Due to the high sensitivity of coda waves to the smallest structural alterations such as strain, humidity or temperature changes, ultrasonic waves are a valid means to examine entire structures employing networks of ultrasonic transducers. In order to substantiate this ex ante assessment, the viability of measuring ultrasonic waves as a valid point of reference and inference for structural changes is to be further scrutinized in this work. In order to investigate the influence of mechanical strain on ultrasonic signals, a four-point bending test was carried out on a reinforced concrete beam at Ruhr University Bochum. Thus, measurements collected from a network of selected transducer pairings arranged across the central, shear-free segment of the test specimen, were correlated to their respective strain fields. Detected ultrasonic signals were evaluated employing Coda Wave Interferometry. Such analysis comprised the initial non-cracked state as well as later stages with incremental crack depth and quantity. It was to ascertain that the test specimen can in fact be qualitatively compartmentalized into areas of compression and tension identified via Relative Velocity Changes presented in Attribute Maps. However, since results did not entail a zero crossing, i.e., neither positive nor negative values were to be calculated, only relative changes in this work displayed staggered over the height of the object under test, are discussed. Under the given methodological premises, additional information is currently required to make quantitative assertions regarding this correlation of ultrasonic and strain results. This holds true for the comparability of the ultrasonic and strain results for both non-cracked and even the cracked state.
Imaging wood defects using air coupled ferroelectret ultrasonic transducers in reflection mode
(2020)
Air-coupled ultrasound (ACU) is used to detect defects in wood panels without physically contacting the sample and with a quick scanning rate. Transducers made of cellular polypropylene (PP) with a high signal-to-noise ratio are quite suitable for ACU testing of wood. The extremely low modulus of elasticity and low density of PP transducers results in a small difference in acoustic impedance for the Transmission of ultrasonic waves between the transducer and air, allowing new areas of application to become possible.
To demonstrate the suitability of the reflection technique, measurements are shown on the three samples Multiplex, LVL, and MDF and compared with transmission measurements. Due to this acoustic barrier and the use of cellular PP transducers, an exact detection of delamination and cavities is possible in wood panels up to 40 mm thick. If only one side of an object is accessible and the depth of the defect is of interest, the reflection technique is preferred at the expense of a reduced measuring accuracy and Penetration depth.
Recent years have seen extended use of ultrasonic techniques for concrete infrastructure assessement. They are applied for quality assurance and condition assessement at bridges, power plants, dams and other important objects. However, there are still a couple of significant limitations. They include, but are not limited to depth of penetration, imaging complex structures or early stage detections of distributed damage. The talk will give information on recent research in this area. Specifically, the application of the unique deep penetration system LAUS is shown. Ultrasonic monitoring using embedded transducers to check for subtle and sudden changes in the material is introduced as well. Comments on initiatives for validation, standardization and certification will be given.