Investigation of chloride-induced pitting corrosion of steel in concrete with innovative methods
(2016)
The combination of electrochemical and 3D computed tomography (CT) investigations offers the possibility of verifying electrochemical measurements non-destructively. Determining the steel surfaces damaged by pitting corrosion allows developing specimens having damage pattern corresponding to practice. Corrosion phenomena like decoupled pitting corrosion cannot be verified by electrochemical measurements only, but with the combination of those two kinds of investigations it is possible. Another advantage is the minimization of the number of samples. The classical experimental procedure requires the destruction of samples after each damage step.This can be avoided by the use of 3D computed tomography. As long as the corrosion phenomena are completely within the examination zone shown by the 3D computed tomography, the electrochemical measurements can be calculated on an area basis to get the specific corrosion rate or polarization resistance.
Hochfeste und ultrahochfeste Stahlfaserbetone eignen sich aufgrund ihrer Eigenschaften für den Einsatz bei extremen mechanischen Beanspruchungen. Das für diesen Einsatz erforderliche duktile Bruchverhalten unter Zugbeanspruchung wird ausschließlich durch die Zugabe von geeigneten Stahlfasern und deren Wirkung in der Zementsteinmatrix erreicht. Für eine gezielte stoffliche Optimierung des Systems sind fundierte Kenntnisse zur Wirkungsweise der Stahlfasern notwendig, die bei bisherigen Untersuchungen lediglich auf Basis von klassischen Messverfahren zerstörender Prüfungen gewonnen wurden. Durch das Einbeziehen von Methoden der zerstörungsfreien Materialcharakterisierung können das Bruchverhalten hochfester und ultrahochfester Stahlfaserbetone orts- und zeitaufgelöst untersucht und die einzelnen Phasen des Schädigungsprozesses identifiziert werden. Anhand der vorliegenden Ergebnisse von Zugversuchen eines ultrahochfesten Stahlfaserbetons wird der kombinierte Einsatz von Methoden der zerstörungsfreien Materialprüfung gezeigt und deren Anwendbarkeit in der Analyse des Bruchverhaltens diskutiert. Das Hauptaugenmerk liegt dabei auf der Charakterisierung der ausschlaggebenden Versagensmodi unter Zugbelastung durch die einzelnen Verfahren und dem Vergleich zu klassischen Messmethoden (z. B. Extensometer). Die Zugversuche wurden dazu parallel durch optische Verformungsanalyse mittels Bildkorrelation (DIC), Schallemissionsanalyse (SEA) und 3-D-Computertomografie (CT) begleitet.
Larger high pressure die castings (HPDC) and decreasing wall thicknesses are raising the issue of casting defects like pores in aluminum structures. Properties of components are often strongly influenced by inner porosity. As these products are being established more and more in lightweight construction (e.g. automotive and other transport areas), non-destructive testing methods, which can be applied fast and on-site, are required for quality assurance. In this contribution, the application of active thermography for the direct detection of larger pores is demonstrated. The analysis of limits and accuracy of the method are completed by numerical simulation and the method is validated using computed
tomography.
Im Frühjahr 1969 wurde bei Ausgrabungen der Universität Bonn unter Leitung von Elmar Edel auf der Qubbet el-Hawa ein außergewöhnliches Depot mit Materialien einer antiken Gusswerkstatt gefunden. Im Zuge der Fundteilung gelangten die meisten Stücke des Konvolutes in das Ägyptische Museum der Universität Bonn und werden dort aufbewahrt.
Die Deponierung des für die Forschung zur antiken Metallurgie bisher einzigartigen Konvoluts geschah im Zuge der Nachnutzung von Grabanlagen aus dem Alten Reich (um 2100 v. u. Z.) in der ägyptischen Spätzeit (um 550 – 400 v. u. Z.). Das Depot enthält Objekte, die alle Fertigungsstufen von Metallgegenständen im Wachsausschmelzverfahren dokumentieren. Es wurden Stücke von Rohwachs sowie Wachsmodelle und die zu deren Herstellung genutzten Negativformen gefunden. Weiterhin enthielt es vollständige Gussformen, die in einem aufwendigen Mehrschalenverfahren hergestellt wurden und teilweise bereits für den Guss ausgebrannt worden sind. Schließlich zählen einige Metallfiguren sowie weitere figürliche Objekte zum Konvolut, die alle in den Bereich einer kunsthandwerklichen Werkstatt deuten. Eine Besonderheit stellen zudem Gussformen dar, in denen Fragmente von Metallfiguren zur Reparatur im Überfangguss vorbereitet waren.
Das Depot wurde in der Gesamtpublikation der Bonner Grabungen bisher nur summarisch vorgestellt. 2014/15 initiierten die Abteilung Ägyptologie der Universität Bonn und das LVR-LandesMuseum Bonn unter Ludwig D. Morenz und Michael Schmauder ein gemeinsames und von der Fritz-Thyssen-Stiftung gefördertes Forschungsprojekt, das von Martin Fitzenreiter, Johannes Auenmüller und Frank Willer geleitet wurde. In Kooperation mit Dietmar Meinel (Bundesanstalt für Materialforschung und -prüfung Berlin / BAM, Fachbereich 8.5 Mikro-ZfP), Roland Schwab (Curt-Engelhorn-Zentrum Archäometrie gGmbH, Mannheim), Gerwulf Schneider (FU Berlin, Exzellenzcluster TOPOI), Ursula Baumer und Patrick Dietemann (beide Doerner-Institut / München), Thorsten Geisler-Wierwille (Steinmann Institut für Geologie, Mineralogie und Paläontologie der Universität Bonn) sowie Ursula Tegtmeier (Labor für Archäobotanik der Universität Köln) wurden die Objekte des Konvolutes eingehend und mit zeitgemäßen Verfahren untersucht. Die Ergebnisse dieses Forschungsprojekts werden in dieser Publikation vorgelegt.