In Germany, the concept of dry interim storage in dual purpose metal casks before disposal is being pursued for spent nuclear fuel (SF) and high active waste (HAW) management. However, since there is no repository available today, the initially planned and established dry interim storage license duration of up to 40 years will be too short and its extension will become necessary. For such a storage license extension it is required to assess the long-term performance of SF and all safety related storage system components in order to confirm the viability of extended storage.
The main safety relevant components are the thick-walled dual purpose metal casks. These casks consist of a monolithic cask body with integrated neutron shielding components (polymers, e.g. polyethylene) and a monitored double lid barrier system with metal and elastomeric seals. The metal seals of this bolted closure system guarantee the required leak-tightness whereas the elastomeric seals allow for leakage rate measurement of the metal seals.
This paper presents an update on running long-term tests on metal seals at different temperatures under static conditions over longer periods of time. In addition, first results of our approach to understand the aging behavior of different elastomeric seals and neutron radiation shielding material polyethylene are discussed.
Due to delays in the siting procedure to establish a deep geological repository for spent nuclear fuel and high level radioactive waste as well as in construction of the already licensed Konrad repository for low and intermediate level radioactive waste, extended periods of interim storage become more relevant in Germany. BAM is involved in most of the cask licensing procedures and especially responsible for the evaluation of cask-related long-term safety issues.
The long-term performance of elastomer seals for lid systems of transport and storage casks, whether used as auxiliary seals in spent fuel casks or as primary seals for low and intermediate level waste packages, is an important issue in this context. The polymeric structure of these seals causes a complex mechanical behavior with time-dependent sealing force reduction.
The results of a comprehensive purpose-designed test program consisting of basic compression and tension tests as well as relaxation tests on unaged specimens of representative types of elastomers (fluorocarbon rubber (FKM) and ethylene propylene diene rubber (EPDM)) at different temperatures and strain rates are presented. They were used to identify the constitutive behavior and to obtain parameters for finite element material models provided by the computer code ABAQUS®. After estimating the influence of uncertainties such as Poisson’s ratio and friction coefficient by sensitivity analyses, the chosen parameters had to prove their suitability for the finite element simulation of the specimen tests themselves.
Based on this preliminary work the simulation of a specific laboratory test configuration containing a typical elastomer seal with circular cross section is presented. The chosen finite element material model and the implemented parameters had to show that they are able to represent not only the specimen behavior under predominantly uniaxial load but also the more complex stress states in real components. Deviations between the measured and calculated results are pointed out and discussed.
For the consideration of long-term effects in the simulation of elastomer behavior, test results of aged specimens are needed. First information about a new test program, started recently and planned to provide these data, are given.
Dual purpose casks for the transportation and storage of spent nuclear fuel and other radioactive materials require very high leak-tightness of lid closure Systems under accident conditions as well as in the long-term to prevent activity release. For that purpose metal seals of specific types with an inner helical spring and outer metal liners are widely used and have shown their excellent performance if certain quality assurance requirements for fabrication and assembling are satisfied. Well defined surface roughness, clean and dry inert conditions are therefore essential. No seal failure in a loaded cask happened under these conditions until today.
Nevertheless, the considered and licensed Operation period is limited and all safety assessments have been performed and approved for this period of time which is 40 years in Germany so far. But in the meantime longer storage periods might be necessary for the future and therefore additional material data will be required. BAM is involved in the qualification and evaluation procedures of those seals from the early beginning. Because long-term tests are always time consuming BAM has early decided to perform additional tests with specific test seal configurations to gain a better understanding of the long-term behavior with regard to seal pressure force, leakage rate and useable resilience which is safety relevant mainly in case of accidental mechanical loads inside a storage facility or during a subsequent transport. Main test parameters are the material of the outer seal jacket (silver or aluminum) and the temperature. This paper presents the BAM test program including an innovative test mock-up and most recent test results. Based on these data extrapolation models to extended time periods are discussed, and also future plans to continue tests and to investigate seal behavior for additional test parameters are explained.
