Energy dispersive synchrotron diffraction for in-situ analyses of hydrogen behavior in steels
(2013)
The extent of hydrogen embrittlement phenomenon is dependent on the interaction of hydrogen with the material i.e. diffusion behavior, lattice distortions, phase transformations and residual stresses developments. For the better understanding of the hydrogen interaction with the metal, possibilities of performing in-situ observations of the mentioned factors has to be accomplished. The EDDI (Energy Dispersive Diffraction) beamline at the BESSY II facility in Berlin provides this possibility and was used in order to investigate the aspects of this phenomenon in in-situ scale.
The energy dispersive method entails a synchrotron X-ray white beam with a wide energy range (20–120 keV) which allows a fixed position of the sample and the detector, and combined with the high photons flux it allows a very short measurement time for obtaining a full scale X-Ray Diffraction patterns.
In this contribution, the successful usage of high energy X-rays, applied for the first time for hydrogen behavior observations, provided the ability for evaluating in-situ the hydrogen diffusion behavior and the hydrogen interaction with stresses fields in the material.
Steel samples were charged with hydrogen and examined by Synchrotron radiation.
Two different methods were used in this research; the first is diffusible hydrogen concentration evaluation extracted from the lattice distortions, i.e. changes of the lattice parameter. The second is calculation of the residual stresses present in the sample and the interaction of hydrogen with them, using the known sin2ψ method.
The present contribution highlights recent trends in investigating hydrogen diffusion and cracking in steel welds. For such studies, supermartensitic stainless steels (SMSS) have exemplarily been selected. These materials have been used for offshore and marine constructions for about two decades now. They present a versatility of improved properties such as high strength to thickness ratio, good weldability and good corrosion resistance. However, as shown by respective failure cases, SMSS welds might become prone to hydrogen assisted cracking and the degradation phenomena are more easily to investigate due to the nearly homogeneous martensitic microstructure than in other materials. Generally, it has to be distinguished between cracking that occurs during or shortly after fabrication welding, or during subsequent operation of SMSS components. In order to achieve crack avoidance during fabrication and service, conclusive test sequences have to be applied, ranging from field tests at real components and full scale tests investigating the materials behavior under real service conditions to basic and small scale tests, such as tensile and corrosion tests, oriented more towards a materials ranking. Considerable testing of SMSS welds has been carried out and the present paper particularly summarizes spotlights on 1:1 scale component testing of welded tubulars, slow strain rate testing and basic tests oriented to elucidate the hydrogen behavior and degradation in SMSS weld microstructures. Also, permeation tests, hydrogen dependent degradation of mechanical properties and thermal desorption spectroscopy are adressed. As a specific item, first results of lately conducted investigations for tracking hydrogen movement in such weld microstructures by using high energy synchrotron radiation are elucidated.