In Germany, for the transport and storage of spent nuclear fuel, casks with double closure lid systems are used, which are equipped with Helicoflex® metal seals. The original interim storage period for these casks was planned to be 40 years. However, recent political developments indicate that a storage time of more than 80 years might be necessary. Therefore, the current storage licenses have to be renewed in due course, which requires extended knowledge of the long-term behaviour of all cask components.
At the Bundesanstalt für Materialforschung und -prüfung (BAM), metal seals have been investigated after ageing at temperatures between room temperature and 150 °C for up to 7 years. At regular intervals the seals have been tested for leakage rate as well as for their mechanical behaviour. From these tests pronounced influence of ageing could be shown which results in the decrease of the seal force and the useable resilience. The main reason attributed to these performance changes is the increasing permanent deformation of the outer layer of the seal due to creep. So far, an explicit analytical description of the long-term behaviour that could be used for predictions exceeding the tested ageing times and temperatures was not suitable.
In addition to the component tests that were already conducted, a comprehensive investigation programme has been started to describe the mechanical behaviour of the individual seal components.
The individual seal components are tested regarding different material characteristics including creep, deformation and microstructural properties. The comparability of the material characterization is ensured by comparing the basic raw material of the specimen with the actual component material.
Furthermore, detailed investigations of the time and temperature dependent deformation behaviour are realized by ageing seal segments at multiple temperatures for different periods of time and employing standardized tests.
By analysing the acquired data in combination with the ongoing long-term component tests a dataset for analytical prediction of the long-term behaviour of the seals is intended for an extended period of time under a certain temperature regime.
Component and material investigations on metal seals for high level radioactive waste containers
(2018)
Long-term investigations performed at BAM look to extend the state of knowledge on safety-related components of interim storage containers. Metal seals act as the primary sealing barrier in the bolted double lid closure system of the containers. The behaviour of metal seals has been investigated for ageing times up to 8.5 years and for various temperatures. The main cause for reduction in useable resilience overtime was due to creep deformation of the outer jacket of the seal.
Component and material investigations on metal seals for high level radioactive waste containers
(2018)
In Germany casks for interim storage of spent nuclear fuel and high level radioactive waste are equipped with Helicoflex® metal seals as main sealing barrier of the double lid system. The long-term behaviour of those seals is investigated at Bundesanstalt für Materialforschung und –prüfung (BAM) in order to evaluate the safety function of the containment at different temperatures over storage periods of 40 years or more in case extended interim storage becomes necessary.
Long-term investigations have been done for ageing times of up to 8.5 years at temperatures ranging from room temperature to 150 °C. It was found that the seal force and useable resilience decrease over time, which is mainly caused by creep deformation of the aluminium (or silver) outer jacket of the seals. This effect becomes stronger with increasing temperature.
The ageing processes of the seal material and the overall seal behaviour is under investigation in order to derive analytical descriptions for the long-term seal performance. Thus, standardized tests on the basic seal materials, with focus on aluminium, and additional investigations on the seals as a component are conducted. The current investigations include compression and tension creep measurements as well as tensile testing. Furthermore, ageing of seal segments provides information on the development of the contact area width, jacket thickness and microstructural changes in dependence of time and temperature. The obtained data are used for the development of material models and an analytical approach to describe and predict the time and temperature dependent sealing behaviour in the long-term.
The aging management system for the mechanical components of nuclear power plants (NPPs) must be established and used by the licensee in such a way that the quality of safety relevant components is guaranteed for the completely designed lifetime of the NPP. This demands an extensive plant life management with special emphases on the knowledge of the degradation in material properties. The basic safety concept in Germany observes this circumstance. Lifetime extension of the German NPPs is an aim of the current valid coalition agreement of the German government. Operational extension of interim storage facilities requires, in comparison to the aging management system for NPP, an aging management system adapted to the Special circumstances of spent fuel storage casks. Extension of interim storage periods for spent fuel casks beyond the designed lifetime requires, in comparison to the components of an NPP, an increasing knowledge of material degradation with potential impact on cask integrity, e.g. leak tightness. Dry interim storage in Germany has been approved for 40 years. After that time, according to the present strategy, a final repository should be available. However, until now, such a final facility still does not exist, and the German exploration and licensing process is heavily delayed. Currently, discussions are continuing regarding further exploration of the Gorleben salt mine. There is willingness to overcome this situation that is clearly described in the available coalition agreement of the federal government. Anyway, however, the prediction is viewed; a repository for heat generating radioactive waste in Germany will not be available in the near future and may not be available when first storage facilities and casks reach their 40 years of approved lifetime, which will occur in ~25 years starting from now. Therefore, the question must be asked:
what has to be done with the existing storage casks in the interim facilities? May these casks be fit for continued use, with an extension of the storage period? One option is to have an aging management system, which creates enough information about the technical condition of safety relevant cask properties. This is the basis for safety evaluation for extended storage periods. In the present paper, possible aging mechanisms for high level waste storage casks are discussed, as well as the influence of the time dependent changes of the component properties.
In Germany spent nuclear fuel is stored and transported in casks that possess bolted lid systems equipped with double jacket metal seals of Helicoflex® type in order to enable safe enclosure of the radioactive inventory. A dry interim storage period of 40 years was planned and the casks are licensed for that time span. However, due to political reasons and delayed disposal projects this time span is expected to increase significantly. It is therefore necessary to evaluate the long-term sealing behavior of the casks exceeding 40 years of operating time. In this paper, we discuss our approach to investigate the aging behavior of such metal seals, and to predict the long-term sealing behavior.
Accelerated aging component tests with seals are performed at temperatures up to 150°C to investigate the course of seal force, useable resilience and leakage rate. Even though these tests have already shown a significant decrease in seal force and useable resilience after aging times of less than 1 year, for most seals the leakage rate stayed better than the specified value. However, observation of the leakage rate has to be continued to determine the aging effect on the seal properties. As a main influence on the seal long-term behavior the increasing permanent deformation of the outer jacket has been recognized. It is made of aluminum or silver which means that the temperatures that are relevant for the aforementioned application in casks lead to creep deformation.
For further investigation of seal behavior a comprehensive research program concerning the material characteristics and aging behavior of the individual seal components, with an emphasis on the outer jacket material, has been launched. The aim is to get a better understanding of the time and temperature dependent creep mechanisms and deformation. The examinations are separated into tests on seal segments and tests on standardized specimen.
In order to be able to study the aging process, seal segments are compressed in flanges and stored at temperatures ranging from room temperature to 150°C. After defined time intervals the segments are analyzed by using standardized tests including structure investigation and creep tests. The results are compared with the behavior of the specimen basic raw material. This is done to ensure comparability of the thin jacket material and additional sheet material used for standardized tests. Thus, the prediction of component changes after different aging times at different temperatures can be made. As a result forecasts on the long term seal behavior are intended.