Mixtures of hexamethyldisiloxane (HMDSO) and oxygen have been used for deposition of SiO2-like layers by plasma polymerization under low-pressure conditions onto polyethylene and polystyrene used as basecoat. Water glass was cast onto these 0.5 µm plasma thick siloxane-like layers with a thickness of 5 to 40 µm. The adhesion of these bilayer systems and their flame resistance were tested.
The effect of different plasma parameters such as monomer/gas ratio, pressure and power input into the discharge on the deposition rate and the composition of the formed layers was studied. Characterization and chemical composition of the formed films were performed using infrared, X-ray photoelectron and solid state nuclear magnetic resonance spectroscopy.
Peel strengths of composites were measured and the locus of peel front propagation was detected. Thermal properties of composites were analyzed by thermo-gravimetric analysis. Finally, the fire-retardant properties of thick coated polymers were determined by exposure to flames and the behavior of coatings on the polymers during flaming was observed visually.
We report on a new series of isoreticular frameworks based on zinc and 2-substituted imidazolate-4-amide-5-imidate (IFP-1–4, IFP=imidazolate framework Potsdam) that form one-dimensional, microporous hexagonal channels. Varying R in the 2-substitued linker (R=Me (IFP-1), Cl (IFP-2), Br (IFP-3), Et (IFP-4)) allowed the channel diameter (4.0–1.7 Å), the polarisability and functionality of the channel walls to be tuned. Frameworks IFP-2, IFP-3 and IFP-4 are isostructural to previously reported IFP-1. The structures of IFP-2 and IFP-3 were solved by X-ray crystallographic analyses. The structure of IFP-4 was determined by a combination of PXRD and structure modelling and was confirmed by IR spectroscopy and 1H MAS and 13C CP-MAS NMR spectroscopy. All IFPs showed high thermal stability (345–400°C); IFP-1 and IFP-4 were stable in boiling water for 7 d. A detailed porosity analysis was performed on the basis of adsorption measurements by using various gases. The potential of the materials to undergo specific interactions with CO2 was investigated by measuring the isosteric heats of adsorption. The capacity to adsorb CH4 (at 298 K), CO2 (at 298 K) and H2 (at 77 K) at high pressure were also investigated. In situ IR spectroscopy showed that CO2 is physisorbed on IFP-1–4 under dry conditions and that both CO2 and H2O are physisorbed on IFP-1 under moist conditions.
Synthesis and characterisation of highly fluorescent core-shell nanoparticles based on Alexa dyes
(2012)
Current and future developments in the
emerging field of nanobiotechnology are closely
linked to the rational design of novel fluorescent
nanomaterials, e.g. for biosensing and imaging applications.
Here, the synthesis of bright near infrared
(NIR)-emissive nanoparticles based on the grafting
of silica nanoparticles (SNPs) with 3-aminopropyl
triethoxysilane (APTES) followed by covalent attachment
of Alexa dyes and their subsequent shielding by an
additional silica shell are presented. These nanoparticles
were investigated by dynamic light scattering (DLS),
transmission electron microscopy (TEM) and fluorescence
spectroscopy. TEM studies revealed the monodispersity
of the initially prepared and fluorophorelabelled
silica particles and the subsequent formation of
raspberry-like structures after addition of a silica
precursor.Measurements of absolute fluorescence quantum
yields of these scattering particle suspensions with
an integrating sphere setup demonstrated the influence
of dye labelling density-dependent fluorophore aggregation
on the signaling behaviour of such nanoparticles.
Since more than 40 years ammonia plasma exposure of polyolefins is used for introduction of primary amino groups. The selectivity of this reaction and the yield in primary amino groups was found to be low. Here, a prominent side-reactions of this process was investigated, the hydrogenation by NH3 plasma. For identification of hydrogenation ammonia (NH3) and deuterated ammonia (ND3) were exposed to Polyethylene (h-PE) and fully deuterated polyethylene (d-PE) as well as hexatriacontane (h-HTC) and fully deuterated hexatriacontane (d-HTC) as low-molecular weight model for PE. HD exchange was assumed and detected by Time-of-Flight Secondary Ion Mass Spectrometry (ToFSIMS), X-ray Photoelectron Spectroscopy (XPS), Attenuated Total Reflectance (ATR-FTIR) and 1H and 2H Nuclear magnetic Resonance. Results show a significant HD exchange within the sampling depth of ATR (2.5 µm). However, N- and NH2 introduction was limited to the topmost surface as shown by SIMS and XPS (a few nanometers).
Bei der Betonage von Abdichtbauwerken können Temperaturen bis 110 °C und hohe Drücke bis 5 MPa erreicht werden. Mittels Technikumsversuchen wurde nachgewiesen, dass Mikroakustik- und Ultraschallsensoren zum Einbau in Demonstrationsbauwerke geeignet sind.
Die Untersuchungen wurden bei der BAM (Bundesanstalt für Materialforschung und -prüfung) in Berlin durchgeführt. Es ist vorgesehen, die Sensoren in Morsleben am Demonstrationsbauwerk im Anhydrit einzusetzen.