The tribological performance of short glass fibers (SGF),solid lubricants and silica nanoparticles filled epoxy (EP) composites was investigated under oil lubrication conditions. It is demonstrated that the addition of SGF greatly reduces the friction and wear of EP. However, further addition of solid lubricants and silica nanoparticles does not change obviously the friction and wear. It is identified that the high tribological performance of SGF reinforced EP is related to the high load carrying capacity and abrasion resistance of SGF. The nanostructure of the tribofilm was comprehensively characterized. It is deemed that the tribofilm plays an important role in the tribological performance by avoiding the direct rubbing of the sliding pairs exposed to boundary and mixed lubrication conditions.
The composition and nanostructure of a beneficial tribofilm formed during sliding of a hybrid nanocomposite against steel were characterized comprehensively. A similar nanostructure was produced by high energy ball milling of the three identified tribofilm constituents: silica, hematite and graphite. By supplying powders to a pin-on-disc test it has been shown that neither silica, nor hematite, nor a mixture of both provide the low coefficient of friction (COF) observed for the hybrid composite. Only if graphite was blended with the oxides, the low COF was obtained. Thus, a film of finely dispersed stable inorganic wear products containing 15 vol% graphite provides low friction and wear in the considered case.
A model based on movable cellular automata (MCA) is described and applied for simulating the stress–strain and sliding behavior of a nanocomposite consisting of an epoxy matrix and 6 vol.% of homogeneously distributed silica nanoparticles. Tensile tests were used for verification of the model. It was realized that a slight modification of epoxy properties due to the addition of silica nanoparticles had to be taken into account in order to obtain good correlation between experimental and modeling results. On the other hand, sliding simulations revealed no susceptibility of results to slight modifications of matrix properties, but a significant impact of nanoparticles on the interface structure and smoothness of sliding mechanism. Furthermore, assuming both possibilities, bond breaking and rebinding of automata pairs, can explain different friction levels of polymer materials.
We applied a combination of Raman spectroscopy (RS) and cross-sectional transmission electron microscopy (X-TEM) to identify silicone oil residues and tribofilms at steel disc surfaces after tribological testing. Neither chemical cleaning nor mechanical removal of a 50 µm thick surface layer produced a surface without any silicone residue. Nevertheless, long-term tribological properties are not affected due to silicone degradation which has been proved by Raman spectroscopy. Excellent anti-wear and anti-friction properties of a nanocomposite at severe stressing conditions correlated with the formation of a silica-based tribofilm containing amorphous and graphite-like carbon nanoparticles. Since reliable carbon quantification by analytical TEM is difficult, RS is a useful complementary method for carbon identification at wear scars.
The method of movable cellular automata (MCA) was applied to simulate the stress-strain behavior of a nano composite consisting of an epoxy matrix and 6 vol. % silica nano particles. The size of the elements used for modelling was fixed at 10 nm, corresponding approximately to the diameter of the filler particles. Since not only the stress-strain response of the two constituents but also debonding of neighboring particles and granular flow was taken into account, plastic deformation as well as crack initiation and propagation could be simulated with the model. Modelling results were compared with tensile test results of both, pure epoxy as well as the epoxy-6 vol. % SiO2 composite. Since assuming bulk properties of the two constituents did not yield satisfactory results, slight modifications of the nanoparticle response functions and nanostructures were tested numerically. Finally, it was observed that only the assumption of slightly increased strength properties of the epoxy yielded good correlation between experimental and modelling results. This was attributed to an increased cross linking of the epoxy caused by the presence of silica nano particles.
