Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (34)
- Beitrag zu einem Tagungsband (11)
- Vortrag (5)
- Buchkapitel (2)
- Beitrag zu einem Sammelband (2)
- Sonstiges (1)
Sprache
- Englisch (55) (entfernen)
Schlagworte
- Wear (20)
- Friction (18)
- Tribology (13)
- Laser-induced periodic surface structures (LIPSS) (8)
- DLC (6)
- Roughness (6)
- Simulation (5)
- Slip-rolling (5)
- Femtosecond laser ablation (4)
- 100Cr6 (3)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (5)
In situ Acoustic Emission for wear life detection of DLC coatings during slip-rolling friction
(2006)
Different diamond-like carbon (DLC) coatings on a steel substrate (100Cr6) were tested under slip-rolling friction conditions against uncoated counter bodies of the same steel. The initial maximum Hertzian pressure was varied in a range of P0 = 1.52.3 GPa. The friction tests were carried out under dry conditions and with an unadditivated paraffin oil as lubricant. It could be shown that the thickness of the coatings affects the respective wear life. Further, a very important factor for the wear life of a coating under lubricated slip-rolling conditions is the roughness of the surface of the respective counterbody. The wear life tests were monitored by recording in situ the Acoustic Emission (AE) signals. Some causes for a high AE activity could be identified.
Adhesion measurements are presented which were carried out with an atomic force microscope between polymer balls attached to a cantilever and a silicon wafer under ultra high vacuum conditions. In using a silicon surface with a defined structure a correlation between adhesion force and contact area was found. This correlation could partly be explained by the Johnson-Kendall-Roberts model, if a change of the surface energy is assumed as a result of the structuring. For a constant geometric contact area an additional structuring leads to a decrease of the adhesion force.
A novel tribometer has been designed using commercially available components for sliding motion at 40kHz with amplitude between 2.5 and 5µm. The tribometer is equipped with means to measure amplitude, frequency, power required to keep the sample in motion and load applied. The effective motion between the two contacting bodies is monitored. These data are used to evaluate the coefficient of friction. The wear rate was determined after the tests. The set-up was tested using novel, non-commercial substrates such as AlFeCrTi-alloys and tungsten carbide-based coatings as well as Magnéli-type coatings (Tin-2Cr2O2n-1 and TinO2n-1). This paper presents the principle of the ultra-high frequency tribometer and first tribological quantities of materials and coatings tested.
Diamond like carbon (DLC)-coatings are applied very successfully on computer discs. Sliding friction tests confirm their high performance as dry lubricants with friction coefficients (COFs) below 0.1. In contrast to sliding tests, until very recently most of the DLC-coatings failed in slip-rolling test after fewer cycles than uncoated samples. However, present tests with DLC-coatings of seven different suppliers show a more promising tribological behaviour under slip-rolling conditions. The DLC-coatings were deposited onto steel 100Cr6, HRC 60, with a thickness of 23 ?m. The counter bodies were uncoated, grinded or polished 100Cr6 discs with 30 mm radius of curvature. The tests were performed on a twin disc testing rig (Amsler type) with paraffin oil under boundary/mixed lubrication and rolling with 10% slip. The initial, average Hertzian contact pressure was adjusted to Pm = 1.0, 1.25, and 1.5 GPa. The failure criterion was defined as the occurrence of a single damaged area larger than 1 mm2, which was controlled by optical microscopy (OM). An acoustic emission (AE) measurement system was installed as an additional online control for coating failure. The stressed coatings and the chipping areas were analyzed by OM, SEM, EDX, AFM and Raman spectroscopy.
Until now, the results reveal that a large scatter in lifetime of coatings occurs not only between samples of different coaters but also between the samples of one single batch. The highest lifetime reached by a DLC-coating under these testing conditions is 10 × 106 cycles. That is the highest life time for a coating tested under the testing conditions above in our laboratory so far. The following factors were identified to influence the life time of the coatings: coating thickness, interlayer type, topography of the coatings, counter body roughness and mechanical properties. But the most important factor determining the life time of the coatings is that the coating process does produce homogenous layers free of faults.