Dual purpose casks for the transportation and storage of spent nuclear fuel and other radioactive materials require very high leak tightness of lid closure systems under accident conditions as well as in the long term to prevent activity release. For that purpose metal seals of specific types with an inner helical spring and outer metal liners are widely used and have shown their excellent performance if certain quality assurance requirements for fabrication and assembling are satisfied. Well defined surface roughness, clean and dry inert conditions are therefore essential. No seal failure in a loaded cask happened under these conditions until today. Nevertheless, the considered and licensed operation period is limited and all safety assessments have been performed and approved for this period of time which is 40 years in Germany so far. However, in the meantime longer storage periods might be necessary for the future and therefore additional material data will be required. BAM is involved in the qualification and evaluation procedures of those seals from the early beginning. Because long term tests are always time consuming BAM has early decided to perform additional tests with specific test seal configurations to gain a better understanding of the long term behaviour with regard to seal pressure force, leakage rate and useable resilience which is safety relevant mainly in case of accidental mechanical loads inside a storage facility or during a subsequent transport. Main test parameters are the material of the outer seal jacket (silver or aluminium) and the temperature. This paper presents the BAM test program including an innovative test mock-up and most recent test results. Based on these data extrapolation models to extended time periods are discussed, and also future plans to continue tests and to investigate seal behaviour for additional test parameters are explained.
Metal seals are in common use as an essential component for the leak tight closure of transport and storage casks for spent fuel and vitrified high active waste from reprocessing. They are placed between the massive monolithic cask body made of ductile cast iron or forged steel and the primary and secondary lids, which are fixed with screws around the lid circumference, in order to ensure long term safe enclosure of the radioactive cask inventory. Hereby, long term reliable pressure forces in combination with a tight surface contact are as important as well maintained seal and surface qualities and dry and clean conditions during seal assembly and operation. A few years ago BAM started systematic investigation on the long term seal behavior with re-spect to longer storage periods and seal behavior in accidental cask scenarios with dynamic de-formations of the seal groove geometry or short term drop in pressure force up to lid lifting. BAM has developed test flanges for seals with full scale cross section diameter but much small-er outer diameter to gain representative data for metal-sealed lid systems. They are placed in appropriate testing machines for relevant mechanical loading under static and dynamic condi-tions with the ability to measure the standard helium leakage rate continuously during each test phase. This paper focuses on BAM long term tests of different seal types with aluminum and silver jackets at three different temperatures of +20°C, +100°C and +150°C under static conditions over longer periods of time. Due to creeping effects, a reduction of the pressure force does ap-pear during loading and unloading depending on prior holding times. So far, test results of up to 2 years indicate a clear correlation between seal pressure forces and holding time, temperature and seal type allowing for extrapolating to much longer periods of time. The paper presents basic correlations, test and evaluation procedures as well as important provisional results and gives an outlook on further investigations.
It is important to evaluate the effect of thermal ageing on the sealing performance of metal gaskets under high temperature for long-term usage. Therefore, in order to gain representative data for this kind of metal-sealed lid System, BAM is currently performing laboratory tests of different gasket types with aluminum and silver jackets at three different temperatures under static conditions up to four years so far, using test flanges for gaskets with full scale cross section diameter but much smaller outer diameter. On the other hand, in order to investigate the applicability of the numerical methodology to evaluate the long-term behavior of the metal gaskets, such as a correlation between seal pressure force and holding time, CRIEPI is developing a modeling method including material tests (tensile and creep tests) at high temperature. In this paper, the applicability of the finite element method (ABAQUS) to predict the recovery displacement and residual seal pressure force of the gasket complex was verified by comparing the calculated values with BAM’s laboratory test results under the joint research agreement between BAM and CRIEPI.
Langzeituntersuchungen an Metalldichtungen mit innen liegendem Federkern und doppelter Ummantelung
(2013)
In Deutschland werden in Transport- und Lagerbehältern (TLB) wärmeentwickelnde radioaktive Abfälle gegenwärtig über einen Zeitraum von bis zu 40 Jahren zwischengelagert. Aufgrund der Situation der noch nicht abgeschlossenen Endlagersuche werden hier möglicherweise Verlängerungen in Betracht zu ziehen sein. Im Deckeldichtsystem der TLB werden in der Regel Metalldichtungen vom Typ Helicoflex® eines französischen Herstellers verwendet, die aus einem innen liegenden Spiralfederkern und zwei Ummantelungen bestehen. Die Ermittlung der Fliess- und Relaxationseigenschaften der Dichtungskomponenten über den vorgesehenen langen Betriebseitraum sind vor dem Hintergrund des Erhalte eines geforderten hohen Dichtniveaus ein wichtiger Untersuchungsgegenstand.