Filtern
Erscheinungsjahr
- 2015 (17) (entfernen)
Dokumenttyp
- Beitrag zu einem Tagungsband (10)
- Vortrag (4)
- Zeitschriftenartikel (2)
- Sonstiges (1)
Schlagworte
- Elastomer (6)
- Seal (5)
- Aging (4)
- Compression (4)
- Compression set (4)
- Glass-rubber transition (4)
- O-ring (4)
- Irradiation (3)
- Cask (2)
- Leakage (2)
Eingeladener Vortrag
- nein (4)
A device has been designed, built and tested that allows the investigation of effects of dynamic loads on the leak tightness of elastomer seals at low temperatures. With the test setup, the compression of the tested seal can be reduced by a defined degree in a time period of less than 1 s. For the evaluation of the leak tightness, leakage rates can be determined.
It was shown that the rapid partial release of an elastomer seal leads to its failure already at the beginning of the rubber–glass transition and, therefore, at significantly higher temperatures than the loss of leak tightness observed under static conditions.
Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and for spent fuel transportation casks. In addition, they are also used for spent fuel storage and transportation casks (dual purpose casks (DPC)) as auxiliary seals to allow leakage rate measurements of metal barrier seals for demonstration of their proper assembling conditions. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal, and environmental conditions as well as irradiation during the entire operation period. Concerning DPC, degradation effects should be limited in a way that, for example, effects from potentially released decomposition elements may not harm e.g. metal barrier seals. Leakage rate measurements should be possible also after long interim storage periods prior to subsequent transportation.
Because of the complex requirements resulting from the various applications of containers for radioactive waste and spent nuclear fuel, BAM has initiated several test programmes for investigating the behaviour of elastomer seals. In this contribution the current status is described and first results are discussed.
Due to delays in the site-selection procedure to establish a deep geological repository for spent nuclear fuel and high level waste and in construction of the already licensed Konrad-repository for low and intermediate level waste without heat generation, extended periods of interim storage become more relevant in Germany. BAM is involved in most of the cask licensing procedures and especially responsible for the evaluation of cask-related long-term safety issues.
The long-term performance of elastomer seals for lid Systems of transport and storage casks whether used as auxiliary seals in spent fuel caslcs or as primary seals for low and intermediate level waste packages is an important issue in this context (Jaunich, 2013; Jaunich, 2014; Kömmling, 2015). The polymeric structure of these seals causes a complex mechanical behaviour with time-dependent elasticity reduction and loss of elastic recovery.
The paper presents first results of a comprehensive test Programme consisting of several static and dynamic mechanical short- and long-term tests which have been carried out at BAM on specimens made of representative types of elastomers, fluorocarbon rubber (FKM) and ethylene propylene diene rubber (EPDM). The investigation of the test results used to identify material models and their Parameters as well as the development of two finite element models for the numerical Simulation of tension and compression tests using the finite element code ABAQUS® are described. The calculation results are presented in comparison to the test results. The influence of important material and test parameters was investigated and discussed in sensitivity analyses.
High and ultra-high molecular weight polyethylenes are high performance materials, which are predestined for a wide range of applications due to characteristics like high density, low weight, good dimensional stability, high chemical resistance, and high hydrogen content. These polymers are used in two demanding areas: as implant material in medical technology (only ultra-high molecular weight polyethylenes) and as a component for neutron shielding purposes in casks for storage and transport of radioactive waste. In the medical field (joint replacements) as well as during neutron radiation shielding application, high and ultra-high molecular weight polyethylenes are exposed to gamma irradiation: in the first case requested as sterilization process and for surface-crosslinking and in the second case existing as a side effect of inserting the radioactive material in the cask.
Given that polyethylene as shielding material has to withstand any type of degradation affecting safety relevant aspects to be applicable for long-term radiation shielding purposes for instance over a period of 40 years, the durability of the material is of special interest. High molecular weight polyethylene (HMW-PE; LUPOLEN 5261Z; Lyondell Basell) and ultra-high molecular weight polyethylene (UHMW-PE; GUR 4120; Ticona) were subjected to gamma radiation and afterwards thermally treated. The gamma doses used are in the range of 50 to 600 kGy and irradiation takes place at RT using a Co-60 source. The planned thermal treatment will take place at a temperature of 125 °C for periods of minimum 30 days and maximum of five years. With the applied conventional analytical techniques it is possible to detect structural changes of both types of polyethylene induced by gamma irradiation and certainly of thermal treatment. Through gamma irradiation melting temperature, crystallinity, and density, respectively increased. Furthermore both polyethylenes get oxidized and cross-linked. With regard to the special application as neutron radiation shielding material in casks for storage and transport of radioactive materials, the impact of irradiation lead to changes of material properties. A consolidated view indicates that the detected changes of the irradiated (U)HMW-PE are not safety relevant for long-term neutron radiation shielding purposes over a period of 40 years in Germany.
According to the relevant guidelines and regulations, the safe enclosure of radioactive Container contents has to be guaranteed for long storage periods as well as down to temperatures of -40 °C during transportation. As rubbers are widely used as the main sealing materials for Containers for low- and intermediate-level radioactive waste and as additional component to metal seals in spent fuel and high active waste Containers, a comprehensive eiastomer investigation Programme is in place at BAM. This Programme comprises investigations of overall eiastomer performance, durability, influence of gamma irradiation and low temperature behaviour.
In this paper we focus on the behaviour of eiastomer seals at low temperatures with regard to the potential increase in leakage as material properties of rubbers are strongly temperature-dependent. During continuous cooling, the material behaviour of elastomers changes in the rubber-glass transition temperature ränge from rubberlike entropy-elasticity to stiff energy-elasticity, allowing for almost no strain or retraction. Hence rubbers are normally used above their rubber-glass transition but the minimum limit at which they work has not been defined precisely. For the investigations, fluorocarbon (FKM) and ethylene-propylene-diene (EPDM) rubbers were selected, as they are often used in radioactive waste Containers. The elastomers were studied using several thermoanalytical methods and compression set. The results were compared with component tests to determine the temperature at which the sealing function of O-rings made of eiastomer breaks down. In addition to these results, under static conditions we designed a new measurement set-up which allows for a small deflection of the flange and simultaneous leakage rate measurement at low temperatures.
For many sealing applications rubbers are applied due to their special material properties and easy use. In many applications, e.g. in aviation, traffic or process technology the material can be exposed to low temperatures during Operation. Therefore it is important to know the material behaviour at those low temperatures to determine the temperature range that allows a safe Operation of the seal. As rubbers are used as main sealing materials for Containers for low and intermediate level radioactive waste and as additional component to metal seals in spent fuel and high active waste Containers, a comprehensive elastomer investigation program is run at BAM. This program comprises investigations of elastomer overall performance, durability, influence of gamma irradiation and low temperature behaviour.
In this paper we focus on the behaviour of elastomer seals at low temperatures with regard to potential decrease of leak-tightness as material properties of rubbers are strongly temperature dependent. But additionally to the investigation presented in the past which considered the material properties of new materials and the seal behaviour under purely static conditions [1, 2] we now focus on irradiated materials and on the sealing performance after a fast partial release of the compressed seal.
For the investigations different materials were used, e.g. fluorocarbon (FKM) and ethylenepropylene-diene (EPDM) rubber. To determine the effect of gamma irradiation some samples were irradiated and studied by several thermo-analytical methods and compression set. For the investigation of the seal performance under non static conditions we decided to design a new measurement setup which allows for a small flange deflection and simultaneous leakage rate measurement at low temperatures.