Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (46)
- Vortrag (33)
- Posterpräsentation (17)
- Beitrag zu einem Tagungsband (6)
- Beitrag zu einem Sammelband (1)
- Forschungsbericht (1)
Schlagworte
- Interface (12)
- Verbundwerkstoffe (9)
- Thermoplaste (8)
- Mechanical properties (7)
- Kristallisation (5)
- Adhesion (4)
- Adhäsion (4)
- Epoxy (4)
- Haftung (4)
- Interphase (4)
- Reibung (4)
- Carbon fibres (3)
- Elastic properties (3)
- Interfacial shear strength (3)
- Interfacial strength (3)
- Ionic liquid (3)
- Kristallisationskinetik (3)
- Modellrechnung (3)
- Nanotubes (3)
- Polymer (3)
- Verstärkungsfaser (3)
- A. Carbon fibres (2)
- Avrami (2)
- B. Interfacial strength (2)
- Biegeschwingung (2)
- Cellulose (2)
- Composites (2)
- Ermüdung (2)
- Erstarrung (2)
- Faser (2)
- Fractography (2)
- Functional composites (2)
- Glasfaser (2)
- Glass fibre (2)
- Ionic conductivity (2)
- Morphology (2)
- Multifunctional supercapacitor (2)
- Pull-out (2)
- Push-out Test (2)
- Push-out test (2)
- Recycling (2)
- Simulation (2)
- Sphärolithe (2)
- Structural electrolyte (2)
- Thermoplast (2)
- A. Carbon nanotubes (1)
- A. Coupling agents (1)
- A. Hybrid composites (1)
- A. Polymer-matrix composites (PMCs) (1)
- AFM/SFM (1)
- Acoustic emission (1)
- Adhesion promotion (1)
- Alumina (1)
- B. Adhesion (1)
- B. Debonding (1)
- B. Interface (1)
- Bacteria (1)
- Bicontinuous morphology (1)
- Biopolymer (1)
- Carbon Fibers (1)
- Carbon Fibre (1)
- Carbon fibers (1)
- Carbon fiberepoxy resin laminates (1)
- Carbon fibre (1)
- Carbon fibres nanotubes interface (1)
- Carbon nanotubes (1)
- Cellulose natural fibers (1)
- Characterisation (1)
- Coating (1)
- Composires (1)
- Composite (1)
- Composite material (1)
- Composite materials (1)
- Composite recycling (1)
- Contact angle (1)
- Cooling rate (1)
- Copper (1)
- Copper (Cu) (1)
- Creep (1)
- Critical energy release rate (1)
- Cryogenic (1)
- DSI (1)
- Debonding (1)
- Dentine (1)
- Desorption (1)
- Dielektrische Analyse (1)
- Dynamic (1)
- EDX/EDS (1)
- Electric conductivity (1)
- Electrolyte (1)
- Electrospray ionization (ESI) (1)
- Elektrische Eigenschaften (1)
- Enamel (1)
- Energy release rate (1)
- Epoxy Resin (1)
- Epoxy based network (1)
- Epoxy resin (1)
- Failure (1)
- Failure process (1)
- Fatigue (1)
- Fatigue behavior (1)
- Festigkeit (1)
- Fiber (1)
- Fiber Bragg grating (1)
- Fiber properties (1)
- Fiber-matrix interface (1)
- Fiber/matrix bond (1)
- Fibre reinforced plastic (1)
- Fibre-matrix adhesion (1)
- Fibre/matrix bond (1)
- Fibre/matrix bonding (1)
- Finite element analysis (1)
- Fluorination (1)
- Fracture mechanics (1)
- GFRP (1)
- Gefüllte Kunststoffe (1)
- Geometrical factors (1)
- Glass Fibres (1)
- Glass fibres (1)
- Glass transition (1)
- Grafting (1)
- Hierarchical Structures (1)
- Hierarchical composites (1)
- Hydrogel (1)
- Hydrothermal Ageging (1)
- Indentation (1)
- Indentation hardness (1)
- Interdiffusion (1)
- Interface Strength (1)
- Interfacial Strength (1)
- Irradiation (1)
- Keywords: Poly(ether ether ketone) (1)
- Kurzfaser (1)
- Lamellen (1)
- Layer topography (1)
- Light curing (1)
- Lightweighting (1)
- Längenabhängigkeit (1)
- Mapping (1)
- Matrix (1)
- Matrix residual stress (1)
- Mechanical testing (1)
- Messmethode (1)
- Modellrechnungen (1)
- Modulus (1)
- Multifunctional epoxy (1)
- Multifunctional epoxy resin (1)
- Nachkristallisation (1)
- Nano indentation (1)
- Nano tubes (1)
- Nanoindentation (1)
- Natural (1)
- PA6.6 (1)
- PPA (1)
- Patch (1)
- Photocleavable organosilanes (1)
- Photocleavage (1)
- Photopolymer composites (1)
- Phytolith (1)
- Plasma nanocoatings (1)
- Polymer Matrix Composite (1)
- Polymer composite (1)
- Polymer electrolyte (1)
- Polymer matrix composites (1)
- Polymer-matrix composites (PMC) (1)
- Polymer-metal (1)
- Polyvinylpyrrolidone (PVP) (1)
- Pull-out composite materials (1)
- Pull-out test (1)
- Pull-out tests (1)
- Pulsed laser treatment (1)
- Push-in (1)
- Scherfestigkeit (1)
- Schubfestigkeit (1)
- Self-healing (1)
- Short-beam strength (1)
- Silica fibres (1)
- Single carbon fibers (1)
- Single fiber pull-out test (1)
- Single fibre pull-out test (1)
- Stiffness (1)
- Strain gauge factor (1)
- Strength (1)
- Supercapacitor (1)
- Surface (1)
- Surface area (1)
- Surface modification (1)
- Synthesis (1)
- Temperature sensitivity (1)
- Test method (1)
- Thermal cycling (1)
- Thermoplastic matrix (1)
- Thermoplastic prepreg (1)
- Thermosetting resin (1)
- Thin polymer layers (1)
- Tooth wear (1)
- Transkristallisation (1)
- Unidirectional composites (1)
- Validation (1)
