Component and material investigations on metal seals for high level radioactive waste containers
(2018)
Long-term investigations performed at BAM look to extend the state of knowledge on safety-related components of interim storage containers. Metal seals act as the primary sealing barrier in the bolted double lid closure system of the containers. The behaviour of metal seals has been investigated for ageing times up to 8.5 years and for various temperatures. The main cause for reduction in useable resilience overtime was due to creep deformation of the outer jacket of the seal.
Casks for the transport and storage of heat generating radioactive waste in Germany are normally provided with screwed lid systems, which are in most cases equipped with double jacket metal seals with an inner spring wire to provide long term resistance to the seal compression force. Preservation of the high sealing quality of those seals under operational and accidental stress conditions is essentially important to the safety of those casks. Relative displacements of the lid system surfaces caused by specific impact scenarios cannot be excluded and have to be evaluated with respect to a possible increase in the leakage rate.
To get representative data for such metal sealed lid systems, BAM has developed a special conceptualised flange system placed in an appropriate testing machine for relevant mechanical loading of the metal seals under static and cyclic conditions. Furthermore, the flange system enables continuous measurement of the standard helium leakage rate during each test.
The primary aim of the investigation is to identify the correlation between variation of installation conditions (axial displacements) caused by external loads and the standard helium leakage rate. An essential parameter in this case is the useable resilience ru of a metal seal under relevant stress conditions. The useable resilience ru is the vertical difference in the cross-section between the seal's assembling status and the point where the leakage rate, by means of external load relieving, exceeds the quality criterion of 10-8 Pa m3 s-1. Load relieving can instantly occur due to modification of the seal groove dimension caused by accident impacts and deformation of the lid system. Furthermore, component specific basis data for the development of finite element calculation models should be collected. In the tests, seals are subjected to static and cyclic loads. All tests are performed at ambient temperature.
This paper presents the test configuration, different test series and results of the current experiments. Typical load-displacement-leakage rate correlations are presented and discussed.
The aging management system for the mechanical components of nuclear power plants (NPPs) must be established and used by the licensee in such a way that the quality of safety relevant components is guaranteed for the completely designed lifetime of the NPP. This demands an extensive plant life management with special emphases on the knowledge of the degradation in material properties. The basic safety concept in Germany observes this circumstance. Lifetime extension of the German NPPs is an aim of the current valid coalition agreement of the German government. Operational extension of interim storage facilities requires, in comparison to the aging management system for NPP, an aging management system adapted to the Special circumstances of spent fuel storage casks. Extension of interim storage periods for spent fuel casks beyond the designed lifetime requires, in comparison to the components of an NPP, an increasing knowledge of material degradation with potential impact on cask integrity, e.g. leak tightness. Dry interim storage in Germany has been approved for 40 years. After that time, according to the present strategy, a final repository should be available. However, until now, such a final facility still does not exist, and the German exploration and licensing process is heavily delayed. Currently, discussions are continuing regarding further exploration of the Gorleben salt mine. There is willingness to overcome this situation that is clearly described in the available coalition agreement of the federal government. Anyway, however, the prediction is viewed; a repository for heat generating radioactive waste in Germany will not be available in the near future and may not be available when first storage facilities and casks reach their 40 years of approved lifetime, which will occur in ~25 years starting from now. Therefore, the question must be asked:
what has to be done with the existing storage casks in the interim facilities? May these casks be fit for continued use, with an extension of the storage period? One option is to have an aging management system, which creates enough information about the technical condition of safety relevant cask properties. This is the basis for safety evaluation for extended storage periods. In the present paper, possible aging mechanisms for high level waste storage casks are discussed, as well as the influence of the time dependent changes of the component properties.
Dual purpose casks for the transportation and storage of spent nuclear fuel and other radioactive materials require very high leak tightness of lid closure systems under accident conditions as well as in the long term to prevent activity release. For that purpose metal seals of specific types with an inner helical spring and outer metal liners are widely used and have shown their excellent performance if certain quality assurance requirements for fabrication and assembling are satisfied. Well defined surface roughness, clean and dry inert conditions are therefore essential. No seal failure in a loaded cask happened under these conditions until today. Nevertheless, the considered and licensed operation period is limited and all safety assessments have been performed and approved for this period of time which is 40 years in Germany so far. However, in the meantime longer storage periods might be necessary for the future and therefore additional material data will be required. BAM is involved in the qualification and evaluation procedures of those seals from the early beginning. Because long term tests are always time consuming BAM has early decided to perform additional tests with specific test seal configurations to gain a better understanding of the long term behaviour with regard to seal pressure force, leakage rate and useable resilience which is safety relevant mainly in case of accidental mechanical loads inside a storage facility or during a subsequent transport. Main test parameters are the material of the outer seal jacket (silver or aluminium) and the temperature. This paper presents the BAM test program including an innovative test mock-up and most recent test results. Based on these data extrapolation models to extended time periods are discussed, and also future plans to continue tests and to investigate seal behaviour for additional test parameters are explained.