Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (20)
- Vortrag (6)
- Forschungsbericht (5)
- Zeitschriftenartikel (3)
Sprache
- Englisch (34) (entfernen)
Referierte Publikation
- nein (34) (entfernen)
Schlagworte
- Acoustic emission analysis (4)
- Cracks (4)
- Durability (4)
- Crack formation (3)
- Grout (3)
- Nano-silica (3)
- Shrinkage (3)
- Tensile strength (3)
- accident prevention (3)
- building industry (3)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (14)
- 7.4 Baustofftechnologie (14)
- 7.2 Ingenieurbau (8)
- 8 Zerstörungsfreie Prüfung (3)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (3)
- 7.1 Baustoffe (2)
- 2 Prozess- und Anlagensicherheit (1)
- 2.4 Prüfung und Bewertung von Explosivstoffen/Pyrotechnik (1)
- 2.5 Konformitätsbewertung Explosivstoffe/Pyrotechnik (1)
- 8.6 Faseroptische Sensorik (1)
Eingeladener Vortrag
- nein (6)
Reinforced concrete buildings are frequently damaged by cracks, spalling and corroded
reinforcement bars. The present article focuses on the damage analysis of one of the first
buildings in Berlin that was constructed using reinforced lightweight concrete, which makes it
historically important. The compressive strength, carbonation depth, location and diameter of
reinforcement bars as well as moisture and salt profiles were determined. The carbonationinduced corrosion of the reinforcement bars represented the main damage of the building.
Certified repair mortars with lightweight aggregates (LWA) do not exist on the German
market. Therefore, an appropriate repair mortar was developed in accordance with DIN EN
1504 and the German guideline for the repair and protection of concrete structures (RL-SIB).
On the one hand, historic preservation requirements, such as: colour of the mortar,
possibilities of surface patterning, maximum preservation of the original substance and
reversibility of any Intervention must be met. On the other hand, technical requirements of the
relevant Standards must be achieved. The developed mix was designed to resist the identified
causes of deterioration. Thermal strains within the repair mortar and between the repair
mortar and the Substrate influence the crack formation and thus the durability. Therefore,
special attention was paid to the bonding and shrinking behaviour of the concrete repair
System. By using polymers, both hardened mortar properties and durability were influenced
positively.
It is important to protect critical buildings (shopping centres, government buildings and embassies), infrastructure and utilities, train and underground stations against being damaged, destroyed or disrupted by deliberate acts of terrorism, criminal activity and malicious behaviour. Normal regulations and building guidelines do not generally take into account these threats. The introduction of regulations or guidelines should support the resilience of the buildings and infrastructure against explosive incidents. In order to protect the infrastructure, methods are required to quantify the resistance of structural elements against explosive loading and to assess the hazards resulting from failure of an element. The applicable state-of-the-art techniques may be either experimental or numerical methods, or a combination of both. Therefore, the thematic group (TG) on the resistance of structures to explosion effects was formed in order to bring the required expertise together, make it commonly available and to find and define harmonised methods and solutions which can be provided to the decision-makers responsible for critical infrastructure protection. This first report of the TG gives a comprehensive summary of the existing methods which can be used to analyse and test the resistance of glazing and windows under blast-loading conditions. Within this context, the experimental methods of testing using high explosives and testing using blast simulators called shock tubes is presented and explained. In addition, the potential of numerical simulations is highlighted in terms of their applicability to the different glass materials. A short, comprehensive theoretical background is given for each method. Based on this, each method is described with its requirements, realisation and the related measurement techniques. Furthermore, an interpretation of the measurements is highlighted. For the numerical simulations, the basic discretisation and calculations schemes are presented in combination with the available constitutive material descriptions for the different significant materials. Finally the chances for verification and validation of the numerical results are presented. Hence the report builds the basis for an actual evaluation of the different test methods and their applicability to certain problems, and provides helpful information for critical infrastructure stakeholders, owners and operators considering the structural resistance of the infrastructure to the effects of explosion in a comprehensive document.
