Single walled carbon nanotubes (SWNT) have been produced in an electric arc discharge by using a graphite rod as anode which is filled with a powder mixture of graphite and metallic catalysts like nickel and yttrium. The soot material containing approximately a third of SWNT was collected from the cathode region as a soft, voluminous material. The main by-products in this process are amorphous carbon and graphitic nanoparticles which have to be removed by an appropriate purification process. The as-produced soot material was purified by gas phase oxidation in air at 355 °C. The oxidation of amorphous carbon in air is advantageous against wet chemical methods because it is better controllable. Thermogravimetric analysis and electron microscopy were used to investigate the oxidation behavior of the different kinds of carbon. Oxidation of SWNT and amorphous carbon occurs simultaneously even at moderate temperatures, whereas amorphous carbon is more rapidly oxidized than SWNT. For optimizing the purification procedure by gas phase oxidation, kinetic studies were used to determine the oxidation time for each component in the soot at a given temperature. So it is possible to remove the amorphous carbon quantitatively with minimal losses of SWNT. But it was found that graphitic nanoparticles have the highest stability against oxidation and could therefore not be quantitatively removed by this method without the complete destruction of SWNT. Therefore, the electric arc discharge process has to be a controlled process for minimum production of graphitic nanoparticles to obtain a material with a high content of SWNT.
Nanocomposites of bisphenol A polycarbonate with 2, 4, 6, and 15 wt% multiwall carbon nanotubes (MWNT) and their use in fire retardancy are investigated. Their thermal behavior and pyrolysis are characterized using thermogravimetry, differential scanning calorimeter, oscillatory shear rheology, and dynamic mechanical analysis. The flammability is addressed using LOI and UL 94; the fire behavior, with a cone calorimeter using different irradiation. With increasing MWNT content the storage modulus is increased (10-20%) and melt viscosity increases by several orders of magnitude, particularly for low shear rates. The melt flow, dripping, and deformation during fire are hindered, which influences UL 94 and cone calorimeter results. The peak heat release rate is reduced up to 40-50% due to an improved barrier for small amounts (2 wt%) of MWNT and for low irradiation, whereas the effect is reduced for increasing irradiation and nearly vanishes for increasing filling. Adjuvant but also deleterious mechanisms result in the complex dependency on the MWNT content. Significant flame retardancy effects are specific and limited to only some fire properties. This study allows the materials' potential for implementation in different fire scenarios and tests to be assessed and provides insight into active mechanisms.