This paper presents investigations on the tribological behaviour of PTFE composites against steel at cryogenic temperatures. The results showed that the friction coefficient decreases with temperature down to 77 K, but did not follow a linear evolution further down to extreme low temperatures. It can be stated that the cryogenic environment has a significant influence on the tribological performance of the polymer composites. The effect of low temperatures was more clearly detected at low sliding speed, where friction heat is reduced. A change in wear mechanism from adhesive to abrasive was observed in this case. SEM and AFM analyses showed that the PTFE matrix composites investigated under these experimental conditions have transferred material onto the disc down to very low temperatures. Chemical analyses indicate the presence of iron fluorides.
Windings in superconducting magnets operating at 4.2 K are highly susceptible to quenching caused by small frictional heat inputs. Small movements in the magnet system are inevitable during ramping due to the increasing electromagnetic forces. Friction pairs of polymer based materials have been investigated at 4.2 K to gain an understanding of their sliding behavior in conditions representative of superconducting MRI systems. The results indicate that polymer-polymer pairs experience unstable sliding behavior with repeated stick-slip whereas polymer-aluminum couples have stable sliding behavior up to high contact pressures of 20 MPa.
Outstanding features favour the application of polymers and polymer composites in low-temperature technology. The booming hydrogen technology is a challenge for these materials, which are considered as seals and bearings in cryogenic pumps. In the present study, three types of thermoplastics, i.e., polyetheretherketone (PEEK), polyetherimide (PEI) and polyamide 6,6 (PA6,6), and one epoxy were considered as matrix materials. Micron-sized fillers, i.e., short carbon fibres, graphite flakes, and PTFE powders, were incorporated into these polymers together with nano-sized TiO2 particles. Optimised compositions of each matrix were selected from our previous works at room temperature in order to be studied at very low temperature conditions. In particular, frictional tests were carried out with polymer composite pins against polished steel surfaces under constant load over a certain distance in liquid hydrogen and liquid nitrogen. Afterwards, worn surfaces were analysed by using scanning electron microscopy (SEM). It was found out that the tribological properties in liquid hydrogen are dominated by the matrix materials, in particular thermoplastics perform generally slightly better than thermosetting resins.
Influence of the Temperature on the Tribological Behaviour of PEEK Composites in Vacuum Environment
(2008)
This paper describes tribological experiments carried out with polyetheretherketone (PEEK), filled with carbon fibres and solid lubricants (polytetrafluoroethylene (PTFE), graphite or MoS2), against steel discs. Oscillating sliding tests were performed in high vacuum environment in the temperature range between -40°C and +160°C. Results indicate that MoS2 filled PEEK show the best tribological performance in vacuum. Particularly, in the lower temperature range and at higher loads the friction behaviour is improved by the MoS2 content.
This study deals with the development of PEEK (polyehteretherketone) and PTFE (polytetrafluoroethylene) based composites, optimized for low friction and low wear performance under extreme environments. It is demonstrated that the incorporation of a harder polymer component into PTFE (such as PEEK particles), a short fiber reinforcement (e.g. carbon fibers CF), and internal lubricants (e.g. PTFE particles), helps to reduce the friction and to improve the wear resistance over a very wide temperature range.
Costs reduction is one of the major objectives in mechanical applications with a parallel increase of the power output. Another driver represents new environmental standards and their increasing restrictions in the automotive industry leading to the question, if materials based concepts may substitute harmful EP/AW additives in lubricants. This paper presents the slip-rolling resistance of different DLC/THC coatings on steel substrates with a definite slip rate of 10%. Industrial DLC coatings of ta-C and a-C:H types from various manufacturers were deposited on steels SAE 52100 and AMS 5898 to compile the slip-rolling resistance under initial average Hertzian contact pressures between 1.5 GPa and 2 GPa. The tests were carried out on Amsler-type twin disc tribometer under the regime of mixed/boundary lubrication in unadditivated paraffinic oil (ISO VG 46) and a factory fill engine oil. The spherical steel sample was uncoated and the cylindrical coated with DLC. Some coatings achieved 10 million cycles without any damage under a maximal Hertzian contact pressure Pmax well over 2.25 GPa, thus exceeding FZG 12.
The light-weight approach and fuel economy targets in today's automotive engineering require tribosystems, which can withstand higher contact pressures associated with low coefficients of friction. The application of high-performance coatings represents one approach among others. This paper presents some recently developed DLC coatings (a-C:H and ta-C) as well as a novel coating-substrate system (Zr(C,N)) in a benchmark test procedure under slip-rolling conditions in the presence of liquid lubricants. Various coatings with different thickness, interlayer and substrates were evaluated for their slip-rolling resistance in different lubricants at ambient temperature and at 120 °C. Results indicate that some of these coating systems can withstand at least 10 million cycles under initial Hertzian contact pressures of up to Pmax = 3.500 MPa and oil temperatures of at least 120 °C associated with low coefficients of friction under mixed/boundary conditions. Surface of the coatings and the counter bodies were analysed and compared with untreated substrates.
The tribological behaviour of MoS2/ta-C double layer coatings deposited by Laser-Arc technology was investigated in vacuum and air. In vacuum environment, the friction coefficient against steel balls varies between 0.005 and 0.02 depending on the contact pressure. At high contact pressures, the friction coefficient is as low as 0.005 and the life time between 340,000 and 500,000 cycles. Furthermore, it is shown that a ta-C base layer improves the performance of MoS2 coating.
Surface analyses were performed before and after the tribological tests by means of SEM, EDX, XRD, and TEM. They show that in the top layer beneath the sliding surface crystallization of the initially quasi-amorphous MoS2 took place. TEM images also verified an orientation of the basal MoS2-lattice planes parallel to the surface.
The focus of this study is to evaluate the influence of hydrogen on the friction and wear behavior of a wide range of polymer materials. Thereby, the tribological performance of filled und unfilled polymers from different suppliers were compared at room temperature in air and hydrogen gas (H2) as well as in liquid hydrogen at -235°C (LH2).