Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (20)
- Vortrag (6)
- Forschungsbericht (5)
- Zeitschriftenartikel (3)
Sprache
- Englisch (34) (entfernen)
Referierte Publikation
- nein (34) (entfernen)
Schlagworte
- Acoustic emission analysis (4)
- Cracks (4)
- Durability (4)
- Crack formation (3)
- Grout (3)
- Nano-silica (3)
- Shrinkage (3)
- Tensile strength (3)
- accident prevention (3)
- building industry (3)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (14)
- 7.4 Baustofftechnologie (14)
- 7.2 Ingenieurbau (8)
- 8 Zerstörungsfreie Prüfung (3)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (3)
- 7.1 Baustoffe (2)
- 2 Prozess- und Anlagensicherheit (1)
- 2.4 Prüfung und Bewertung von Explosivstoffen/Pyrotechnik (1)
- 2.5 Konformitätsbewertung Explosivstoffe/Pyrotechnik (1)
- 8.6 Faseroptische Sensorik (1)
Eingeladener Vortrag
- nein (6)
The interaction mechanism of ultrasonic waves with surface-breaking cracks in reinforced concrete has been studied. For this, a detailed numerical analysis of the medium was first conducted using the spectral finite element method. Subsequently, measurements were conducted on a reinforced beam sample before and after mechanical-load-induced cracking. It was concluded that for the considered configuration, waves passing through the cracks dominated the tip-diffracted ones. In addition, substantial changes in the travel time and amplitude of the signals were observed when cracks were present.
Alkali-activated slag materials are known for their high Chloride penetration resistance. This makes them potentially applicable as repair systems for damaged steel-reinforced concrete structures, which are exposed to chloride attack. For this purpose, the influence of the activator composition, i.e. the SiO2 and Na2O concentration of the alkaline solution on a) the compressive strength, b) shrinkage and mass change and c) the resistance against chloride penetration of four alkali-activated slag mortars (AASM) were studied. An ordinary Portland cement-based mortar was used as the reference sample. Increasing SiO2 and Na2O concentrations increased the strength, shrinkage and mass loss of the AASMs. The resistance of the mortars against chloride penetration was evaluated using the non-steady-state migration coefficient Dnssm obtained from NT BUILD 492. The results indicate that the Dnssm is related to differences in the pore solution of the AASMs rather than to differences in their microstructure. An upcoming study of the authors is going to evaluate this hypothesis by the accelerated chloride penetration (diffusion) test.
Grouting is a universal repair and strengthening technique, which is constantly used for structural remediation of concrete components, trenches, mine subsidence, dam joints, restoration of masonry structures, and geological stabilizations. Having an extremely small particle size of only few microns, ultrafine cements are ideal for grouting applications due to their superior permeability and compressive strength properties of the hardened cement paste compared to that of the less-expensive, but coarser ordinary Portland cements. Supplementary cementitious materials (SCMs) are often used to replace ultrafine cement in order to modify certain properties and to reduce costs. The aim of this experimental study is to investigate the effect of three supplementary materials: microsilica (MS), fly ash (FA), and metakaolin (MK) on the workability, and mechanical properties of an ultrafine cement based grout with a constant water-binder ratio and constant superplasticizer content. Maximum percentages of replacement with ultrafine cement were 6% by volume of cement for MS and 16% for FA, and MK. In general, results suggest that the workability is improved by addition of FA, whereas is reduced, when modified with MS and MK. The compressive strength of grout after cement replacement remains comparable to that of pure cement grout. However, there is a tendency of the MS to positively affect the compressive strength opposite to FA, whereas flexural strength is positively affected by FA. Based on the results, it is evident that grouts with Hägerman cone flow more than 500 mm and compressive strength of more than 90 MPa after 28 days can be produced.