Excellent tribological properties of an advanced polymer matrix composite were obtained by a combination of micro- and nano-sized fillers. Surface features and the nanostructure of tribofilms were characterized by advanced microscopic techniques, and correlated with the macroscopic behavior in terms of wear rate and friction evolution. A model based on movable cellular automata was applied for obtaining a better understanding of the sliding behavior of the nanostructured tribofilms. The failure of the conventional composite without silica nanoparticles could be attributed to severe oxidational wear after degradation of an initially formed polymer transfer film. The hybrid composite preserves its antiwear and antifriction properties because flash temperatures at micron-sized carbon fibers, lead to polymer degradation and subsequent release of nanoparticles. It has been shown that the released particles are mixed with other wear products and form stable films at the disc surface thus preventing further severe oxidational wear. Furthermore, the released wear product also is embedding carbon fibers at the composite surface thus preventing fiber fragmentation and subsequent third body abrasion. With nanoscale modelling we were able to show that low friction and wear can be expected if the nanostructured silica films contain at least 10 vol.% of a soft ingredient.
The topographic effect of steel counterface, finished by mechanical grinding with Ra ranging from 0.01 to 0.95 µm, on the structure and functionality of the tribofilm of a hybrid nanocomposite, i.e. epoxy matrix filled with monodisperse silica nanoparticles, carbon fibers and graphite, was systematically investigated. The nanostructure of the tribofilm was comprehensively characterized by using combined focused ion beam and transmission electron microscope analyses. It was identified that oxidation of the steel surface, release, compaction and tribosintering of silica nanoparticles and deposition of an epoxy-like degradation product as well as fragmentation of carbon fibers are main mechanisms determining the structure and functionality of the tribofilm. The size of roughness grooves determines the type and size class of wear particles to be trapped at the surface. An optimum groove size leading to a maximum of surface coverage with a nanostructured tribofilm formed mainly from released silica nanoparticles was identified.
Exploring the influence of counterpart materials on tribological behaviors of epoxy composites
(2016)
The dependence of the friction and wear of epoxy (EP) composites materials on counterpart materials, such as standard bearing steel, medium carbon steel and chrome-plating (Cr), was investigated. The conventional composite filled with short carbon fiber (SCF) and graphite shows the highest tribological performance when rubbing against Cr, whereas, the hybrid nanocomposite (EP filled with SCF, graphite and silica nanoparticles) exhibits the lowest friction and wear when sliding against the standard bearing steel. The role of nanoparticles in the tribological performance is distinctly different when sliding against with various counterpart materials. It is demonstrated that counterpart materials exert an important influence on material transfer, tribo-oxidation and mechanical mixing of wear products, resulting in the different formation mechanisms of transfer film.
The effect of steel counterface topography on the formation mechanisms of nanostructured tribofilms of polyetheretherketone (PEEK) hybrid nanocomposites was studied. Three types of surface finishes with mean roughness Ra ranging from nano- to micro-scale were investigated. Tribo-sintering of nanopartides, oxidation of counterface steel and compaction of wear debris are identified to be competing factors dominating the formation and function of the tribofilms. Counterface topography played an important role on the competing factors, and thereby influenced significantly the final structure, the load-carrying capability and the lubrication performance of the tribofilms. It was disclosed that a thin tribofilm, which mainly consists of silica nanoparticles and which forms on the counterface with a submicron roughness, benefits best the tribological performance of the composites
Formation and function mechanisms of nanostructured tribofilms of epoxy-based hybrid nanocomposites
(2015)
The nanostructures and properties of the tribofilms of epoxy (EP) composites filled with short carbon fibers (SCF) and different volume fractions of monodisperse silica nanoparticles were investigated. When the conventional composite filled only with SCF was considered under a high pv condition, an iron oxide layer is formed on the steel counterface. The addition of even only 0.05 vol% nano-silica leads to a significant change of the tribofilm's structure and the tribological behavior of the composite. With increasing silica content, the oxidation layer on the steel surface is gradually replaced by a silica-based tribofilm. A close relationship between the tribofilms structure and the tribological behavior of the composites was identified. Mixing, possible reactions and tribo-sintering of silica nanoparticles with other wear products are deemed to be main mechanisms inducing the formation and the lubricity of the silica-based tribofilm.