- Beton (6)
- Alkali-Kieselsäure-Reaktion (4)
- Polypropylene fibres (4)
- Schallemissionsanalyse (4)
- AKR (3)
- Acoustic emission (3)
- High performance concrete (3)
- ASR (2)
- Degradation (2)
- Ermüdung (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (4)
- 7.1 Baustoffe (4)
Eingeladener Vortrag
- nein (2)
The susceptibility of different aggregate types used in concrete to ASR is strongly associated with their petrography. The aim of this study is to assess the influence of the aggregate size on the ASR potential, in particular applied to the sand fractions in the size range of 0.125-4 mm. The investigation concept is based on the hypothesis that at a specific particle size reactive aggregates could change their characteristic influence in mitigating ASR instead of promoting it. For the study of the size dependent behaviour mortars are prepared, considering aggregates of different reactivity, including very reactive, slow-late and quasi non-reactive types. The analysis is based on a stepwise substitution concept, in which mortars with a constant overall grain size distribution are compared, while only one size fraction of the non-reactive base aggregate is substituted by a reactive aggregate type of this specific size fraction. For the expansion experiments an accelerated mortar bar test (80°C, immersed in NaOH solution) was applied. The results show that the slow-late reactive greywacke yielded a strong reduction of the expansion below an aggregate size in the range of 0.5-1 mm. On the other side with the very reactive borosilicate glass, the expansions increased steadily with decreasing size. To validate if the acquired expansions were caused by ASR, thin sections were analysed. Mainly, higher expansion values were consistent with extensively more amounts of ASR indicators.
ln den letzten Jahren sind im deutschen Bundesautobahnnetz verstärkt Schäden an Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Die damit einhergehende oft drastische Reduzierung der Nutzungsdauer der Betonfahrbahndecke führte zu einer starken Intensivierung der Forschung auf diesem Gebiet. Zentraler Forschungsgegenstand war bisher neben der Suche nach geeigneten präventiven betontechnologischen Maßnahmen vor allem die Entwicklung performanceorientierter Prüfverfahren zur AKR-Prävention. Dabei wurden insbesondere die klimatischen Einwirkungen auf die Betonfahrbahndecke und der externe Alkalieintrag zeitraffend simuliert. Die zusätzlich interagierenden mechanischen Einwirkungen aus dem Verkehr fanden bisher keine Berücksichtigung. Vor diesem Hintergrund verfolgt die 2011 eingerichtete und 2015 um weitere drei Jahre verlängerte DFG-Forschergruppe 1498 u. a. das Ziel, den Einfluss einer mechanisch induzierten Vorschädigung (Ermüdungsbeanspruchung) auf den AKR-Schädigungsprozess zu klären. Die hierfür erforderliche Beschreibung der vielfältigen interagierenden Schädigungs- und Transportprozesse erfordert eine enge Verknüpfung von Experimenten mit einer mehrskaligen Modellierung. Die experimentelle Basis bildet die mechanische Vorschädigung (Ermüdung) großformatiger Balken aus einem Fahrbahndeckenbeton mit einem erhöhten AKR-Schädigungspotenzial. Aus diesen Balken werden nach der Ermüdungsbeanspruchung kleinformatige Probekörper gewonnen, an denen die Auswirkungen der mechanischen Vorschädigung auf das Betongefüge und die interagierenden Transport- und Schädigungsprozesse analysiert werden. Das Teilprojekt der SAM hat in diesem Kontext die Aufgabe, ganzheitlich die Rissbildungsprozesse und den interagierenden Eintrag bzw. Auslaugung der Alkalien von der mechanisch induzierten Vorschädigung bis zum AKR-Schädigungsprozess in enger Abstimmung mit den Forschungspartnern zu untersuchen. Den Schwerpunkt dieses Beitrags bildet die Charakterisierung der Rissbildungsprozesse durch die mechanische Vorschädigung und ihrer Auswirkungen auf die interagierenden Transportprozesse. Das schließt die Vorstellung der hierfür angewandten innovative Prüftechniken und Prüfmethodologien ein.
In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces which can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced life expectancy of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology, the main research focus up to now has been the development of performance-oriented testing procedures for ASR prevention. This included more specifically the accelerated simulation of climatic effects and external alkali penetration on road surfaces. The effects of mechanical pre-damage resulting from cyclic traffic loading and climatic impact had previously not been taken into consideration. Since 2011, the five-partner research group 1498 sponsored by the German Research Foundation (DFG) has been pursuing research on how simultaneous cyclic loading and external alkali penetration impacts destructive ASR in road surface concretes. The depiction of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and their multi-scale modelling. This paper aims to focus on the aforementioned experiments by means of innovative testing techniques. The research is founded on a series of cyclic fatigue tests performed on large-format beams, both with and without previous application of a sodium chloride (NaCl) solution, with simultaneous tracking of crack development. Subsequently, smaller test specimens were extracted from the pre-damaged beams for further experiments. These included the spatial visualization and quantification of fatigue-induced cracks using micro X-ray 3D-computed tomography (3D-CT). Additionally, the effects of fatigue-induced cracks on alkali transport were investigated using Laser-Induced Breakdown Spectroscopy (LIBS). Subsequent storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced predamage on the ASR.
Die vorstehend dargestellten Untersuchungen lassen sich wie folgt zusammenfassen:
• Mit dem für die mechanische Vorschädigung entwickelten Versuchsstand und gewählten Prüfregime können die für die ermüdungsinduzierte Schadensevolution typische stabilisierende und stabile Phase in der auf Zug beanspruchten Betonrandzone gut abgebildet werden. So wurde dort zum Beispiel, ausgehend von dem hier gewählten praxisnahen Belastungsregime, mit Ultraschall in der Ruhephase durch das Trockenschwingen ein maximaler Abfall des relativen dynamischen E-Moduls von ca. 8 - 10 % ermittelt.
• Mit aufbauenden kapillaren Aufsaugversuchen wurde gezeigt, dass die erzeugte Betondegradation zu einer moderaten Erhöhung der Aufnahme des Prüfmediums führt.
• Zur Bewertung der Auswirkungen einer alleinigen Vorschädigung (Trockenschwingen) auf die schädigende AKR mittels Performance-Prüfung ist die Klimawechsellagerung aufgrund der einseitigen Tausalzbeaufschlagung am besten geeignet. Die hier ermittelten Dehnungsverläufe lassen auf einen moderaten Einfluss der mechanischen Vorschädigung auf die AKR schließen.
• Die zusätzlich im Kontext der Nasschwingversuche durchgeführten 60°C Betonversuche zeigen, dass die zyklische Beanspruchung vor und nach dem Aufbringen der Tausalzlösung die schädigende AKR gleichfalls moderat erhöht.
In derzeit laufenden ergänzenden Untersuchungen wird der separate Einfluss der ermüdungsinduzierten Rissbildung auf die schädigende AKR an homogen, stärker geschädigten Prüfkörpern mit einem hohen inneren AKR-Schädigungspotenzial im 60°C Betonversuch grundhaft analysiert. Zusätzlich wird gegenwärtig der Einfluss der degradierten Betonrandzone auf die Dehnungsverteilung an großformatigen Prüfkörpern
über die Höhe im 40°C Betonversuch vertiefend für die makroskopische Modellierung untersucht.