- Verlustfaktor (1)
- Viscoelastic (1)
- Water Diffusion (1)
- Wetting (1)
- Work of adhesion (1)
- Zirconia (1)
- multi scale testing (1)
- o-Nitrobenzyl ester (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (33)
Epoxy R-Glass Fiber-Reinforced Polymer (GFRP) composite plates were hydrothermally aged at 60 ◦C for 23, 75, and 133 days. The water content reached 0.97 wt%, 1.45 wt% and 1.63 wt%, respectively. The studied GFRP matrix was inert to hydrolysis or chain scission, allowing for investigation of irreversible changes in the fiber-matrix interphase due to hydrothermal aging upon re-drying. During each period, a subset of the specimens was removed from the water bath and dried in a chamber. The weight loss upon drying was explained with epoxy leaching (impurities), sizing-rich interphase hydrolysis, glass fiber surface hydrolysis, accumulated degradation products escaping, and water changing state from bound to free. The influence of hydrothermal aging on the fiber-matrix interfacial properties was investigated. Lower interfacial strength of hydrothermally aged (wet)
samples was attributed to plasticization of the epoxy, plasticization and degradation of the sizing-rich interphase (including formation of hydrolytic flaws), and hydrolytic degradation of the glass fiber surface. The kinetics of epoxy-compatible epoxysilane W2020 sizing-rich interphase hydrolysis provided an estimate of ca. 1.49%, 4.80%, and 8.49% of the total composite interphase degraded after 23, 75, and 133 days, respectively. At these conditions, the interface lost 39%, 48%, and 51% of its strength. Upon re-drying the specimens, a significant part of the interfacial strength was regained. Furthermore, an upward trend was observed, being 13%, 10% and 3% strength, respectively; thus, indicating a possibility of partial recovery of properties.
Manufacturing and deformation behavior of alumina and zirconia helical springs at room temperature
(2023)
Ceramic helical springs with identical dimensions were produced by hard machining from alumina, alumina toughened zirconia (ATZ), and tetragonal zirconia polycrystals (TZP) stabilized with different oxides. According to the results of the spring constant determination under deformation rates of 3 mm/min, the deformation behavior of all ceramic springs obeys to Hook’s law. However, variation of the deformation rate, tests under constant load, and spring recovery behavior revealed differences in the deformation behavior of alumina, TZP, and ATZ springs. Alumina springs exhibited time-independent deformation in all tests. In contrast, anelastic deformation at room temperature was demonstrated in all springs containing TZP. This deformation is completely reversible over a period of several days. Anelastic behavior is particularly pronounced in Y-TZP springs, whereas Ce-TZP springs exhibit comparatively very low but still reliably detectable anelasticity. Oxygen vacancies in the TZP ceramic are considered the most likely explanation for the anelastic behavior of TZP springs at room temperature.
Lightweighting as a cross-cutting technology contributes significantly to achieve the European Green Deal goals. Based on, but not limited to, advanced materials and production technologies, the demand for natural resources and CO2 emmissions are reduced by lightweighting during production, as well as use phase. Therefore, lightweighting is a crucial transformation technology assisting in decoupling economic growth from resource consumption. In this manner, lightweighting contributes significantly as a key technology of relevance for many industrial sectors such as energy, mobility, and infrastructure, towards resource efficiency, climate action and economic strength, as well as a resilient Europe. To strengthen international partnerships, addressing global issues of today at the edge of science with high performance lightweight material based on carbon fibers, an overview about the BAM expertise in carbon fiber reinforced materials is given.
With this presentation, the push-out technique is explained. The focus of the experimental work is on the characterization of the fiber-matrix interface of short fiber reinforced composites. The reinforcing component was glass fibers and the matrix polymer was PA6.6 and PPA.
It is demonstrated for the first time that the push-out technique ca be applied on injection molded short fiber PMC and is sensitive to the mechanical interface properties. Further studies are planned on the influence of multiple processing, the temperature and humidity.