebnissen konnte eine Beeinträchtigung der Verbundzone als Folge der Chromatreduzierung für die Zementarten CEM I und CEM II nachgewiesen werden. Die Störung der Verbundzone ist in Bezug auf die sich ausbildende Porenstruktur als dauerhaft anzusehen. Die Auswirkungen auf das Verbundverhalten werden mit zunehmendem Betonalter weitgehend kompensiert. Die Ergebnisse der bezogenen Verbundspannung bei Verschiebewegen von 0,1 mm und 0,5 mm liegen trotz der Gefügestörung noch im Bereich der Erwartungswerte für den unverzinkten Betonstahl. Unter baupraktischen Gesichtspunkten muss die auftretende Gefügestörung hinsichtlich der Verbundspannung daher keine Berücksichtigung finden.