The strength of composite reinforcement fibres is normally measured on samples of much greater length than the actual residual fibre lengths found in many composite materials. This is due to a number of limitations of the standard techniques which are employed. We present a description of a technique which enables values for the tensile strength of composite reinforcement fibres at short gauge lengths to be obtained. The technique is based on an adaptation of a micro-mechanical test apparatus for fibre pullout measurements. Data is presented which was obtained at gauge lengths of 180380 µm on E-glass and S-2 glass® fibres taken from different chopped reinforcement products. The technique can be used at gauge lengths as short as 20 µm. The data indicates that the values of average fibre strength in these products are significantly below the pristine glass strength values.
An advanced equipment for single-fibre pull-out test designed to monitor the fracture process
(1995)
A mathematical model for the description of the overall crystallization of polymers has been developed which separates the pure geometric spreading of the semicrystalline superstructures from the increasing crystallinity inside these entities. The model uses the Avrami theory for the geometric part and a freely optional function for the increasing local crystallinity. The two functions are combined by a mathematical procedure called convolution. The free option of the local crystallinity function enables this model to permit calculation of this function, which is not accessible to direct measurement. Thus with given Avrami parameters and measured values of the time-dependent overall crystallinity, this function of the local crystallinity (secondary crystallization function) can be calculated. The model has been applied to test data produced by computer simulations.
Bestimmung der Haftfestigkeit in Verbundwerkstoffen mittels Indentations- und Durchdrückexperimenten
(2004)
Bestimmung zeitabhängiger lokaler Eigenschaften von Polymeren mit der Nano-Indentationstechnik
(2009)
Lightweighting as a cross-cutting technology contributes significantly to achieve the European Green Deal goals. Based on, but not limited to, advanced materials and production technologies, the demand for natural resources and CO2 emmissions are reduced by lightweighting during production, as well as use phase. Therefore, lightweighting is a crucial transformation technology assisting in decoupling economic growth from resource consumption. In this manner, lightweighting contributes significantly as a key technology of relevance for many industrial sectors such as energy, mobility, and infrastructure, towards resource efficiency, climate action and economic strength, as well as a resilient Europe. To strengthen international partnerships, addressing global issues of today at the edge of science with high performance lightweight material based on carbon fibers, an overview about the BAM expertise in carbon fiber reinforced materials is given.
The quality of interfacial interaction is dictated by the surface chemistry of the carbon fibres and the composition of the matrix. The composition of poly(vinylidene fluoride) (PVDF) was modified by the addition of maleic anhydride grafted PVDF. The surface properties of the various matrix formulations were characterised by contact angle and electrokinetic measurements. Carbon fibres were modified by industrial electrochemical oxidation and oxidation in nitric acid, or the use of a traditional epoxy-sizing of industrially oxidised fibres. The surface composition, morphology and wetting behaviour of the carbon fibres was characterised. The interaction between modified PVDF and the carbon fibres was studied by direct contact angle measurements between PVDF melt on single carbon fibres and by single fibre pull-out tests. The best wetting and adhesion behaviour was achieved between PVDF containing 5 ppm grafted maleic anhydride (MAH) and epoxy-sized carbon fibres. The addition of MAH-grafted PVDF to the unmodified PVDF caused the apparent interfacial shear strength to increase by 184%. The apparent interfacial shear strength of this fibrematrix combination allowed for the utilisation of 100% of the yield tensile strength of PVDF.