Effects of amorphous nano-silica additions on mechanical and durability performance of SCC mixtures
(2012)
In the recent years the application of nanotechnology in building materials has increased
exponentially. One of the most referred and used nano-materials is amorphous silica with
particles size in the nano-range, even though its application and effect in concrete has not been
fully understood yet. It has been reported that nano-silica (nS) addition increases the
compressive strength and reduces the overall permeability of hardened concrete due to the
pozzolanic properties which are resulting in finer hydrated phases (C-S-H gel) and densified
microstructure (nano-filler and anti leaching effects). These effects enhance the durability of
concrete structures such as bridges, quays or off-shore oil facilities in marine environments.
In this study two different types of nano-silica were applied in self-compacting concrete (SCC),
both having similar particle size distributions (PSD) but produced in two different processes
(fumed powder silica and precipitated silica in colloidal suspension). The influence of nanosilica
on SCC was investigated with respect to the properties of concrete in the fresh state
(workability) and hardened state (mechanical properties and durability). Additionally, the
densification of microstructure of the hardened concrete was verified by SEM and EDS analyses.
The obtained results demonstrate that an efficient use of nano-silica in SCC can improve its
mechanical properties and durability. Considering the reactivity of the two nano-silica studied,
colloidal type shown more reactivity at early age, which influenced all the final SCC properties.
This paper presents experimental investigations and analyses on the early-age-behavior of zero-slump concrete, such as compaction behavior and green-strength. First, the influence of the granulometric properties of the fines is discussed in detail. For this purpose, the early-age behavior of two different fines (quartz flour and fly ash) is investigated by means of the intensive compaction test (IC-test). The tests on the influence of the fines focus on effects caused by differences in the particle shape and the use of a plasticizing admixture. The conducted tests on the compaction behavior of the fines and their corresponding green-strength are extended to continuously graded granular mixes. Here, the influence of optimized particle packing on the early-age behavior is presented and a comparison on the basis of the aforementioned quartz flour and fly ash is made. In this consideration, experimental investigations on the early-age behavior of a zero-slump concrete mix and possible effects on the hardened concrete properties are included.
This paper addresses the characterization of six different amorphous silica samples with respect to their application in cement paste. Different mixes are compared and analyzed using the mini spread-flow test. Also the granular properties, different void fraction states of packing and distribution moduli q are analyzed and compared using a mix design tool. A deformation coefficient is derived from the spread-flow test, which correlates with the value of specific surface area computed from the particle size distribution, and intrinsic density of the samples. Finally, the thickness of a constant water layer of 25 nm around the particles is computed at the onset of flowing. The granular analysis demonstrated that it is possible to decrease the water demand of the cement paste when nanoparticles are added and the resulting grading follows the modified Andreasen and Andersen curve (q = 0.5), and the concentration of nano silica is less than 5% bwoc.