Introduction of a monitoring system for Bingham fluids in additive manufacturing with concrete
(2022)
Freeform additive manufacturing of concrete structures is a rising technology in civil engineering with several fascinating advantages. Nonetheless, to ensure reliability and structural integrity, standards and quality control are required in the future to bring this technology into the market. As the concrete is manufactured continuously, continuous quality control of the printing process is also required, i.e. comprehensive process monitoring. At BAM, a test rig will be installed, enabling the printing of concrete structures with a maximum size of 2 m x 1 m x 1 m (l x w x h). Here, process monitoring is the focus of the test rig. In this study, we show the results of the first pump tests, including the measurement of several parameters such as temperature and pressure along the supply system, i.e. from the concrete pump to the printer head.
Remediation of Cracks Formed in Grouted Connections of Offshore Energy Structures under Static Loads
(2018)
The future energy demand necessitates the exploration of all potential energy sources both onshore and offshore. Global trend has shifted towards offshore energy, which can be obtained from either carbon intensive or renewable options, hence requiring structures such as rigs, platforms, and monopiles. Most of these structures adopt easily installable construction techniques, where lower foundation need to be connected with the super structure by mean of grouted composite joints. Generally, these composite connections have exterior sleeve, interior pile and infill grout. Being located in remote offshore conditions, connections can experience considerable adverse loading during their lifetimes. Degradations were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites may often be proven difficult, which eventually leads to reduced capacity of connections in the long run. Thus, repair and rehabilitation of such connections should be planned ahead to minimize operational delays and costs in the future. This study aims at characterizing the nature of crack generation in grouted connections and thereby identifying the potential of repair using suitable repair material. Scaled grouted joints were manufactured using a novel mold, and connections were loaded under static load to visualize the main failure pattern. The failure mechanism and loading capacity are found compatible to previous results from earlier literature. Grouted connection was then repaired using cementitious injectable grout. The effectiveness of the repair system is also discussed.
Grouts have numerous applications in construction industry such as joint sealing, structural repair, and connections in precast elements. They are particularly favoured in rehabilitation of structures due to penetrability and convenience of application. Grouts for repair applications typically require high-performance properties such as rapid strength development and superior shrinkage characteristics. Sometimes industrial by-products referred as supplementary cementitious materials (SCM) are used with neat cement due to their capabilities to provide binding properties at delayed stage. Micro silica, fly ash and metakaolin are such SCMs, those can modify and improve properties of cement products. This study aims at investigating long-term mass loss and linear shrinkage along with long-term compressive and flexural strength for grouts produced from ultrafine cement and SCMs. A series of mixtures were formulated to observe the effect of SCMs on these grout properties. Properties were determined after 365 days of curing at 23oC and 55% relative humidity. The effect of SCMs on the properties are characterised by statistical models. Response surfaces were constructed to quantify these properties in relation to SCMs replacement. The results suggested that shrinkage was reduced by metakaolin, while micro silica and fly ash had positive effects on compressive and flexural strength, respectively.
Grouting is a universal repair and strengthening technique, which is constantly used for structural remediation of concrete components, trenches, mine subsidence, dam joints, restoration of masonry structures, and geological stabilizations. Having an extremely small particle size of only few microns, ultrafine cements are ideal for grouting applications due to their superior permeability and compressive strength properties of the hardened cement paste compared to that of the less-expensive, but coarser ordinary Portland cements. Supplementary cementitious materials (SCMs) are often used to replace ultrafine cement in order to modify certain properties and to reduce costs. The aim of this experimental study is to investigate the effect of three supplementary materials: microsilica (MS), fly ash (FA), and metakaolin (MK) on the workability, and mechanical properties of an ultrafine cement based grout with a constant water-binder ratio and constant superplasticizer content. Maximum percentages of replacement with ultrafine cement were 6% by volume of cement for MS and 16% for FA, and MK. In general, results suggest that the workability is improved by addition of FA, whereas is reduced, when modified with MS and MK. The compressive strength of grout after cement replacement remains comparable to that of pure cement grout. However, there is a tendency of the MS to positively affect the compressive strength opposite to FA, whereas flexural strength is positively affected by FA. Based on the results, it is evident that grouts with Hägerman cone flow more than 500 mm and compressive strength of more than 90 MPa after 28 days can be produced.
