The strength of composite reinforcement fibres is normally measured on samples of much greater length than the actual residual fibre lengths found in many composite materials. This is due to a number of limitations of the standard techniques which are employed. We present a description of a technique which enables values for the tensile strength of composite reinforcement fibres at short gauge lengths to be obtained. The technique is based on an adaptation of a micro-mechanical test apparatus for fibre pullout measurements. Data is presented which was obtained at gauge lengths of 180380 µm on E-glass and S-2 glass® fibres taken from different chopped reinforcement products. The technique can be used at gauge lengths as short as 20 µm. The data indicates that the values of average fibre strength in these products are significantly below the pristine glass strength values.
A mathematical model for the description of the overall crystallization of polymers has been developed which separates the pure geometric spreading of the semicrystalline superstructures from the increasing crystallinity inside these entities. The model uses the Avrami theory for the geometric part and a freely optional function for the increasing local crystallinity. The two functions are combined by a mathematical procedure called convolution. The free option of the local crystallinity function enables this model to permit calculation of this function, which is not accessible to direct measurement. Thus with given Avrami parameters and measured values of the time-dependent overall crystallinity, this function of the local crystallinity (secondary crystallization function) can be calculated. The model has been applied to test data produced by computer simulations.
The quality of interfacial interaction is dictated by the surface chemistry of the carbon fibres and the composition of the matrix. The composition of poly(vinylidene fluoride) (PVDF) was modified by the addition of maleic anhydride grafted PVDF. The surface properties of the various matrix formulations were characterised by contact angle and electrokinetic measurements. Carbon fibres were modified by industrial electrochemical oxidation and oxidation in nitric acid, or the use of a traditional epoxy-sizing of industrially oxidised fibres. The surface composition, morphology and wetting behaviour of the carbon fibres was characterised. The interaction between modified PVDF and the carbon fibres was studied by direct contact angle measurements between PVDF melt on single carbon fibres and by single fibre pull-out tests. The best wetting and adhesion behaviour was achieved between PVDF containing 5 ppm grafted maleic anhydride (MAH) and epoxy-sized carbon fibres. The addition of MAH-grafted PVDF to the unmodified PVDF caused the apparent interfacial shear strength to increase by 184%. The apparent interfacial shear strength of this fibrematrix combination allowed for the utilisation of 100% of the yield tensile strength of PVDF.
Poly (ether ether ketone) (PEEK) has a high continuous service temperature, excellent mechanical properties, and good solvent and abrasion resistance, which can be further improved through the addition of carbon nanotubes (CNTs). CNT-PEEK nanocomposites are promising matrices for continuous carbon fibre composites; powder processing can mitigate the high melt viscosities in these systems. In this study, model single fibre (hierarchical) composites were produced by embedding sized and desized carbon fibres in nanocomposite CNTPEEK powders followed by single fibre pull-out tests to assess interfacial characteristics. Carbon fibre-PEEK interfacial shear strength is typically 40–45 MPa. Increasing CNT loadings increased fibre-matrix interfacial shear strength linearly up to ~70 MPa at 5.0 wt%, which was attributed to the CNT-based mechanical modification of the PEEK matrix. Apparent interfacial shear strength was inversely correlated with the embedded fibre length irrespective of carbon fibre sizing or CNT loading, indicating brittle fracture of the fibre-matrix interface.
Pulled out carbon fibres were still coated with the matrix, which indicated strong adhesion at the interface in all samples, likely related to a transcrystalline region. Adhesion was, however, negatively affected by the presence of epoxy sizings. Frictional shear strength was independent of embedded fibre length and CNT content for all samples.
Carbon nanotube-grafted carbon fiber polymer composites: Damage characterization on the micro scale
(2017)
Multiwall carbon nanotubes (CNTs) e carbon fibers (CFs)hybrid materials were produced by directly growing CNTs on CFs by means of chemical vapor deposition. For the latter, the oxidative dehydrogenation reaction of C2H2 and CO2 was applied, which allows growing CNTs without damaging the CF surface. Uni-directional nano-engineered carbon fiber reinforced composites (nFRCs) were fabricated by impregnating these hybrid materials with epoxy. The nFRCs subjected to single fiber push-out tests revealed a decrease of the interfacial shear strength (IFSS) of about 36% compared to the carbon fiber composites without CNTs. By means of transverse three-point bending tests performed on pre-notched composite beams inside a scanning electron microscope, the fracturing behavior parallel to the fibers was studied in-situ. The nFRCs showed significantly reduced fiber/matrix debonding while CNTs pull-out, CNTs bridging as well as matrix failure occurred. These results demonstrate that the presence of CNTs in nFRCs affects the stress distribution and consequently the damage Initiation as well as the damage propagation. The presence of CNTs suppresses the stress concentration at the fiber/Matrix interface and reduces the debonding of CFs from the matrix. However, our results indicate that the stress concentration shifts towards the CNTs' ends/matrix interface and causes promoted matrix failure leading to lower IFSS.
