Experimental and numerical studies of shock absorbing materials for containers for radioactive waste
(2012)
The method for the determination of compression set values with a Dynamic Mechanical Analysis (DMA) setup at low temperatures, which was presented previously, allows a much faster and readily automated procedure than the standardized compression set test according to ISO 815-2. This method is applied to a series of different elastomeric materials that are commonly used for sealing applications. The results of the compression set test are compared with results from thermal analysis to allow an in depth comparison of the material behaviour at low temperatures.
Furthermore, a comparison between two EPDM materials is presented. These materials show very similar properties determined by thermo analytical methods such as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) but differ clearly in their compression set behaviour. This comparison shows the importance and value of information of the compression set test in addition to thermal analysis to judge the behaviour of sealing materials and confirms the relevance of the new compression set test method for the investigation of low temperature properties of elastomers.
The molecular dynamics of liquid-crystalline polymethacrylates with biphenyl in the side group forming a highly ordered smectic E phase at low temperatures is investigated by dielectric spectroscopy (DS). Although no glass transition is found by DSC, DS detects a relaxation in the smectic E phase resembling to glassy dynamics. The temperature dependence of its relaxation rate is Arrhenius like at low temperatures, which changes to a VFT law at higher temperatures. Such a behavior is found to be characteristic for glassy dynamics in confining space. It is discussed, considering the structure of the polymers as nanobiphasic consisting of liquid-crystalline layers while the backbones fill the interlayer space. A comparison is made to polymethacrylates having phenyl benzoate as mesogen.