Windings in superconducting magnets operating at 4.2 K are highly susceptible to quenching caused by small frictional heat inputs. Small movements in the magnet system are inevitable during ramping due to the increasing electromagnetic forces. Friction pairs of polymer based materials have been investigated at 4.2 K to gain an understanding of their sliding behavior in conditions representative of superconducting MRI systems. The results indicate that polymer-polymer pairs experience unstable sliding behavior with repeated stick-slip whereas polymer-aluminum couples have stable sliding behavior up to high contact pressures of 20 MPa.
Mittels lasergesteuerter gepulster Vakuumbogentechnologie (Laser-Arc) wurde eine reihe von reinen MoS2-Schichten sowie Kombinationsschichten aus MoS2 und tetraedrischem amorphen Kohlenstoff (ta-C) hergestellt. Mit diesen Schichtvarianten erfolgten tribologische Tests im Vakuum sowie in Atmosphäre. Dabei wurden im Hochvakuum reibungskoeffizienten bis zu 0,005 gemessen. Durch die Verwendung einer ta-C unterschicht konnte eine Lebensdauer von über 5×105 Lastzyklen erreicht werden. Zudem erwies sich diese unterschicht als vorteilhaft für das tribologische Verhalten der MoS2/ta-C Schichten unter atmosphärischen Bedingungen. -------------------------------------------------------------------------------------------------------------------------------------------
A series of MoS2 and combined MoS2/ta-C coatings were prepared by lasercontrolled arc evaporation (Laser-Arc) in order to study the tribological coating behaviour under vacuum and atmospheric conditions. Very low friction coefficients down to 0.005 were measured under high vacuum. By using a ta-C underlayer beneath the MoS2 a increased lifetime up to 5×105 load cycles could be obtained. Also under atmospheric conditions the underlayer had a beneficial effect on coating performance.