Biopolymers are very efficient for significant applications ranging from tissue engineering, biological devices to water purification. There is a tremendous potential value of cellulose because of ist being the most abundant biopolymer on earth, swellability, and functional groups to be modified. A novel, highly efficient route for the fabrication of mechanically stable and natural hydrogels is described in which cellulose and glycine are dissolved in an alkaline solution of NaOH and neutralized in an acidic solution. The dissolving temperature and the glycine amount are essential parameters for the self-assembly of cellulose chains and for Tuning the morphology and the aggregate structures of the resulting hydrogels. Glycine plays the role of a physical crosslinker based on the Information obtained from FTIR and Raman spectra. Among the prepared set of hydrogels, CL5Gly30 hydrogels have the highest capacity to absorb water. The prepared CL5Gly30 gels can absorb up to seven times their dry weight due to its porous 3-D network structure. CL5Gly10 hydrogel exhibits 80% deformation under 21 N force executed. The method developed in this article can contribute to the application of heavy metal adsorption in aqueous solutions for water purification and waste management.
Characterisation of the fibre/matrix interface in reinforced polymers by the push-in technique
(1997)
The push-in test is the only micromechanical test method that is not restricted to artificial fibre/matrix arrangements, but allows the in situ characterisation of interfaces in composites fabricated and stressed under realistic conditions. However, with the application of this method to reinforced polymers some problems arise both in the mathematical model for evaluating test data and in the practical performance of the test. Because in some cases the deformation of the relatively compliant polymeric matrices cannot be neglected, an extension of the existing model is required. For this purpose, the elastic energy of the material around the debonded part of the fibre is estimated and included in the energy-balance analysis. Because of the small diameter of the fibres usually used for reinforcing polymers, a test apparatus was designed which ensures a high positioning accuracy in the xy plane as well as in the z direction. In order to minimise thermal and mechanical influences, the microscope for fibre selection and the force sensor/indenter are directly connected together and the apparatus is designed to be stiff in all components. A solid-state bending joint guarantees very precise control of the axial movement. Three examples of the application of this easy-to-handle and low-cost test apparatus are presented briefly in the paper: assess fibre/matrix combinations, measures to improve the interfacial adhesion and the influence of water on the interface.
Circumventing boundary effects while characterizing epoxy/copper interphases using nanoindentation
(2017)
Characterization of the size and mechanical properties of interphases is essential when designing multicomponent materials. When nanoindentation is used to investigate the size and mechanical properties of an interphase, a common challenge is that the indenter or the stress zone formed around it are often restricted by the reinforcement, making it difficult to distinguish the mechanical property variations caused by the interphase itself from those caused by the boundary effect. In this work, a testing system was developed that allows determining the indent affected zone and accounting for it in the interphase measurements of an epoxy/Cu system. Using finite element analysis, we confirmed the validity of the proposed system. Nanoindentation was used to investigate the Interphase between copper and two different epoxy systems; amine-cured and anhydride-cured. Nanoindentation results showed that a copper layer that is only 10 nm thick still exhibits a constriction effect on the indentations in its vicinity. The amine-cured epoxy did not show any sign of interphase existence using the introduced method. However,
a soft interphase with a thickness of ~1.7 μm was measured on theanhydride-cured epoxy. Furthermore, we show that the proposed system can be used to determine the interphase thickness as well as its relative mechanical properties regardless of the indentation depth.
This system can be further used for investigating other polymer/metal interphases to better understand the factors influencing them, thus helping engineer the interphase size and properties to enhance composite performance.
Thin coatings of poly(acrylic acid) (PAA) and poly(hydroxyethylmethacrylate) (PHEMA) were deposited onto carbon fibers by means of the electrospray ionization (ESI) technique in ambient air. These high-molecular weight polymer layers were used as adhesion promoters in carbon fiberepoxy resin composites. Within the ESI process, the carbon fibers were completely enwrapped with polymer in the upper 10 plies of a carbon fiber roving. As identified with scanning electron microscopy also shadowed fibers in a bundle as well as backsides of fiber rovings were pinhole-free coated with polymers (electrophoretic effect'). Under the conditions used, the layers have a granular structure. Residual solvent was absent in the deposit. PAA and PHEMA films did not show any changes in composition and structure in comparison with the original polymers as analyzed by X-ray photo-electron spectroscopy and matrix-assisted laser desorption/ionization time-of-flight mass spectrometry. Single-fiber pullout tests of coated fibers embedded in epoxy resin showed significantly increased interfacial shear strength. It is assumed that chemical bonds between carbon fiber poly(acrylic acid) and epoxy resin contribute significantly to the improved interactions.
Structural electrolytes were prepared using a fully formulated commercially available high performance epoxy resin (MTM57) and an ionic liquid based electrolyte: lithium bis(trifluoromethylsulfonyl)imide (LiTFSI) dissolved in 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (EMIM-TFSI). Through a systematic study, the composition of the formulations was found to have a greater effect than the curing temperature on the morphology and properties of the resulting structural electrolytes. The presence of lithium salt is essential to form a structurally homogeneous electrolyte. Bicontinuous morphologies containing continuous (coarse) epoxy networks surrounded by connected spherical epoxy nodules were obtained with different length scales upon varying the lithium salt concentration. Increasing the LiTFSI concentration improved the miscibility of MTM57 with the electrolyte and decreased the characteristic length scale of the resulting bicontinuous microstructure. The properties of the structural electrolytes correlated with the morphology, showing increased Youngs modulus and decreased ionic conductivity with increasing lithium salt concentration. The miscibility of the epoxy system with the electrolyte was also improved by substitution of EMIM-TFSI with an equal weight of an aprotic organic solvent, propylene carbonate (PC); however, the window of PC concentrations which resulted in structural electrolytes with bicontinuous microstructures was very narrow; at PC concentrations above 1 wt %, gel-like polymers with no permanent mesoporosity were obtained.