At present, Wind Turbine Generators (WTGs) operating in onshore and offshore wind farms are primary sources of renewable energy around the world. Cylindrical grouted sleeve connections are usually adopted in these WTG structures to connect the upper structure and foundation for ease of installation. These structures including grouted connections experience considerable adverse loading during their lifetimes. Settlements were reported inside similar connections used in energy structures especially oil and gas platforms, which were installed in last three decades. Thus, repair and rehabilitation of such connections in existing wind structures should also be planned ahead to keep them operating in the future. The nature of failure and crack generation in grouted connections are crucial prior to adopt a strengthening strategy. This pilot study is carried out to actualize the failure mechanism in the grouted connection, when subjected to axial loading. A novel reusable scaled cylindrical grouted connection with shear keys was designed and tested for its load bearing behaviour. The mechanical test was accompanied by classical measuring techniques (e.g. displacement transducer) as well as non-destructive measuring techniques (e.g. digital image correlation (DIC), acoustic emission analysis (AE)). The failure mechanism incorporating slippage of the shear keys and cracking of the grout was investigated. The capacity and applicability of such test mould were also discussed. The knowledge is expected to pave way towards repair of deteriorated grouted connections with similar geometry and failure pattern.
Additive manufacturing of concrete structures is a novel and emerging technology. Freecontouring in civil engineering, which allows for entirely new designs, is a significant advantage. Inthe future, lower construction costs are expected with increased construction speeds and decreasingrequired materials and workers. However, architects and civil engineers rely on a certain quality ofexecution to fulfil construction standards. Although several techniques and approaches demonstratethe advantages, quality control during printing is highly challenging and rarely applied. Due to thecontinuous mixing process commonly used in 3D concrete printing, it is impossible to exclude varia-tions in the dry mixture or water content, and a test sample cannot be taken as a representative samplefor the whole structure. Although mortar properties vary only locally, a defect in one layer duringprinting could affect the entire integrity of the whole structure . Therefore, real-time process monitor-ing is required to record and document the printing process.At the Bundesanstalt für Materialforschung und -prüfung (BAM) a new test rig for the additive man-ufacturing of concrete is built. The primary purpose is measuring and monitoring the properties of amortar during the printing process.The following study investigates an approach for calculating yield stress and plastic viscosity based onexperimentally recorded pressure data. The calculations assume that fresh mortar behaves as a Bing-ham fluid and that the Buckingham-Reiner-equation is applicable. A test setup consisting of rigid pipeswith integrated pressure sensors at different positions is utilized.Monitoring the printing process with different sensors is crucial for the quality control of an ongoingprocess.
Effects of amorphous nano-silica additions on mechanical and durability performance of SCC mixtures
(2012)
In the recent years the application of nanotechnology in building materials has increased
exponentially. One of the most referred and used nano-materials is amorphous silica with
particles size in the nano-range, even though its application and effect in concrete has not been
fully understood yet. It has been reported that nano-silica (nS) addition increases the
compressive strength and reduces the overall permeability of hardened concrete due to the
pozzolanic properties which are resulting in finer hydrated phases (C-S-H gel) and densified
microstructure (nano-filler and anti leaching effects). These effects enhance the durability of
concrete structures such as bridges, quays or off-shore oil facilities in marine environments.
In this study two different types of nano-silica were applied in self-compacting concrete (SCC),
both having similar particle size distributions (PSD) but produced in two different processes
(fumed powder silica and precipitated silica in colloidal suspension). The influence of nanosilica
on SCC was investigated with respect to the properties of concrete in the fresh state
(workability) and hardened state (mechanical properties and durability). Additionally, the
densification of microstructure of the hardened concrete was verified by SEM and EDS analyses.
The obtained results demonstrate that an efficient use of nano-silica in SCC can improve its
mechanical properties and durability. Considering the reactivity of the two nano-silica studied,
colloidal type shown more reactivity at early age, which influenced all the final SCC properties.