Filtern
Erscheinungsjahr
- 2015 (5) (entfernen)
Dokumenttyp
Referierte Publikation
- ja (5)
Schlagworte
- Tribofilm (4)
- Nanocomposite (3)
- Ball milling (1)
- Coefficient of friction (1)
- Cross-sectional TEM (1)
- Mechanically mixed layer (1)
- Movable cellular automata (1)
- Nanoparticles (1)
- Pin-on-disc test (1)
- Polymer-matrix composite (1)
- Raman spectroscopy (1)
- Silicone oil residue (1)
- Sliding simulation (1)
- Sliding wear (1)
- Stressstrain behavior (1)
- Surface topography (1)
- TEM (1)
- Tribo-sintering (1)
- Tribology (1)
The composition and nanostructure of a beneficial tribofilm formed during sliding of a hybrid nanocomposite against steel were characterized comprehensively. A similar nanostructure was produced by high energy ball milling of the three identified tribofilm constituents: silica, hematite and graphite. By supplying powders to a pin-on-disc test it has been shown that neither silica, nor hematite, nor a mixture of both provide the low coefficient of friction (COF) observed for the hybrid composite. Only if graphite was blended with the oxides, the low COF was obtained. Thus, a film of finely dispersed stable inorganic wear products containing 15 vol% graphite provides low friction and wear in the considered case.
We applied a combination of Raman spectroscopy (RS) and cross-sectional transmission electron microscopy (X-TEM) to identify silicone oil residues and tribofilms at steel disc surfaces after tribological testing. Neither chemical cleaning nor mechanical removal of a 50 µm thick surface layer produced a surface without any silicone residue. Nevertheless, long-term tribological properties are not affected due to silicone degradation which has been proved by Raman spectroscopy. Excellent anti-wear and anti-friction properties of a nanocomposite at severe stressing conditions correlated with the formation of a silica-based tribofilm containing amorphous and graphite-like carbon nanoparticles. Since reliable carbon quantification by analytical TEM is difficult, RS is a useful complementary method for carbon identification at wear scars.
The effect of steel counterface topography on the formation mechanisms of nanostructured tribofilms of polyetheretherketone (PEEK) hybrid nanocomposites was studied. Three types of surface finishes with mean roughness Ra ranging from nano- to micro-scale were investigated. Tribo-sintering of nanopartides, oxidation of counterface steel and compaction of wear debris are identified to be competing factors dominating the formation and function of the tribofilms. Counterface topography played an important role on the competing factors, and thereby influenced significantly the final structure, the load-carrying capability and the lubrication performance of the tribofilms. It was disclosed that a thin tribofilm, which mainly consists of silica nanoparticles and which forms on the counterface with a submicron roughness, benefits best the tribological performance of the composites
A model based on movable cellular automata (MCA) is described and applied for simulating the stress–strain and sliding behavior of a nanocomposite consisting of an epoxy matrix and 6 vol.% of homogeneously distributed silica nanoparticles. Tensile tests were used for verification of the model. It was realized that a slight modification of epoxy properties due to the addition of silica nanoparticles had to be taken into account in order to obtain good correlation between experimental and modeling results. On the other hand, sliding simulations revealed no susceptibility of results to slight modifications of matrix properties, but a significant impact of nanoparticles on the interface structure and smoothness of sliding mechanism. Furthermore, assuming both possibilities, bond breaking and rebinding of automata pairs, can explain different friction levels of polymer materials.
Formation and function mechanisms of nanostructured tribofilms of epoxy-based hybrid nanocomposites
(2015)
The nanostructures and properties of the tribofilms of epoxy (EP) composites filled with short carbon fibers (SCF) and different volume fractions of monodisperse silica nanoparticles were investigated. When the conventional composite filled only with SCF was considered under a high pv condition, an iron oxide layer is formed on the steel counterface. The addition of even only 0.05 vol% nano-silica leads to a significant change of the tribofilm's structure and the tribological behavior of the composite. With increasing silica content, the oxidation layer on the steel surface is gradually replaced by a silica-based tribofilm. A close relationship between the tribofilms structure and the tribological behavior of the composites was identified. Mixing, possible reactions and tribo-sintering of silica nanoparticles with other wear products are deemed to be main mechanisms inducing the formation and the lubricity of the silica-based tribofilm.