X-ray refraction is based on optical deflection of X-rays, similar to the well-known small angle X-ray scattering, but hundreds of times more intense, thus enabling shorter measurement time. We show that X-ray refraction techniques are suitable for the detection of pores, cracks, and in general defects. Indeed, the deflected X-ray intensity is directly proportional to the internal specific surface (i.e., surface per unit volume) of the objects. Although single defects cannot be imaged, the presence of populations of those defects can be detected even if the defects have sizes in the nanometer range.We present several applications of X-ray refraction techniques to composite materials:- To visualize macro and microcracks in Ti-SiC metal matrix composites (MMC);- To correlate fatigue damage (fibre de-bonding) of carbon fibre reinforced plastics (CFRP) to X-ray refraction intensity;- To quantify the impact damage by spatially resolved single fibre de-bonding fraction as a function of impact energy in CFRP laminates.An example of classic high-resolution computer tomography of an impact-damaged CFRP will also be presented, as a benchmark to the present state-of-the-art imaging capabilities. It will be shown that while (absorption) tomography can well visualize and quantify delamination, X-ray refraction techniques directly yield (spatially resolved) quantitative information about fibre de-bonding, inaccessible to absorption tomography.
Simple models describing the relationship between basic mechanical properties and the relative density of various types of porous metals (such as foams, sponges and lattice structures) are well established. Carefully evaluating these relationships experimentally is challenging, however, because of the stochastic structure of foams and the fact that it is difficult to systematically isolate density changes from variations in other factors, such as pore size and pore distribution. Here a new method for producing systematic sets of stochastic foams is employed based on electron beam melting (EBM) additive manufacturing (AM). To create idealised structures, structural blueprints were reverse-engineered by inverting X-ray computed tomographs of a randomly packed bed of glass beads. This three-dimensional structure was then modified by computer to create five foams of different relative density ρr, but otherwise consistent structure. Yield strength and Young’s modulus have been evaluated in compression tests and compared to existing models for foams. A power of 3 rather than a squared dependence of stiffness on relative density is found, which agrees with a recent model derived for replicated foams. A similar power of 3 relation was found for yield strength. Further analysis of the strength of nominally fully dense rods of different diameters built by EBM AM suggest that surface defects mean that the minimum size of features that can be created by EBM with similar strengths to machined samples is ∼1 mm.
Selective Electron Beam Melting (SEBM) is a promising powder bed Additive Manufacturing technique for near-net-shape manufacture of high-value titanium components. However without post-manufacture HIPing the fatigue life of SEBM parts is currently dominated by the presence of porosity. In this study, the size, volume fraction, and spatial distribution of the pores in model samples have been characterised in 3D, using X-ray Computed Tomography, and correlated to the process variables. The average volume fraction of the pores (b0.2%) was measured to be lower than that usually observed in competing processes, such as selective laser melting, but a strong relationship was found with the differentbeamstrategies used to contour ,and infill by hatching, a part section. The majority of pores were found to be small spherical gas pores, concentrated in the infill hatched region; this was attributed to the lower energy density and less focused beam used in the infill strategy allowing less opportunity for gas bubbles to escape the melt pool. Overall, increasing the energy density or focus of the beam was found to correlate strongly to a reduction in the level of gas porosity. Rarer irregular shaped pores were mostly located in the contour region and have been attributed to a lack of fusion between powder particles.